1、BRITISH STANDARD BS EN 10246-7:1996 Non-destructive testing of steel tubes Part 7: Automatic full peripheral ultrasonic testing of seamless and welded (except submerged arc welded) steel tubes for the detection of longitudinal imperfections The European Standard EN 10246-7:1996 has the status of a B
2、ritish Standard ICS 23.040.10 钢管的无损检验 弧焊接除外）长度误差检测的自动超声波 检验 第 7 部分：用于无缝和焊接铁磁钢管（埋 标准搜搜网 提供各类标准行业资料免费下载 BS EN 10246-7:1996 This British Standard, having been prepared under the direction of the Engineering Sector Board, was published under the authority of the Standards Board and comes into effect o
3、n 15 July 1996 BSI 02-1999 The following BSI references relate to the work on this standard: Committee reference ISE/73 Draft for comment 91/37479 DC ISBN 0 580 25876 9 Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Committee ISE/
4、73, Steels for pressure purposes, upon which the following bodies were represented: Associated Offices Technical Committee BEAMA Ltd. British Compressed Air Society British Forging Industry Association British Gas plc British Steel Industry Electricity Supply Industry in England and Wales Engineerin
5、g Equipment and Materials Users Association Lloyds Register of Shipping Power Generation Contractors Association (BEAMA Ltd.) Process Plant Association The Welding Institute Co-opted members The following bodies were also represented in the drafting of the standard, through subcommittees and panels:
6、 British Fluid Power Association British Gas British Stainless Steel Association British Welded Steel Tube Association Confederation of British Industry Electricity Association Energy Industries Council Seamless Steel Tube Association Amendments issued since publication Amd. No.DateComments 标准搜搜网 提
7、供各类标准行业资料免费下载 BS EN 10246-7:1996 BSI 02-1999i Contents Page Committees responsibleInside front cover National forewordii Foreword2 Text of EN 10246-73 标准搜搜网 提供各类标准行业资料免费下载 BS EN 10246-7:1996 ii BSI 02-1999 National foreword This British Standard has been prepared by Technical Committee ISE/73 and
8、 is the English language version of EN 10246-7:1996, published by the European Committee for Standardization (CEN). This British Standard contains elements of BS 3889 Non-destructive testing of pipes and tubes Part 1:1983 Methods of automatic ultrasonic testing for the detection of imperfections in
9、wrought steel tubes. A complete list of the Parts of EN 10246 is given in Annex A of this standard. When all relevant Parts have been published, BS 3889-1:1983 will be withdrawn. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are
10、 responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, the EN title page, pages 2 to 9 and a back cover. This standard has
11、 been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. 标准搜搜网 提供各类标准行业资料免费下载 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10246-7 March 1996 ICS 23.040.10 Descriptors: Metal tubes, steel tubes, we
12、lded tubes, seamless tubes, non-destructive tubes, ultrasonic tests, inspection, leak-tightness English version Non-destructive testing of steel tubes Part 7: Automatic full peripheral ultrasonic testing of seamless and welded (except submerged arc welded) steel tubes for the detection of longitudin
13、al imperfections Essais non destructifs des tubes en acier Partie 7: Contrle automatique par ultrasons sur toute la circonfrence pour la dtection des imperfections longitudinales des tubes en acier sans soudure et souds (sauf larc immerg sous flux en poudre) Zerstrungsfreie Prfung von Stahlrohren Te
14、il 7: Automatische Ultraschallprfung nahtloser und geschweiter (ausgenommen unterpulvergeschweiter) Stahlrohre ber den gesamten Rohrumfang zum Nachweis von Lngsfehlern This European Standard was approved by CEN on 1995-12-28. CEN members are bound to comply with the CEN/CENELEC Internal Regulations
15、which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European
16、Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national
17、standards bodies of Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. CEN European Committee for Standardization Comit Europen de Normalisation Europisches Komitee fr Normung
18、 Central Secretariat: rue de Stassart 36, B-1050 Brussels 1996 Copyright reserved to CEN members Ref. No. EN 10246-7:1996 E 标准搜搜网 提供各类标准行业资料免费下载 EN 10246-7:1996 BSI 02-1999 2 Foreword This European Standard has been prepared by Technical Committee ECISS/TC 29, Steel tubes and fittings for steel tu
19、bes, the secretariat of which is held by UNI. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 1996, and conflicting standards shall be withdrawn at the latest by September 1996. Accordin
20、g to the CEN/CENELEC Internal Regulations, the following countries are bound to implement this European Standard: Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. Contents P
21、age Foreword2 1Scope3 2General requirements3 3Method of test3 4Reference standards3 5Dimensions of reference notches4 6Equipment calibration and checking5 7Acceptance5 8Test reporting6 Annex A (informative) Table of Parts of EN 10246 Non-destructive testing of steel tubes7 Annex B (normative) Testin
22、g of tubes having an outside diameter-to-thickness ratio less than five8 Annex C (normative) Manual ultrasonic testing of untested ends/suspect areas8 Figure 1 Reference notch forms4 Figure B.1 Mode transformed compression wave adaptation of shear wave testing8 Table 1 Acceptance level designation a
23、nd corresponding reference notch depth4 Table 2 Minimum notch depth categories4 Table B.1 Ratios8 标准搜搜网 提供各类标准行业资料免费下载 EN 10246-7:1996 BSI 02-19993 1 Scope This Part of EN 10246 specifies the requirements for automatic full peripheral ultrasonic shear wave testing of seamless and welded steel tube
24、s, with the exception of submerged arc-weld (SAW) tubes, for the detection of longitudinal imperfections according to six different acceptance levels (see Table 1 and associated notes). This Part of EN 10246 is applicable to the inspection of tubes with an outside diameter greater than 10 mm, and wi
25、th an outside diameter-to-thickness ratio equal to or greater than five. For tubes with an outside diameter-to-thickness ratio less than five, one of the options specified in Annex B shall be used by agreement between purchaser and manufacturer. European Standard EN 10246 Non-destructive testing of
26、steel tubes comprises the Parts shown in Annex A. 2 General requirements 2.1 The ultrasonic inspection covered by this Part of EN 10246 is usually carried out on tubes after completion of all the primary production process operations. This inspection shall be carried out by suitably trained, qualifi
27、ed and competent NDT personnel approved by the manufacturer. 2.2 The tubes to be tested shall be sufficiently straight to ensure the validity of the test. The surfaces shall be sufficiently free from foreign matter which would interfere with the validity of the test. 3 Method of test 3.1 The tubes s
28、hall be tested using an ultrasonic shear wave technique for the detection of predominantly longitudinal imperfections. 3.2 During testing, the tubes and the transducer assembly shall be moved relative to each other so that the whole of the tube surface is scanned. The chosen relative speed of moveme
29、nt during testing shall not vary by more than 10 %. NOTEIt is recognized that there may be a short length at both tube ends which cannot be tested. Any untested ends shall be dealt with in accordance with the requirements of the appropriate product standards (see also Annex C). 3.3 During testing, t
30、he tubes shall be scanned in two opposing circumferential directions of beam travel, unless otherwise agreed between purchaser and manufacturer. 3.4 The ultrasonic test frequency to be applied shall be in the range of 1 MHz to 15 MHz dependent upon the thickness and surface finish of the tube to be
31、tested. 3.5 The maximum width of each individual transducer, measured parallel to the major axis of the tube, shall be 25 mm. For U1 and U2 category tubes with an outside diameter equal to or less than 50 mm, the width of any one transducer is normally restricted to a maximum of 12,5 mm (see also 5.
32、3). 3.6 The equipment shall be capable of classifying tubes as either acceptable or suspect by means of an automatic trigger/alarm combined with a marking and/or sorting system. 3.7 Where manual ultrasonic testing of untested tube ends and/or local suspect areas is required, this shall be carried ou
33、t in accordance with Annex C. 4 Reference standards 4.1 The reference standards defined in this Part of EN 10246 are convenient standards for the calibration of non-destructive testing equipment. The dimensions of these standards should not be construed as the minimum size of imperfection detectable
34、 by such equipment. 4.2 The ultrasonic equipment shall be calibrated using a longitudinal reference notch on the outside and inside surfaces, or the outside surface only of a tubular test piece. The internal notch shall not be used when the tube internal diameter is less than 20 mm, unless otherwise
35、 agreed between purchaser and manufacturer. 4.3 The test piece shall have the same specified diameter, thickness, surface finish and heat treated condition as the tube to be tested, and shall have similar acoustic properties (for example velocity, attenuation coefficient, etc). 4.4 The external and
36、internal notches shall be sufficiently separated from the extremities of the test piece and from each other (when both are used), so that clearly distinguishable signal indications are obtained. 4.5 The reference notch or notches shall lie parallel to the major axis of the test piece. The reference
37、notch or notches shall be of the “N” type except that the “V” type notch may be used at the discretion of the manufacturer when the specified notch depth is less than or equal to 0,5 mm (see Figure 1). In the case of the “N” type notch, the sides shall be nominally parallel and the bottom shall be n
38、ominally square to the sides. 标准搜搜网 提供各类标准行业资料免费下载 EN 10246-7:1996 4 BSI 02-1999 4.6 The reference notch shall be formed by machining, spark erosion or other methods. NOTEIt is recognized that the bottom or the bottom corners of the notch may be rounded. 5 Dimensions of reference notches The dimen
39、sions of the reference notches shall be as follows: 5.1 Width, w (see Figure 1). The width of the reference notch shall be 1,0 mm max. 5.2 Depth, d (see Figure 1). 5.2.1 Reference notch depth. The reference notch depth shall be as given in Table 1. Table 1 Acceptance level designation and correspond
40、ing reference notch depth 5.2.2 Minimum notch depth The minimum notch depth is related to the type of tube used for a particular application and is denoted by a sub-category as given in Table 2, unless otherwise agreed between purchaser and manufacturer. Table 2 Minimum notch depth categories 5.2.3
41、Maximum notch depth The maximum notch depth for all acceptance levels and sub-categories shall be 1,5 mm, with exception that in the case of tubes with a thickness in excess of 50 mm, the maximum notch depth, may be extended to 3,0 mm unless otherwise agreed. 5.3 Tolerance on depth The tolerance on
42、depth shall be 15 % of reference notch depth or 0,05 mm, whichever is the larger, with the exception that when the notch depth is less than 0,2 mm, the tolerance on the depth shall be 0,03 mm. Figure 1 Reference notch forms Acceptance levelNotch depth in % of the specified thickness (see note 1) U1
43、(see note 2)3 U2 (see note 3)5 U310 U412,5 U515 U620 NOTE 1The values of notch depth specified in this table are the same, for the corresponding categories, in all European Standards concerning non-destructive testing of steel tubes where reference is made to different acceptance levels. It should,
44、however, be kept in mind that although the reference standards are identical, the various test methods involved can give different test results. Accordingly the acceptance level designation prefix U (ultrasonic) has been adopted to avoid any inferred direct equivalence with other test methods. NOTE
45、2Acceptance level U1 is not applicable to welded tubes. NOTE 3For welded tubes, acceptance level U2 can be used as an alternative to or in combination with U3 by agreement between purchaser and manufacturer. Sub-categoryMinimum notch depth Typical tube condition A0,1 mmCold-finished and machined tub
46、es B0,2 mm C0,3 mmAll other conditions D0,5 mm NOTE 1The minimum notch depth that can be used is related to specific tube manufacturing methods where the surface finish plays a dominant role in the minimum notch depth that can be adopted for ultrasonic equipment calibration in order to achieve an ac
47、ceptable signal/noise ratio. NOTE 2Sub-categories A and B do not apply to welded tubes. 标准搜搜网 提供各类标准行业资料免费下载 EN 10246-7:1996 BSI 02-19995 5.4 Length The length of the reference notch or notches shall be at least twice the width of the transducers, with the following exception: for U1 and U2 catego
48、ry tubes with an outside diameter less than or equal to 50 mm and where the width of any one transducer exceeds 12,5 mm, the length of the reference notch or notches shall not exceed 12,5 mm (at full depth). 5.5 Verification The reference notch dimensions and shape shall be verified by a suitable technique. 6 Equipment calibration and checking 6.1 The equipment shall be adjusted to consistently produce, (for example, from three consecutive passes of the test piece through the equipment), clearly identifiable signals from both the external and internal reference notches or from t