《AS NZS 3750.1-2008 Paints for steel structures Part 1 Epoxy mastic (two-pack)—For rusted steel.pdf》由会员分享，可在线阅读，更多相关《AS NZS 3750.1-2008 Paints for steel structures Part 1 Epoxy mastic (two-pack)—For rusted steel.pdf（32页珍藏版）》请在三一文库上搜索。
1、 AS/NZS 3750.1:2008 Australian/New Zealand Standard Paints for steel structures Part 1: Epoxy mastic (two-pack)For rusted steel AS/NZS 3750.1:2008 AS/NZS 3750.1:2008 This Joint Australian/New Zealand Standard was prepared by Joint Technical Committee CH-003, Paints and Related Materials. It was appr
2、oved on behalf of the Council of Standards Australia on 19 March 2007 and on behalf of the Council of Standards New Zealand on 3 March 2007. This Standard was published on 19 May 2008. The following are represented on Committee CH-003: AUSTROADS Australasian Corrosion Association Australian Paint Ap
3、proval Scheme Australian Paint Manufacturers Federation Australian Pipeline Industry Association Business New Zealand Engineers Australia Institution of Professional Engineers New Zealand Master Painters Australia Master Painters New Zealand Association National Association of Testing Authorities Au
4、stralia Water Corporation Western Australia Keeping Standards up-to-date Standards are living documents which reflect progress in science, technology and systems. To maintain their currency, all Standards are periodically reviewed, and new editions are published. Between editions, amendments may be
5、issued. Standards may also be withdrawn. It is important that readers assure themselves they are using a current Standard, which should include any amendments which may have been published since the Standard was purchased. Detailed information about joint Australian/New Zealand Standards can be foun
6、d by visiting the Standards Web Shop at .au or Standards New Zealand web site at www.standards.co.nz and looking up the relevant Standard in the on-line catalogue. Alternatively, both organizations publish an annual printed Catalogue with full details of all current Standards. For more frequent list
7、ings or notification of revisions, amendments and withdrawals, Standards Australia and Standards New Zealand offer a number of update options. For information about these services, users should contact their respective national Standards organization. We also welcome suggestions for improvement in o
8、ur Standards, and especially encourage readers to notify us immediately of any apparent inaccuracies or ambiguities. Please address your comments to the Chief Executive of either Standards Australia or Standards New Zealand at the address shown on the back cover. This Standard was issued in draft fo
9、rm for comment as DR 04186. The Standard is downloaded from Standard Sharing AS/NZS 3750.1:2008 Australian/New Zealand Standard Paints for steel structures Part 1: Epoxy mastic (two-pack)For rusted steel COPYRIGHT Standards Australia/Standards New Zealand All rights are reserved. No part of this wo
10、rk may be reproduced or copied in any form or by any means, electronic or mechanical, including photocopying, without the written permission of the publisher. Jointly published by Standards Australia, GPO Box 476, Sydney, NSW 2001 and Standards New Zealand, Private Bag 2439, Wellington 6020 ISBN 0 7
11、337 8659 6 Originated as AS 3750.11994. Revised and redesignated AS/NZS 3750.1:2008. AS/NZS 3750.1:2008 2 PREFACE This Standard was prepared by the Joint Standards Australia/Standards New Zealand Committee CH-003, Paints and Related Materials to supersede AS 3750.11994. It forms part of a series of
12、product Standards for paint systems referred to in AS/NZS 2312, Guide to the protection of structural steel against atmospheric corrosion by the use of protective coatings. See AS/NZS 3750.0 for other published Standards in this series. The terms normative and informative have been used in this Stan
13、dard to define the application of the appendix to which they apply. A normative appendix is an integral part of a Standard, whereas an informative appendix is only for information and guidance. The Standard is downloaded from Standard Sharing 3 AS/NZS 3750.1:2008 CONTENTS Page SECTION 1 SCOPE AND G
14、ENERAL 1.1 SCOPE 4 1.2 REFERENCED DOCUMENTS 4 1.3 DEFINITIONS 4 1.4 SAFETY PRECAUTIONS4 SECTION 2 MATERIALS REQUIREMENTS 2.1 GENERAL 5 2.2 CONDITIONS OF TEST.5 2.3 LIQUID PAINT.5 2.4 SPRAY APPLICATION PROPERTIES5 2.5 APPLIED FILM 6 2.6 MIXING RATIO .7 2.7 ADDITIONAL TESTS8 SECTION 3 PACKAGING AND LA
15、BELLING 3.1 PACKAGING9 3.2 LABELLING.9 APPENDICES A PURCHASING GUIDELINES 10 B GUIDANCE ON THE USE AND APPLICATION OF EPOXY MASTIC PAINT. 11 C REFERENCED DOCUMENTS 14 D PREPARATION OF TEST PANELS 16 E DETERMINATION OF THE CURING PROPERTIES OF AN EPOXY MASTIC 17 F ASSESSMENT OF RESISTANCE OF AN EPOXY
16、 MASTIC TO WATER 19 G ASSESSMENT OF RESISTANCE OF AN EPOXY MASTIC TO MINERAL OIL. 21 H ASSESSMENT OF RESISTANCE OF AN EPOXY MASTIC TO ALKALI AND ACID 23 I PROCEDURE FOR TESTING DURABILITY OF AN EPOXY MASTIC. 25 J ADDITIONAL TESTS 27 AS/NZS 3750.1:2008 4 COPYRIGHT STANDARDS AUSTRALIA/STANDARDS NEW ZE
17、ALAND Australian/New Zealand Standard Paints for steel structures Part 1: Epoxy mastic (two-pack)For rusted steel S E C T I O N 1 S C O P E A N D G E N E R A L 1.1 SCOPE This Standard specifies requirements for a two-component, high-build, high-solids, epoxy mastic for the protection of iron and ste
18、el against exterior atmospheric corrosion in a severe industrial or coastal marine environment. It is intended primarily for use on imperfectly prepared surfaces, i.e., surfaces where residual rust and some previously applied paint of any type are still present. These coatings are also suitable for
19、applications over blast cleaned surfaces where extended service life may be achieved. Paint specified in this Standard is described in AS/NZS 2312 as Paint Reference C32. Commonly known as surface tolerant epoxy, this product may be pigmented with aluminium or micaceous iron oxide. It may also be pr
20、oduced in a limited range of colours and is designed primarily for use as a single coat, high-build, self priming finish. NOTES: 1 This paint may be used as detailed for systems EPMI and EPM2 in AS/NZS 2312. 2 Appendix A contains recommendations and advice on information which should be provided by
21、the purchaser at the time of enquiry or order. 3 Additional information on the use and application of epoxy paints is contained in Appendix B. 1.2 REFERENCED DOCUMENTS A list of the documents referred to in this Standard is contained in Appendix C. 1.3 DEFINITIONS For the purpose of this Standard, t
22、he definitions given in AS/NZS 2310 and those below apply. 1.3.1 Epoxy mastic A high-build paint consisting essentially of epoxy resin base, polyamide or amine adduct or other hardener, together with various agents to improve wetting, adhesion and flexibility, with appropriate pigments and solvents
23、mixed together in the proportions recommended by the manufacturer. NOTE: Anti-settling and anti-sag agents may be necessary to provide high-build and prevent sagging during application. 1.4 SAFETY PRECAUTIONS Health and safety aspects referenced in Section 13 of AS/NZS 2312 should be followed in con
24、junction with the manufacturers safety data sheets (MSDSs). The Standard is downloaded from Standard Sharing 5 AS/NZS 3750.1:2008 COPYRIGHT S E C T I O N 2 M A T E R I A L S R E Q U I R E M E N T S 2.1 GENERAL The paint shall comply with the requirements detailed in Clauses 2.3 to 2.5 inclusive. Th
25、ese properties and requirements are summarized in Table 1. 2.2 CONDITIONS OF TEST Unless otherwise specified in this Standard, the following test conditions shall apply: (a) The test panel material and its preparation shall be in accordance with Appendix D. (b) The size of test panels shall be as sp
26、ecified in Table 1. (c) Conditions for testing shall be in accordance with AS/NZS 1580.101.5. (d) The spreading rate of paint shall be such that when applied by spraying it shall result in a dry film thickness of 125 m to 150 m per coat as determined by either AS/NZS 1580.108.1 or AS/NZS 1580.108.2.
27、 (e) Conditions for air-drying shall be in accordance with AS/NZS 1580.101.1. 2.3 LIQUID PAINT 2.3.1 Condition in container When each component is tested in accordance with AS/NZS 1580.103.1 at the time of delivery from the manufacturer/supplier, it shall be free from gel, coarse particles, skins an
28、d foreign matter. 2.3.2 Volume solids When determined in accordance with AS 1580.301.2, utilizing air-drying conditions of 7 days under routine conditions of AS/NZS 1580.101.1 in lieu of a 3 h drying period at 105C, the volume solids of the mixed paint shall be greater than 70 percent. 2.3.3 Storage
29、 properties 2.3.3.1 Degree of settling When stored at 23 3C in sealed, unopened containers for 12 months from the date of manufacture, the degree of settling of either component, when determined in accordance with AS/NZS 1580.211.1, shall be not less than 6. 2.3.3.2 Re-incorporation after storage Wh
30、en stored at 23 3C in sealed, unopened containers for up to 12 months from the date of manufacture, and tested in accordance with AS/NZS 1580.211.2, the components shall be readily re-incorporated and, when mixed in the recommended proportions, shall produce a paint of uniform consistency free from
31、lumps, gel and other defects. 2.4 SPRAY APPLICATION PROPERTIES 2.4.1 General Spray application properties shall be assessed using vertical steel panels prepared by abrasive blast cleaning to the Class Sa 2 requirements of AS 1627.4, using fresh garnet abrasive blast material. 2.4.2 Thinning If requi
32、red, thinning shall be done in accordance with the manufacturers instructions. AS/NZS 3750.1:2008 6 COPYRIGHT 2.4.3 Spraying technique The spraying technique shall be in accordance with manufacturers recommendations. 2.4.4 Pot-life assessment When initially mixed and thinned as appropriate to the me
33、thod of application, and again at the end of a 2 h standing period, a 4 L volume of the paint shall be tested in accordance with AS/NZS 1580.205.2 or AS/NZS 1580.205.4. When applied at the manufacturers maximum recommended thickness, it shall exhibit satisfactory spraying properties. When dry, the f
34、ilm shall be free from sags, runs, pinholes, craters and any other film defect. A slight orange peel effect is characteristic. NOTE: The panel should be retained for assessment of finish (see Clause 2.5.4). 2.5 APPLIED FILM NOTE: The results of tests in Clauses 2.5.6, 2.5.7 and 2.5.8 should only be
35、used as a guide to performance. These tests are considered to provide an accelerated test of resistance to conditions which are not expected to be encountered by the product during its useful service life. The tests are included to demonstrate that the paint contains sufficient properly cross-linked
36、 resin to provide long-term protection. 2.5.1 Curing and hard-dry properties When a test panel is prepared and tested in accordance with Appendix E, it shall withstand a load of 1.5 kg. 2.5.2 Colour When a tinplate test panel is coated with test paint, the colour of the paint film shall be an approx
37、imate match to that of the specified reference sample. 2.5.3 Recoating properties When one coat of paint is applied to a steel test panel and allowed to air-dry for 48 h and a second coat of the paint is applied and dried in the same manner, when tested in accordance with AS/NZS 1580.404.1 the recoa
38、ted panel shall not show any evidence of wrinkling, patchiness or lifting from the previous coat and, when tested in accordance with AS 1580.408.2, the intercoat adhesion rating shall be 4. 2.5.4 Finish When a coat of paint is applied to a steel test panel, air-dried for 7 days and examined in accor
39、dance with AS 1580.603.1, the film shall be of uniform colour and appearance, and be free of film defects. 2.5.5 Flexibility When one coat of paint is applied to a tinplate test panel, allowed to air-dry for 7 days and tested in accordance with AS 1580.402.1 using a 12 mm diameter mandrel, the paint
40、 shall show no cracking or detachment. NOTE: Damage in the form of stretch marks should not be cause for rejection. 2.5.6 Resistance to distilled water When a steel test panel is prepared and tested in accordance with Appendix F, it shall meet the following requirements after the 30-day immersion pe
41、riod: The Standard is downloaded from Standard Sharing 7 AS/NZS 3750.1:2008 COPYRIGHT Property of coating Method of test Requirements Blistering and wrinkling None Adhesion rating AS 1580.408.2 1 Colour AS/NZS 1580.601.1 Rating 4 Gloss of immersed part AS/NZS 1580.602.2 80% of unimmersed part Scrat
42、ch resistance AS/NZS 1580.403.1 1.5 kg Corrosion of substrate None 2.5.7 Resistance to oil When a steel test panel is prepared and tested in accordance with Appendix G, it shall meet the following requirements after the 24-hour immersion period: Property of coating Method of test Requirements Bliste
43、ring and wrinkling AS/NZS 1580.481.1.9None Adhesion rating AS 1580.408.2 1 Colour AS/NZS 1580.601.1 Rating 4 Gloss of immersed part AS/NZS 1580.602.2 80% of unimmersed part Scratch resistance AS/NZS 1580.403.1 1.5 kg 2.5.8 Resistance to alkali/acid When a steel test panel is prepared and tested in a
44、ccordance with Appendix H, it shall meet the following requirements after the 7-day immersion in each reagent: Property of coating Method of test Requirements Blistering and wrinkling AS/NZS 1580.481.1.9None Adhesion rating AS 1580.408.2 1 Scratch resistance AS/NZS 1580.403.1 1.5 kg Corrosion of sub
45、strate AS 1580.481.3 None NOTE: This test should not be carried out on aluminium pigmented paints. 2.5.9 Durability of the paint system When the paint system is prepared, exposed for 24 months and tested in accordance with Appendix I, its durability shall comply with the following ratings: Property
46、of coating Method of test Rating Erosion AS/NZS 1580.481.1.6 10% Cracking AS/NZS 1580.481.1.8 0 Blistering AS/NZS 1580.481.1.9 0 Flaking AS/NZS 1580.481.1.10 0 Corrosion AS 1580.481.3 0 Creep from score AS 1580.481.3 5 mm 2.6 MIXING RATIO The two components shall be supplied in separate containers i
47、n such concentrations that the mixing ratio of the base and the hardener shall be a simple ratio such as 1:1, 2:1, 3:1 or 4:1 by volume. AS/NZS 3750.1:2008 8 COPYRIGHT 2.7 ADDITIONAL TESTS NOTE: Appendix J gives information on consistency and gloss tests that may be included in a product specificati
48、on. TABLE 1 SUMMARY OF PROPERTIES OF EPOXY MASTIC (2-PACK) Clause number Property Requirement Test method Test panel material Minimum test panel size mm 2.3.1 Condition in container Free from gel, particles, skin AS/NZS 1580.103.1 N/A 2.3.2 Volume solids 70% AS 1580.301.2 N/A 2.3.3.1 Degree of settl
49、ing (12 months) Settlement rating 6 AS/NZS 1580.211.1 N/A 2.3.3.2 Re-incorporation after storage (12 months) Readily re- incorporated; uniform; consistency free from lumps and gel AS/NZS 1580.211.2 N/A 2.4 Spray application properties and pot-life Good spraying properties Free from sag, run, pinholes, craters AS/NZS 1580.205.2 AS/NZS 1580.205.4 Steel 1000 1000 2.5.1 Curing and hard-dry properties Withstand a scratch load of 1.5 kg