《BS EN 12332-1-1999 Rubber- or plastics-coated fabrics. Determination of bursting strength. Steel ball method.pdf》由会员分享，可在线阅读，更多相关《BS EN 12332-1-1999 Rubber- or plastics-coated fabrics. Determination of bursting strength. Steel ball method.pdf（8页珍藏版）》请在三一文库上搜索。
1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS EN 12332-1:1999 The Eu
2、ropean Standard EN 12332-1:1998 has the status of a British Standard ICS 59.080.40 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Rubber- or plastics-coated fabrics Determination of bursting strength Part 1: Steel ball method Licensed Copy: sheffieldun sheffieldun, na, Sat Oc
3、t 28 16:00:06 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS EN 12332-1:1999 This British Standard, having been prepared under the direction of the Sector Committee for Materials and Chemicals, was published under the authority of the Standards Committee and comes into effect on 15 February 1999 BSI
4、02-1999 ISBN 0 580 30370 5 Amendments issued since publication Amd. No.DateText affected National foreword This British Standard is the English language version of EN 12332-1:1998. It supersedes method 8A of BS 3424-6:1982, which is withdrawn by amendment. On eventual publication of BS EN 12332-2, B
5、S 3424-6:1982 will be withdrawn in its entirety. The UK participation in its preparation was entrusted to Technical Committee TCI/78, Coated fabrics, which has the responsibility to: aid enquirers to understand the text; present to the responsible European committee any enquiries on the interpretati
6、on, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. A list of organizations represented on this committee can be obtained on request to its secretary. Cross-references The British Standards which impl
7、ement international or European publications referred to in this document may be found in the BSI Standards Catalogue under the section entitled International Standards Correspondence Index, or by using the Find facility of the BSI Standards Electronic Catalogue. A British Standard does not purport
8、to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover
9、, the EN title page, pages 2 to 5 and a back cover. Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 16:00:06 GMT+00:00 2006, Uncontrolled Copy, (c) BSI CEN European Committee for Standardization Comite Europe en de Normalisation Europa isches Komitee fu r Normung Central Secretariat: rue de S
10、tassart 36, B-1050 Brussels 1998 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 12332-1:1998 E EUROPEAN STANDARDEN 12332-1 NORME EUROPE ENNE EUROPA ISCHE NORM July 1998 ICS 59.080.40 Descriptors: textiles, coated fabrics, fabrics
11、coated with rubber, fabrics coated with plastics, burst tests, determination, bursting strength English version Rubber- or plastics-coated fabrics Determination of bursting strength Part1: Steel ball method Supports textiles reve tus de caoutchouc ou de plastique De termination de la re sistance a l
12、e clatement Partie 1: Me thode a la bille Mit Kautschuk oder Kunststoff beschichtete Textilien Bestimmung der Berstfestigkeit Teil 1: Stahlkugelverfahren This European Standard was approved by CEN on 21 June 1998. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipul
13、ate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European Standard exi
14、sts in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national standards bo
15、dies of Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 16:00:06 GMT+00:00 2006, Uncontrolled Copy, (
16、c) BSI Page 2 EN 12332-1:1998 BSI 02-1999 Foreword This European Standard has been prepared by Technical Committee CEN/TC 248, Textiles and textile products, the Secretariat of which is held by BSI. This European Standard shall be given the status of a national standard, either by publication of an
17、identical text or by endorsement, at the latest by January 1999, and conflicting national standards shall be withdrawn at the latest by January 1999. EN 12332 deals with the determination of the bursting strength of coated fabrics. It consists of two parts: Part 1: Steel ball method Part 2: Hydrauli
18、c method NOTEPersons using this standard should be familiar with normal laboratory practice. This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user to establish appropriate safety and health practices and to ensure
19、compliance with any national regulatory conditions. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland,
20、Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom. Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 16:00:06 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ? Page 3 EN 12332-1:1998 BSI 02-1999 1 Scope This part of EN 12332 describes a meth
21、od for determining the bursting strength of coated fabrics using a mechanically operated steel ball. 2 Normative references This European Standard incorporates by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the tex
22、t and the publications are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated by amendment or revision. For undated references the latest edition of the publication referred to applies. EN
23、ISO 2231, Rubber- or plastics-coated fabrics Standard atmospheres for conditioning and testing. EN ISO 2286, Rubber- or plastics-coated fabrics Determination of roll characteristics. ISO 1302, Technical drawings Method of indicating surface texture. ISO 7500-1, Metallic materials Verification of sta
24、tic uniaxial testing machines Part 1: Tensile testing machines. 3 Principle A coated fabric is securely clamped between rigid coaxial apertures. A polished steel ball, traversing at a fixed speed, is pressed against the coated fabric specimen until failure occurs. The force required to cause failure
25、 and the displacement of the polished steel ball at failure are recorded. 4 Apparatus 4.1 Constant rate of extension (CRE) tensile testing machine, having the following characteristics: a) a traverse speed of (5,00,5) mm/s; b) a force range such that the failure force of the fabric under test will b
26、e between 10 % and 90 % of the upper force limit; c) the accuracy of the force-measuring system and the relative resolution of the force indicator shall conform to the maximum permissible values for a Class 1 machine as specified in ISO 7500-1; d) an autographic recorder. 4.2 Bursting attachment (se
27、e Figure 1). The test specimen is held securely by a ring mechanism of internal diameter (450,5) mm, when the centre of the test specimen is pressed against a polished steel ball of diameter (380,02) mm. The surface of the steel ball has an upper limit of the surface roughness parameter Raof 0,4 mm
28、(roughness grade number N5) as described in ISO 1302. The direction of motion of the ring clamp or steel ball shall be at right angles to the plane of the fabric. The clamping surfaces of the upper and lower clamps are grooved concentrically so that the crowns of the grooves of one plate fit the gro
29、oves of the other. The grooves are not less than 0,3 mm apart and not less than 0,15 mm deep. The grooves start no further than 3 mm from the edge of the aperture and are rounded to a radius of not greater than 0,4 mm. The lower inner edge of the lower clamp is rounded to a radius of 0,5 mm. 5 Test
30、specimens 5.1 Preparation of test specimens Cut six test specimens with a diameter of not less than 65 mm, in a diagonal arrangement across the full usable width of the coated fabric, in accordance with EN ISO 2286 (see Figure 2). 5.2 Conditioning Precondition the test specimens in accordance with E
31、N ISO 2231, but do not expose specimens to a temperature above 50 8C. Condition the test specimens for at least 24 h in one of the standard atmospheres for testing coated fabrics according to EN ISO 2231, ensuring exposure of all the surfaces to the air by, for example, placing the test specimens on
32、 wire gauze or mesh. When it is required to determine the properties of wet material, immerse each previously cut test specimen in distilled or deionized water and place under vacuum for 10 min. Immediately after removal from the water, blot each test specimen between two sheets of absorbent paper a
33、nd test at once. 6 Procedure Secure the test specimen in the ring clamp such that the coated side of the fabric faces away from the steel ball, and apply a pre-tension load of (5,00,5) N to the test specimen. Engage the autographic recorder and move the test specimen and steel ball towards each othe
34、r at a speed of (5,00,5) mm/s until the test specimen fails. NOTEFor fabrics coated on both faces, an agreement on the face to be tested should be achieved; otherwise it is recommended to test both faces and indicate this deviation in the test report. If the uncoated face is the external face in use
35、, the testing authority should be especially asked to test the material with the uncoated surface outside, and this deviation should be noted in the report. 7 Assessment of failure Ignore any failure that is confined to the edge of the clamp, and repeat the test on another test specimen. Ignore any
36、test results where the test specimen slips in the clamp, and repeat the test on another test specimen. NOTESlippage is normally evident as blurring of the marks left by the ring clamp on the test specimen. Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 16:00:06 GMT+00:00 2006, Uncontrolled C
37、opy, (c) BSI ? Page 4 EN 12332-1:1998 BSI 02-1999 All dimensions are in millimetres R 0,5 R 0,5 45 0,50 38 0,02 1 2 3 4 1Upper clamp 2Test specimen 3Lower clamp 4Steel ball Figure 1 Apparatus Many tensile machines automatically record the maximum force reached during a test and the distension at thi
38、s point. However, certain types of coated fabrics are known to fail progressively with a number of peak forces until the fabric is completely penetrated. In such cases the first peak recorded shall be regarded as the failure point of the fabric. The first peak is not necessarily the maximum force re
39、corded during a test and can only be determined from an autographic recording of force against distension. Tensile testing machines which are capable of automatically recording zero-slope yield points may detect low first peaks, but it is recommended that an autographic recording is obtained for all
40、 tests. 8 Calculation and expression of results For each test, record the force in newtons required to cause the failure of the test specimen, to the nearest newton. Calculate the arithmetic mean of the six results obtained. For each test, record the displacement of the steel ball required to cause
41、the failure of the test specimen, in millimetres, to the nearest 0,1 mm. Calculate the arithmetic mean of the six results obtained. Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 16:00:06 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ? Page 5 EN 12332-1:1998 BSI 02-1999 1 6 2 3 4 5 Usable width
42、 Figure 2 Recommended positions of test specimens 9 Test report The test report shall include the following particulars: a) reference to this European Standard; b) a simple designation of the tested material; c) the conditioning atmosphere used, or whether the specimens were tested in the wet state;
43、 d) the date of test; e) the number of specimens evaluated; f) the bursting strength in newtons as the mean of the six results obtained; g) the bursting distension in millimetres as the mean of the six results obtained; h) the standard deviation and confidence interval, if required; i) details of an
44、y deviations from the standard test procedure. Licensed Copy: sheffieldun sheffieldun, na, Sat Oct 28 16:00:06 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ? BSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |
45、 | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standa
46、rds in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality o
47、f our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BS
48、I offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: 020 8996 9001. Fax:
49、020 8996 7001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its