《【BS标准word原稿】BS EN 12373-5-1999 Aluminium and aluminium alloys. Anodizing. Assessment of quality of sealed anodic oxidation coatings by measurement of admittance.doc》由会员分享，可在线阅读，更多相关《【BS标准word原稿】BS EN 12373-5-1999 Aluminium and aluminium alloys. Anodizing. Assessment of quality of sealed anodic oxidation coatings by measurement of admittance.doc（13页珍藏版）》请在三一文库上搜索。
1、豆丁网：http:/ STANDARDAluminium and aluminium alloys Anodizing Part 5: Assessment of quality of sealed anodic oxidation coatings by measurement of admittanceThe European Standard EN 12373-5:1998 has the status of aBritish StandardICS 25.220.20; 77.120.10| BS EN12373-5:1999|Licensed Copy: sheffieldun sh
2、effieldun, na, Sat Oct 28 06:55:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI|NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBS EN 12373-5:1999National forewordThis British Standard is the English language version of EN 12373-5:1998. It supersedes BS 6161-6:1984, which is with
3、drawn.The UK participation in its preparation was entrusted to Technical CommitteeSTI/32, Anodic oxidation coatings on aluminium, which has the responsibility to: aid enquirers to understand the text; present to the responsible European committee any enquiries on the interpretation, or proposals for
4、 change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK.A list of organizations represented on this committee can be obtained on request to its secretary.Cross-referencesThe British Standards which implement international or
5、European publications referred to in this document may be found in the BSI Standards Catalogue under the section entitled International Standards Correspondence Index, or by using theFind facility of the BSI Standards Electronic Catalogue.A British Standard does not purport to include all the necess
6、ary provisions of a contract. Users of British Standards are responsible for their correct application.Compliance with a British Standard does not of itself confer immunity from legal obligations.Summary of pagesThis document comprises a front cover, an inside front cover, the EN title page, pages 2
7、 to 4, an inside back cover and a back cover.Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 06:55:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSIAmd. No.DateText affectedThis British Standard, having been prepared under the direction of the Sector Committee for Materials and Chemicals, was pub
8、lished under the authority of the StandardsCommittee and comes into effect on 15 April 1999BSI 04-1999ISBN 0 580 32029 4Amendments issued since publicationEUROPEAN STANDARDEN 12373-5NORME EUROPE ENNEEUROPA ISCHE NORMNovember 1998ICS 25.220.10; 77.120.10Descriptors: surface treatment, anodizing, alum
9、inium, aluminium alloys, sealing, quality control, non-destructive tests, measurementsEnglish versionAluminium and aluminium alloys Anodizing Part 5: Assessment of quality of sealed anodic oxidation coatings by measurement of admittanceAluminium et alliages daluminium Anodisation Partie 5: Evaluatio
10、n de la qualite des couches anodiques colmate es par mesurage de ladmittanceAluminium und Aluminiumlegierungen Anodisieren Teil 5: Pru fung der Qualita t von verdichteten, anodisch erzeugten Oxidschichten durch Messung des ScheinleitwertesLicensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 06:55:
11、04 GMT+00:00 2006, Uncontrolled Copy, (c) BSIThis European Standard was approved by CEN on 5 November 1998.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alterati
12、on. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translatio
13、n under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions.CEN members are the national standards bodies of Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy,
14、 Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom.CENEuropean Committee for Standardization Comite Europe en de Normalisation Europa isches Komitee fu r NormungCentral Secretariat: rue de Stassart 36, B-1050 Brussels1998 CEN All rights of exploitation in any f
15、orm and by any means reserved worldwide for CEN nationalMembers.Ref. No. EN 12373-5:1998 EPage EN 12373-5:1998BSI 04-1999Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 06:55:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSIForewordThis European Standard has been prepared by Technical Committee C
16、EN/TC 132, Aluminium and aluminium alloys, the Secretariat of which is held by AFNOR.This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by May 1999, and conflicting national standards shall be withdrawn
17、 atthe latest by May 1999.According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg
18、, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom.It is based upon ISO 2931:1983.EN 12373, Aluminium and aluminium alloys Anodizing, comprises the following parts: Part 1: Method for specifying decorative and protective anodic oxidation coatings on aluminium; Part 2:
19、 Determination of mass per unit area (surface density) of anodic oxidation coatings Gravimetric method; Part 3: Determination of thickness of anodic oxidation coatings Non-destructive measurement by split-beam microscope; Part 4: Estimation of loss of absorptive power of anodic oxidation coatings af
20、ter sealing by dye spot test with prior acid treatment; Part 5: Assessment of quality of sealed anodic oxidation coatings by measurement of admittance; Part 6: Assessment of quality of sealed anodic oxidation coatings by measurement of the loss of mass after immersion in phosphoric acid/chromic acid
21、 solution without prior acid treatment; Part 7: Assessment of quality of sealed anodic oxidation coatings by measurement of the loss of mass after immersion in phosphoric acid/chromic acid solution with prior acid treatment; Part 8: Determination of the comparative fastness to ultra-violet light and
22、 heat of coloured anodic oxidation coatings; Part 9: Measurement of wear resistance and wear index of anodic oxidation coatings using an abrasive wheel wear test apparatus; Part 10: Measurement of mean specific abrasion resistance of anodic oxidation coatings using an abrasive jet test apparatus; Pa
23、rt 11: Measurement of specular reflectance and specular gloss of anodic oxidation coatings atangles of 208, 458, 608 or 858; Part 12: Measurement of reflectance characteristics of aluminium surfaces using integrating-sphere instruments; Part 13: Measurement of reflectivity characteristics of alumini
24、um surfaces using a goniophotometer or an abridged goniophotometer; Part 14: Visual determination of image clarity of anodic oxidation coatings Chart scale method; Part 15: Assessment of resistance of anodic oxidation coatings to cracking by deformation; Part 16: Check for continuity of thin anodic
25、oxidation coatings Copper sulfate test; Part 17: Determination of electric breakdown potential; Part 18: Rating system for the evaluation of pitting corrosion Chart method; Part 19: Rating system for the evaluation of pitting corrosion Grid method.ContentsPageForeword 21Scope32Symbols and abbreviati
26、ons33Principle34Apparatus35Test pieces36Procedure37Expression of results48Test report4Introduction 3Page 3EN 12373-5:1998IntroductionThe test described in this standard is intended to give a quick, non-destructive assessment of the quality of sealed anodic oxidation coatings and is very suitable for
27、 routine production control. It is carried out following sealing and before any other supplementary process is undertaken, for example, oiling, waxing or lacquering.The correlation of the results obtained with those of other sealing tests may be affected by the presence of sealing additives, or cont
28、aminants such as silicate or phosphate. For this reason, sealing quality should be checked from time to time by one of the reference acid-dissolution methods specified in EN 12373-61) or EN 12373-71).The pretreatment, the anodizing process, the colouring process used and the alloy can all have an ef
29、fect on admittance readings.1 ScopeThis part of this European Standard specifies a method for assessing the quality of sealed anodic oxidation coatings on aluminium and its alloys by measurement of the admittance.The method is applicable to anodic oxidation coatings sealed in an aqueous medium.The m
30、ethod is suitable for use as a production control test and as an acceptance test where there is agreement between the supplier and the purchaser.Any type of anodized component may be tested by the method described, provided that there is sufficient area (a circle of about 20 mm diameter) and that th
31、e film thickness is greater than 3 mm.2 Symbols and abbreviationsAdmittance, Y, is the inverse of the complex apparent resistance, Z (impedance), which, in an alternating current circuit, is represented by the vectorial sum of the actual resistance, R, and the reactance, Xc:3 PrincipleAn anodic oxid
32、ation coating on aluminium is represented as an electrical diagram made up of a number of ohmic and capacitative resistances mounted in series and/or parallel in an alternating currentcircuit. The numerical value of these resistances depends upon the following variables:a) basis metal (for example,
33、composition, size and distribution of intermetallic compounds, and surface condition);b) type of sealing process (for example, steam, hot water, nickel or cobalt salts or cold impregnation); c) thickness and density of the anodic oxidation layer (depending upon electrolyte, type of current, current
34、density, electrolyte temperature, etc.);d) dyeing or pigmentation processes used to colour the anodic oxidation coating;e) time and conditions of storage between sealing and measurement.4 Apparatus4.1 Device for measuring admittance, covering a range of 3 mS to 300 mS.The instrument shall measure at
35、 a frequencyof 1 kHz 10 Hz and be equipped with two electrodes, one with a contact screw by means of which a connection shall be made with the basis metal of the sample, and the other a pencil-like probe.4.2 Cell, containing the electrolyte, formed conveniently by a rubber ring of 13 mm internal dia
36、meter and approximately 5 mm thickness, the surface of which is self-adhesive. This type of cell has an internal area of 133 mm2.4.3 Electrolyte, aqueous solution of potassium sulfate, 35 g/l.5 Test piecesAnodized products, of any shape or dimension, provided that it is possible to determine the thi
37、cknessY = 1ZZ = X 2 + R2 c(1) (2)of the coating at the point of measurement, to applythe electrolyte-filled cell and, if necessary, to determine the surface area tested.6 ProcedureIn equation (2):R is the resistance, in ohms;cX = 1is the reactance, where:2 fCf is the frequency of the alternating cur
38、rent;Cis the capacitance.Carry out the test preferably within 1 h to 4 h after sealing and cooling to room temperature, and, in any case, within 48 h.Degrease the test area of the test piece, using a suitable organic solvent.NOTE If a silicone or wax preservative has been applied after sealing, degr
39、easing may not be adequate. In such cases, satisfactory cleaning can sometimes be achieved by first using an organic solvent followed by rubbing with a paste of magnesium oxide or pumice powder and water until no water break occurs.Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 06:55:04 GMT+
40、00:00 2006, Uncontrolled Copy, (c) BSI1) See foreword.BSI 04-1999Page EN 12373-5:1998BSI 04-1999Screw one electrode into the test piece so that it makes good electrical contact with the basis metal. Carefully fix the cell (4.2) on the test area. If the areaPerform these corrections using the followi
41、ng formulae:133 Ymof the cell is modified by the geometric shape of the test piece, determine the new dimensions. Fill the cellY1 = A(3)with the electrolyte (4.3). At each point of measurement, use a new cell and fresh electrolyte. IfY2 = Y1 f1 (4)Y2 ethe test is carried out on an oblique or vertica
42、l surface, introduce into the cell a cotton wool plug soaked inthe electrolyte, or use a cell of special design.Y3 = 20where(5)Immerse the other electrode in the solution and measure the admittance.Carry out the measurement at a temperature of between 10 8C and 35 8C. Take the reading atleast 2 min
43、after the introduction of the electrode into the cell, and record the temperature.After the admittance has been measured, determine the thickness of the anodic oxidation coating at the pointof measurement.NOTE Cells which are not perfectly attached, and therefore not watertight, will give an inaccur
44、ate reading.7 Expression of resultsTo allow comparison of results, the result recorded shall include three corrections to the measured value:a) a correction to relate the measured admittance value to a measuring area of 133 mm2 (in the case where it is not possible to use this exact area, and if the actual measuring area is between 100 mm2and 200 mm2);b) a correction to relate the measured admittance value to that measured at an ambient temperature of 25 8C;