《CC复合材料高温长时烧蚀行为与控制方法.doc》由会员分享,可在线阅读,更多相关《CC复合材料高温长时烧蚀行为与控制方法.doc(2页珍藏版)》请在三一文库上搜索。
1、CC复合材料高温长时烧蚀行为与控制方法Abstract: TaC ceramic interlayer was deposited on carbon fiber in three-dimensional fine-woven punctured felt by using chemical vapor infiltration method. By controlling the flow direction of the reaction gases in the preform, C/C composites with gradient distributed TaC interlaye
2、r were obtained. Microstructure, flexural property and fracture toughness of the as-prepared composites were studied. The results show that TaC interlayer is deposited on the surface of carbon fiber and presents a gradient distribution in C/C composites. The average flexural strength and fracture to
3、ughness of the as-prepared composites are 272.6 MPa and 5.0 MPa?m1/2, respectively. In general, with the decreasing of the TaC content along the thickness direction (Z-axis) of the composites,the length of carbon fiber pulled out from the carbon matrix becomes shorter. In TaC-rich area, TaC content
4、has significant influence on fracture behavior of the composites. The fracture behavior of the TaC-rich area is brittle in outer layer which has more TaC, while change to pseudo-ductile in inner layer which has less TaC. Key Words: C/C composite; Interlayer; Gradient distribution; Microstructure; Mechanical property 阅读全文链接(需实名注册):http:/