1、Tempers For Aluminum And Aluminum Alloy Products The Aluminum Association Incorporated 1525 Wilson Boulevard, Suite 600, Arlington, VA 22209 www.aluminum.org Revised November 2005 Supersedes: August 2001 Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Emplo
2、yees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from IHS -,-,- Use of the Information The Aluminurn Association has used its best efforts in compiling the information contained in this publication. Although the Associa
3、tion believes that its compilation procedures are reliable, it does not warrant, either expressly or impliedly, the accuracy or completeness of this information. The Aluminum Association assumes no responsibility or liability for the use of the information herein. All Aluminurn Association published
4、 standards, data, specifications and other material are reviewed at least every five years and revised, reaffirmed or withdrawn. Users are advised to contact The Aluminum Association to ascertain whether the information in this publication has been superseded in the interim between publication and p
5、roposed use. Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from IHS -,-,- Listed in this booklet are the tempers for alu
6、minum and aluminum alloy products registered with The Aluminum Association but not contained in The Associations Aluminum Standards and Data. Some of the registered tempers may be the subject of U.S. patents or patent applications, and their listing herein is not to be construed in any way as the gr
7、anting of a license under such patent rights. Tempers for wrought products are given on pages 1-27 and for castings on page 28. Inactive alloys and tempers are listed on pages 32-38. An explanation for The Aluminum Associations “Temper Designation System” is given in the Aluminum Standards and Data
8、and in the American National Standard ANSI H35.1. All new registrations and changes to previously registered mechanical property limits are marked and defined. In addition, the registration column also includes a revision date to indicate changes to the property limits originally registered. Copyrig
9、ht The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from IHS -,-,- When any aluminum or aluminum alloy material is produced in a temp
10、er not previously applied to that material, the temper, along with the alloy designation and product form to which it applies, may be registered with The Aluminum Association. PROCEDURE FOR INDIVIDUAL REGISTRATION OF TEMPERS 1. Any person, firm or corporation may apply to The Aluminum Association to
11、 register a new temper. 2. Selection of the temper designation usually is left to the discretion of the Technical Committee on Product Standards, but consideration will be given to the applicants choice when circumstances so warrant. 3. The temper is registered when, in the opinion of the Technical
12、Committee on Product Standards, it is judged to be technically correct and complete with respect to the following: a. The temper designation conforms to ANSI H35.1 “Alloy and Temper Designation Systems for Aluminum” (reprinted in The Aluminum Association manual Aluminum Standards and Data). b. The m
13、aterial is offered for sale in the proposed temper and is available for use by more than one user. c. The mechanical property limits applicable to the temper are included. (Limits are shown as tentative unless established in accordance with the data base criteria outlined under “Mechanical Propertie
14、s” in Section 6, “Standards Section” of the Aluminum Standards and Data). d. The following additional information is included when characteristics, in addition to mechanical properties, are specified for the temper: (1) Test methods by which conformance with the requirements for specified characteri
15、stics can be evaluated, OR (2) Details of the practice to be followed in producing the temper. e. The minimum tensile strength limit applicable to the O temper accompany the request for registration of H tempers. f. The indication of a variation in treatment of a basic T temper is limited to one add
16、itional digit (excluding zero) unless all available digits have been used, and except as provided for in the Appendix to ANSI H35.1. Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40
17、MDTNo reproduction or networking permitted without license from IHS -,-,- TEMPER REGISTRATION (continued) PROCEDURES FOR ALUMINUM ASSOCIATION TECHNICAL DIVISION (AATD) REGISTRATION OF TEMPERS A temper for an aluminum alloy material may be registered as an AATD temper when, through formal ballot of t
18、he Technical Committee on Product Standards, it is judged to be technically correct with respect to the following: a. The temper designation conforms to ANSI H35.1 “Alloy and Temper Designation Systems for Aluminum” (reprinted in The Aluminum Association manual Aluminum Standards and Data). b. The m
19、aterial is offered for sale in the proposed temper by more than one producer. c. The minimum and/or maximum mechanical property limits applicable to the temper are included. d. The following additional information is included when characteristics, in addition to mechanical properties, are specified
20、for the temper: (1) Test methods by which conformance with the requirements for the specified characteristics can (2) Details of the practices to be followed in.producing the temper. e. The minimum tensile strength limit applicable to the O temper accompany the request for registration of H tempers.
21、 The indication of a variation in treatment of a basicT temper is limited to one additional digit (excluding zero) unless all available digits have been used, and except as provided for in the Appendix to ANSI H35.1. be evaluated, OR f. g. The temper is not being applied to an alloy designated as ex
22、perimental (with prefix “X). REQUIREMENTS FOR PROPOSED CHANGES TO REGISTERED TEMPERS Proposed changes to a registered designations mechanical properties and/or characteristics: a. Require approval by formal ballot of the Technical Committee on Product Standards for registered tempers having “minimum
23、” and/or “maximum” mechanical property limits. b. Require a 30-day review by the Technical Committee on Product Standards for registered tempers having “tentative” mechanical property limits, or tempers applied to experimental alloys (with prefix “X”). The registrant has the final authority to chang
24、e the temper limits, provided the change complies with item 3 under Individual Registration of Tempers. Changes proposed by others than the registrant are acceptable only with the approval of the registrant. REQUIREMENTS FOR DELETION OF TEMPERS FROM THE REGISTRATION LIST 1. When any alloy is removed
25、 from the active alloy registration list, all tempers applicable to that alloy are automatically removed from the active temper registration list. 2. Approval of the Technical Committee on Product Standards through formal ballot is required to effect deletion of any registered temper from the active
26、 registration list, except as provided by the preceding sentence. iii Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from
27、 IHS -,-,- This page left intentionally blank. Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from IHS -,-,- ClaSSifiCati
28、On Of the listed properties is as specified in the COlUm - beginning WROUGHT PRODUCTS 1 100-1 23 on page 30. headed “Basis“ Tensile Strength, Alloy Temper Regis tered Thickness in. :longa tior Percent ir: ?in.or4 L Remarkg Product ksi - Yield 5.0 - 20.0 20.0 22.0 Basis Min Max Min - Min Min Min Min
29、- Min Max Min Min Max Min Max Min Max Min - Min Max Min Max Min Min - 1 Ult. 11.0 16.0 17.0 - 21 .o 22.0 24.0 23.0 BY Alumax - Alcoa Alcoa AATD Alcoa Alcoa AATD AATD AATD AATD AATD AATD Alcoa Alcoa Alcoa Alcoa Date 04/04/78 02/23/56 1 100-02 1100-Hl51 1100-Hl81 1 1 00-Hl 85 1 1 00-Hl 9 1100-Hl91 Fin
30、 Stock Tube Sheet Impact Wire Sheet 0.005-0.01 2 0.013-0.01 9 0.028 standard 2024 heat treatment. 12/21/78 12/21/78 Revised 03/25/98 68.0 71 .O 67.0 71 .O 59.0 61 .O 62.0 62.0 66.0 70.0 72.0 66.0 73.0 64.0 73.0 61 .O 66.0 69.0 68.0 67.0 66.0 65.0 60.0 75.0 - - - - 62.0 58.0 61 .O 57.0 39.0 40.0 40.0
31、 40.0 48.0 52.0 53.0 46.0 54.0 44.0 54.0 42.0 57.0 60.0 52.0 46.0 50.0 45.0 41 .O 57.0 - - - 10 8 10 8 Standard 2024 solution treatment and quench followed by 1 1 Yo nominal cold roll and 1% minimum stretcher stress relief. 0.750-1.300 1.301 -1.500 0.032-0.062 0.063-0.128 0.1 29-0.249 0.250-0.31 O U
32、p thru 0.249 0.250-0.499 0.500-1.499 1.500-2.249 2.250-3.250 Up thru 0.249 0.250-0.499 02/27/97 15 15 15 15 06/22/00 O 1 17/02 11 12 11 8 11 8 10 8 5 7 *Tentative 2027-T3512* 2027-T3511 22 12/08/04 1 1/29/04 Plate Extruded Profiles 0.500-1.500 1.501 -2.250 0.750-1.500 14 14 14 14 4 14 Fracture Touah
33、nessI4- min KI, For thicknesses 0.750-1.500 in. L-T direction 40 ksi . I i n T-L direction 38 ksi fi ootnotes appear beginning on page 3 1 Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:
34、15:40 MDTNo reproduction or networking permitted without license from IHS -,-,- the listed orooerties is as SDeCified in the column headed ?Basis?.? WROUGHT PRODUCT! 2038-209 lassification I Alloy Temper Registered Thickness in. Tensile Strength, Elongation Percent in Pin. or4 D Product ksi - Yield
35、20.0 - 44.0 41 .O 40.0 31 .O - - 70.0 66.0 70.0 66.0 71 .O 71 .O 73.0 68.0 Remarks 3asis? Min Min Ming Ming Min - - - Min6 Ming Min6 Ming Min6 Min6 Min6 Ming Olt. 40.0 - 50.0 62.0 62.0 46.0 - - 77.0 73.0 75.0 73.0 78.0 78.0 80.0 76.0 B Y Reynolds Reynolds Pechiney Alcoa Alcoa Alcoa Date 2038-T4 2038
36、-T6 Sheet Sheet 0.025-0.070 0.025-0.070 20 8 Automotive sheet. Automotive Sheet 1 O l l 0182 1 Oll 0182 12/1 0103 02/28/89 Revised 03/23/99 0311 5/88 Revised 03/09/98 0811 1 188 Revised 07/30/90 Alclad 2056-T3*? Sheet 15 16 0.063 - 0.1 26 0.1 27 - 0.236 0.032-0.249 0.032-0.125 0.126-0.249 Up thru 0.
37、124 0.125-0.249 0.250-0.499 2090-T3 2090-T83 2090-TE6 Sheet Sheet Extrusion 2097-T87 06/08/0 1 Plate 4.001 -5.000 5.001-6.000 Min6 Ming Minio Min6 Mingo Min1 - 5 62.0 62.0 60.0 60.0 60.0 57.0 - 56.0 56.0 55.0 55.0 55.0 52.0 - 6 4 1.5 5 4 1.5 Alcoa *Tentative Fracture Touahness14- min KI, For thickne
38、sses 4.001-5.000 in. L-T direction 32 ksi fi T-L direction 26 ksi fi S-L direction 18 ksi fi For thicknesses 5.001- 6.000 in. L-T direction 29 ksi fi T-L direction 25 ksi S-L direction 18 ksi fi Exfoliation Corrosion Resistance See Footnote 15.b Stress Corrosion Direct Tensile Specimens machined and
39、 tested in accordance with ASTM G47 shall show no evidence of stress corrosion failure when tested in the short transverse direction at 35.0 ksi and exposed for 30 days. Footnotes appei Deginning on page 3 1 Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS E
40、mployees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from IHS -,-,- ROUGHT PRODUCTS 97-2099 Classification of the listed Dra erties is as specified in the column headed “Basis” Thickness in. Tensile Strength, Yongation
41、Jercent in l in. or 4 D Registered Alloy Temper ksi Ult. - - Yield Remark# - lasis B Y AcCook Metals - Date Plate Min6 ving Winlo Min6 uing Win1 vin6 ving Min Min6 Ming MinO Min6 Ming Min” Min6 Ming Min“ - Min6 Ming MinIo Min6 Ming Minio - Mm Min6 Ming 64.0 66.0 65.0 63.0 64.0 64.0 62.0 64.0 62.0 62
42、.0 62.0 59.0 61 .O 61 .O 58.0 60.0 60.0 57.0 - 62.0 62.0 60.0 60.0 60.0 57.0 - 35.0 73.0 73.0 .58.0 60.0 57.0 57.0 58.0 56.0 57.0 58.0 55.0 57.0 57.0 54.0 56.0 56.0 52.0 55.0 55.0 52.0 - 56.0 56.0 55.0 55.0 55.0 52.0 - 25.0 68.0 68.0 10 8 2 9 7 2 9 7 2 5 4 1.5 5 4 1.5 5 4 1.5 !297-T87 06/21/00 Revis
43、ed 06/03/04 Fracture Touahnes-Min Kic For thicknesses 1.500-3.000 inches L-T direction 32 ksi fi T-L direction 27 ksi fi S-L direction 20 ksi 1 SOO-2.000 2.001-2.500 2.501-3.000 3.001 -4.000 4.001-5.000 5.001-6.000 4.001 -5.000 5.001-6.000 For thicknesses 3.001-4.000 inches L-T direction 31 ksi fi T
44、-L direction 27 ksi fi S-L direction 20 ksi fi For thicknesses 4.001-5.000 inches L-T direction 30 ksi fi T-L direction 26 ksi fi S-L direction 18 ksi fi For thicknesses 5.001-6.000 inches L-T direction 29 ksi $ T-L direction 25 ksi fi S-L direction 18 ksi fi Exfoliation Corrosion Resistance See Foo
45、tnote 15.b Stress Corrosion Resistance 30 days at 30 ksi when tested in the ST direction per ASTM G47. !397-T87 Alcoa 02/12/03 Plate 6 4 1.5 5 4 1.5 Stress Corrosion See footnote 4.b Exfoliation Corrosion See footnote 15.b Fracture Touchness - Min K I , For thicknesses 4.001 -5.000 L-T direction 32
46、ksi fi T-L direction 26 ksi fi S-L direction 18 ksi 6 For thicknesses 5.001 -6.000 L-T direction 29 ksi fi T-L direction 25 ksi fi S-L direction 18 ksi fi Note: Fracture toughness test parameters are defined in AMS 4328. Fracture Touahness13 - Min K , For thicknesses 0.250-0.300 inch L-T direction 1
47、 O 1 ksi fi T-L direction 75 ksi fi 2098-0 3098-T82 Pechine) Pechine) 06120103 06/20/03 Plate Plate 0.250 - 0.300 0.250 - 0.300 11 7 6 Stress Corrosion Direct tensile specimens machined and tested in accordance with ASTM G47 shall show no evidence of Stress Corrosion failure when tested in the long
48、transverse direction at 35.0 ksi and exposed for 30 days. 2099-T83 Alcoa 01/07/05 0.050-0.249 0.250-0.499 0.500-0.999 0.500-0.999 Min6 Min6 Min6 Ming - 6 75.0 78.0 79.0 73.0 - 67.0 69.0 71 .O 65.0 6 7 7 7 Tentative Extruded Profiles Footnotes appear beginning on page C Copyright The Aluminum Association Inc. Provided by IHS under license with AA Licensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 04/18/2007 04:15:40 MDTNo reproduction or networking permitted without license from IHS -