1、BRITISH STANDARDBS EN820-1:2002-,-,-Advanced technical ceramics Methods of testing monolithic ceramics Thermomechanical properties Part 1: Determination of flexural strength at elevated temperaturesThe European Standard EN 820-1:2002 has the status of aBritish StandardICS 81.060.30 Copyright British
2、 Standards InstitutionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/5959906001, 11/08/200406:05:32 MST Questions or comments about this message: please call the DocumentPolicy Group at 303-397-2295.BS EN 820-1:2002National forewordThis B
3、ritish Standard is the official English language version ofEN 820-1:2002. It supersedes DD ENV 820-1:1994 which is withdrawn.The UK participation in its preparation was entrusted to Technical CommitteeRPI/13, Advanced technical ceramics, which has the responsibility to:aid enquirers to understand th
4、e text;present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed;monitor related international and European developments and promulgate them in the UK.A list of organizations represented on this commit
5、tee can be obtained on request to its secretary.Cross-referencesThe British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Sear
6、ch” facility of the BSI Electronic Catalogue or of British Standards Online.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard does not of itself confer immunity from legal obli
7、gations.-,-,-This British Standard was published under the authority of the Standards Policy and Strategy Committee on6 March 2003 BSI 6 March 2003ISBN 0 580 41375 6Summary of pagesThis document comprises a front cover, an inside front cover, the EN title page,pages 2 to 10, an inside back cover and
8、 a back cover.The BSI copyright date displayed in this document indicates when the document was last issued.Amd. No.DateCommentsAmendments issued since publicationEUROPEAN STANDARD NORME EUROPENNEEUROPISCHE NORMEN 820-1October 2002ICS 81.060.30Supersedes ENV 820-1:1993English version-,-,-Advanced te
9、chnical ceramics - Methods of testing monolithic ceramics - Thermomechanical properties - Part 1: Determination of flexural strength at elevated temperaturesCramiques techniques avances - Mthode dessai des cramiques monolithiques - Proprits thermodynamiques- Dtermination de la rsistance la flexion t
10、empratures levesHochleistungskeramik - Monolithische Keramik - Thermomechanische Eigenschaften - Teil 1: Bestimmung der Biegefestigkeit bei erhhten TemperaturenThis European Standard was approved by CEN on 8 August 2002.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which
11、stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Management Centre or to any CEN member.This European Standard
12、exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Management Centre has the same status as the official versions.CEN members are the national standards bo
13、dies of Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATION C OM I T EUR OP EN DE NOR M AL I S ATI ON EUR OP I S C
14、HES KOM I TEE F R NOR M UNG Management Centre: rue de Stassart, 36 B-1050 Brussels 2002 CENAll rights of exploitation in any form and by any means reserved worldwide for CEN national Members.Ref. No. EN 820-1:2002 EEN 820-1:2002 (E)ContentspageForeword .31Scope .42Normative references .43Terms and d
15、efinitions.44Apparatus .54.1General .54.2Test jig.54.3Heating device.64.4Test machine .64.5Linear measuring devices .6-,-,-4.6Drying oven .75Test pieces.76Test temperatures and number of tests .77Test procedure .78Calculations.89Accuracy and references .910Test report .102Copyright British Standards
16、 InstitutionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/5959906001, 11/08/200406:05:32 MST Questions or comments about this message: please call the DocumentPolicy Group at 303-397-2295.EN 820-1:2002 (E)ForewordThis document EN 820-1:2
17、002 has been prepared by Technical Committee CEN/TC 184 Advanced technical ceramics, the secretariat of which is held by BSI.This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by April 2003, and conflic
18、ting national standards shall be withdrawn at the latest by April 2003.This document supersedes ENV 820-1:1993.This document has been prepared under a mandate given to CEN by the European Commission and the EuropeanFree Trade Association.EN 820 Advanced technical ceramics Methods of testing monolith
19、ic ceramics Thermomechanical properties consists of three Parts: Part 1 : Determination of flexural strength at elevated temperatures Part 2 : Determination of self-loaded deformation Part 3 : Determination resistance to thermal shock by water quenchingAccording to the CEN/CENELEC Internal Regulatio
20、ns, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and th
21、e United Kingdom.3-,-,-Copyright British Standards InstitutionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/5959906001, 11/08/200406:05:32 MST Questions or comments about this message: please call the DocumentPolicy Group at 303-397-2295
22、.EN 820-1:2002 (E)1ScopeThis Part of this European Standard specifies a method of determining the three-point or four-point flexural strength of advanced monolithic technical ceramics at elevated temperatures as agreed between parties to the test. The test can be performed in any appropriate atmosph
23、ere.2Normative referencesThis European Standard incorporates by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the text, and in the publications listed hereafter. For dated references, subsequent amendments to or revi
24、sions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies (including amendments).EN 843-1, Advanced technical ceramics Monolithic ceramics Mechanical tests
25、 at room temperature Part 1: Determination of flexural strength.ENV 843-5, Advanced technical ceramics Monolithic ceramics Mechanical tests at room temperature Part 5: Statistical analysis of fracture data.EN 10002-2, Metallic materials Tensile testing Part 2: Verification of the force measuring sys
26、tem of the tensile testing machine.EN ISO 17025, General requirements for the competence of testing and calibration laboratories.IEC 60584, Thermocouples - Part 1: Reference tables.IEC 60584, Thermocouples - Part 2: Tolerances.ISO 3611, Micrometer callipers for external measurement.3Terms and defini
27、tionsFor the purposes of this European Standard, the following terms and definitions apply.3.1nominal flexural strengthmaximum nominal stress at the instant of failure supported by the material when loaded in elastic bendingNOTEIt is recognised that flexural strength tests on ceramics at elevated te
28、mperature may reveal inelastic behaviour in the material. Under such conditions, the nominal flexural strength calculated in accordance with this standard is not strictly a valid result, since it tends to overestimate the true surface stress in the test piece. This method requires that the load/disp
29、lacement relationship for each test piece at each temperature is inspected, and the validity of the result determined.3.2three-point flexuremeans of bending a beam test piece whereby the test piece is supported on bearings near its ends, and a central load is applied4-,-,-EN 820-1:2002 (E)3.3four-po
30、int flexuremeans of bending a beam test piece whereby the test piece is supported on bearings near its ends, and is loaded equally at two points symmetrically disposed about the centre of the supported span3.4inelastic deformationfor the purposes of the test, the deformation of a test specimen under
31、 load which is not entirely elastic and reversible on removal of the load3.5subcritical crack growthextension of existing cracks or flaws under a stress which does not produce instant failureNOTEThis effect can be due to the intrinsic crack propagation of the material, additionally influenced by the
32、 environment.4Apparatus4.1GeneralThe test is carried out in a similar manner to that prescribed in EN 843-1 for testing at room temperature, with the exceptions that the test jig shall be constructed from materials which are capable of remaining linearly elastic at the temperature of testing, and th
33、at a means of heating the test jig and test piece to the test temperature is required.4.2Test jigThe test jig shall be of a design that allows full articulation for alignment of the support and loading rollers on the surfaces of the test piece, and in which the rollers are capable of rolling to mini
34、mise friction between the rollers and the test piece.NOTE 1It is recognised that practical limitations can restrict the design of the test jig, and oxidation effects can restrict its function. In such cases, alternatives may be employed, but deviations from the function specified above should be rep
35、orted in the report (see clause 10, d).The outer span of the test jig shall be either 20,0 mm 0,5 mm (span A) or 40,0 mm 0,5 mm (span B). For three-point flexure the loading roller shall be centralised relative to the span to within 0,2 mm. For four-point flexure, the inner span shall be 10,0 0,2 mm
36、 (span A) or 20,0 mm 0,2 mm (span B). The inner rollers shall be symmetrically positioned relative to the outer rollers to better than 0,2 mm.NOTE 2This represents a relaxation of centralisation requirements compared with room temperature testing (requirement0,1 mm, see EN 843-1) because it can beco
37、me relatively more difficult to set up test jigs inside furnaces.Measurements of the positions of the rollers shall be made with a travelling microscope (4.5.2).The rollers shall be made from a material which is capable of remaining linearly elastic up to the maximum temperature of the series of tests. For tests to 400 C, hardened steel rollers as in EN 843-1 shall suffi