《BS-EN-10244-1-2009.pdf》由会员分享，可在线阅读，更多相关《BS-EN-10244-1-2009.pdf（12页珍藏版）》请在三一文库上搜索。
1、BS EN 10244-1:2009 ICS 25.220.40; 77.140.65 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW BRITISH STANDARD Steel wire and wire products Non- ferrous metallic coatings on steel wire Part 1: General principles Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Unc
2、ontrolled Copy, (c) BSI This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 May 2009. BSI 2009 ISBN 978 0 580 62602 9 Amendments/corrigenda issued since publication DateComments BS EN 10244-1:2009 National foreword This British Standard is the
3、 UK implementation of EN 10244-1:2009. It supersedes BS EN 10244-1:2001 which is withdrawn. The UK participation in its preparation was entrusted to Technical Committee ISE/26, Steel wire. A list of organizations represented on this committee can be obtained on request to its secretary. This publica
4、tion does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard cannot confer immunity from legal obligations. Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI
5、 BS EN 10244-1:2009 EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10244-1 April 2009 ICS 25.220.40; 77.140.65Supersedes EN 10244-1:2001 English Version Steel wire and wire products - Non-ferrous metallic coatings on steel wire - Part 1: General principles Fils et produits trfils en acier - Re
6、vtements mtalliques non ferreux sur fils dacier - Partie 1 : Principes gnraux Stahldraht und Drahterzeugnisse - berzge aus Nichteisenmetall auf Stahldraht - Teil 1: Allgemeine Regeln This European Standard was approved by CEN on 13 December 2008. CEN members are bound to comply with the CEN/CENELEC
7、Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN
8、 member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions. CEN
9、members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Swed
10、en, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2009 CENAll rights of exploitation in any form and by any means reserved worldwide for CEN national Members. R
11、ef. No. EN 10244-1:2009: E Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 2 Contents Page Foreword 3 1 Scope 4 2 Normative references 4 3 Terms and definitions .4 4 Requirements relating to coating .4 4.1 Requirements
12、 for the specific type of metal and alloy 4 4.2 Coating mass .4 4.3 Appearance of coating 5 4.4 Special finishes 5 4.5 Adherence of coating 5 5 Test conditions 5 5.1 Selection of samples .5 5.2 Determination of mass of coating 6 5.2.1 Gravimetric method .6 5.2.2 Other methods .7 5.3 Adherence test .
13、7 5.4 Retests 8 Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 3 Foreword This document (EN 10244-1:2009) has been prepared by Technical Committee ECISS/TC 30 “Steel wires”, the secretariat of which is held by AFNOR.
14、This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by October 2009, and conflicting national standards shall be withdrawn at the latest by October 2009. Attention is drawn to the possibility that some o
15、f the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10244-1:2001. This European Standard for non-ferrous metallic coating on steel wire is made up of the follo
16、wing parts: Part 1: General principles Part 2: Zinc or zinc alloy coatings Part 3: Aluminium coatings Part 4: Tin coatings Part 5: Nickel coatings Part 6: Copper, bronze or brass coatings According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countri
17、es are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
18、 Sweden, Switzerland and the United Kingdom. Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 4 1 Scope This part of this European Standard specifies the requirements for the mass, other properties and testing of non-fe
19、rrous metal coatings on steel wire and steel wire products of circular or other cross-section. This European Standard deals with requirements of general application and is of use for those coatings for which no particular requirements have been laid down in (EN 10244-2 to EN 10244-6). Deviations are
20、 possible, particularly if required for well-defined products. In such cases, appropriate requirements should be part of the relevant product standard. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edi
21、tion cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 10021, General technical delivery conditions for steel products EN 10218-1, Steel wire and wire products General Part 1: Test methods 3 Terms and definitions For the purpo
22、ses of this document, the following terms and definitions apply. 3.1 wire with non-ferrous metallic coating wire to which a non-ferrous metallic coating has been applied. NOTE Depending on the metal, the coating may be obtained by dipping in a bath of molten metal, by conversion using a bath of meta
23、llic salts in solution, by extrusion, by cladding, by electroplating using an electrolytic solution or by other methods. 4 Requirements relating to coating 4.1 Requirements for the specific type of metal and alloy The type, quality and grade of coating metal or alloy shall be stated at the time of e
24、nquiry and order. 4.2 Coating mass The coating mass shall be explicitly specified, preferably by reference to the appropriate product standard. If not the appropriate part of this European Standard shall apply. The mass of the coating shall preferably be expressed as being the mass of coating per un
25、it of surface area of bare wire (g/m2). Other expressions may be accepted, such as the quantity of coating per unit of weight of coated wire or the thickness of coating. The latter is generally expressed as being the minimum required thickness. NOTE The thickness of the coating may be converted into
26、 an equivalent mass per unit of bare wire surface or vice versa on the basis of the specific mass of the coating material (see Table 1). A coating of 1 m thickness corresponds to a total additional diameter of 2 m for the overall diameter of the coated wire. Licensed CopyChinese University of Hong K
27、ong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 5 Table 1 Coating mass g/m2 equivalent to a thickness of 1 m Metal or alloya Mass of coating (g/m2) Al 2,69 Cu 8,96 Cu-Sn 91-09 8,56 Cu-Zn 63-37 8,47 Ni 8,85 Sn 7,28 Zn Zn95/Al5 7,14 6,58 a Percentage compositio
28、ns expressed in % by weight (Cu-Zn 63- 37 = Cu 63%, Zn 37%) 4.3 Appearance of coating The coating shall be reasonably smooth, as evenly distributed as industrially practicable and not show discontinuities such as bare patches, dross contamination, etc. 4.4 Special finishes If the purchaser requires
29、a special finish e.g. wax-coating or additional requirements for the coating, these special details shall be agreed at the time of enquiry and order. The inspection methods shall be defined at the same time. 4.5 Adherence of coating The adherence wrapping test shall be carried out in accordance with
30、 EN 10218-1 and the coating shall adhere to the steel below the coating. It shall not crack or split to such an extent that slivers of coating can be removed by simply rubbing with the fingers. The flaking or removal during testing of small particles resulting from mechanical polishing of the coatin
31、g surface or by contact with the forming equipment shall not be considered to be a cause for rejection. The wrapping test shall be carried out on wire with a nominal diameter of 7,5 mm or less. Unless otherwise specified, the relationship between the diameter of the coiling mandrel and the diameter
32、of the wire shall be in accordance with 5.3. In the case of a diameter greater than 7,5 mm, the wrapping test shall be replaced by a bending test in which the wire is bent to least 90 around the mandrel. 5 Test conditions 5.1 Selection of samples 5.1.1 The number and the basis for the selection of t
33、est pieces shall be defined in the product specification. In the absence of such a definition, the manufacturer and purchaser shall agree between them on the degree of sampling. 5.1.2 When taking the samples, care shall be taken to avoid damaging the surface. Parts of the wire which are visibly dama
34、ged shall not be used. Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 6 5.1.3 A test piece of a suitable length for the specified tests shall be taken from one or both ends of each coil selected for sampling. 5.2 Dete
35、rmination of mass of coating 5.2.1 Gravimetric method 5.2.1.1 General The mass of coating shall be determined using a gravimetric method. The metallic coating on a surface of known area is dissolved in a suitable solution to remove the coating completely without attacking the surface of the steel wi
36、re. If necessary a suitable inhibitor is added to the solution. The resulting mass loss is determined by weighing the test piece before and after the coating has dissolved. 5.2.1.2 Procedure If necessary the test piece shall be degreased using an organic solvent which does not attack the coating and
37、 the test piece shall then be dried. Before stripping, the test piece shall be weighed with high accuracy i.e. better than 1 % of the assumed mass of the coating. The test piece shall be immersed fully in the stripping solution at ambient temperature and left until the coating dissolves completely.
38、A sufficient quantity of solution shall be used to limit any changes in the composition of the stripping solution. After stripping, the test piece shall be rinsed under running water and, if necessary, brushed to remove any loose substances which may be adhering to the surface; it shall then be plun
39、ged into alcohol or any other appropriate solvent, rapidly dried and once again weighed to the accuracy stipulated above. The surface area of the exposed surface shall then be determined to an accuracy of 1 % by measuring the dimensions of the test piece. 5.2.1.3 Calculation of the coating mass For
40、the calculation of the coating mass the following symbols are employed: m1: The mass of the sample before chemical stripping expressed in grams; m2: The mass of the sample after chemical stripping expressed in grams; A: The coated surface of the sample in mm2; l: The length of the sample in mm; d: T
41、he diameter of the chemically stripped wire (in case of round wire) in mm; m: Weight loss of the sample by the chemical stripping; mA: The mass of coating in g/m2. The mass of coating on the samples is: m = m1-m2 (in g) The mass of coating per unit surface area = 2 g/mm A m Licensed CopyChinese Univ
42、ersity of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 7 expressed in g/m2 - this becomes: 2 6 A g/m 10 A m m = (1) For round wire the surface area can be expressed as: A = d l (2) 3 2 2 10857 4 =,l d m = ( d l) d 1,962 10-3 (3) Combining (2) and (3)
43、 results in: g109621 3 2 =,dAm (4) or 3 2 109621 = d, m A (5) Combining (1) and (5) results 3 2 6 A 10962, 1 10 = d/m m m 962110 3 2 ,d m m = 9621 2 21 ,d m mm = in g/m2 (6) 5.2.2 Other methods Depending on the type of coating, other methods may be used to obtain the mass of the coating more simply
44、and more quickly. The use of these methods is authorized under the following conditions: proof of the validity of the method shall be supplied and in the event of any dispute, only the gravimetric method shall apply. 5.3 Adherence test If the wire diameter is less than or equal to 7,5 mm, the adhere
45、nce of the coating shall be tested by wrapping the wire for at least six tight turns around a cylindrical mandrel. Wires of diameter greater than 7,5 mm shall undergo a bending test at an angle of at least 90 around the mandrel. Unless otherwise specified in the subsequent parts of this standard or
46、in the product standard the relationship between the diameter of the mandrel and the diameter of the wire shall be in accordance with Table 2. Table 2 Diameter of mandrel for wrapping test Diameter of wire d Diameter of mandrel 4 mm 4d 4 mm 5d Licensed CopyChinese University of Hong Kong, 12/06/2009
47、 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 EN 10244-1:2009 (E) 8 5.4 Retests Testing and retesting shall be in accordance with EN 10021. Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 This page has been intentionally left blan
48、k Licensed CopyChinese University of Hong Kong, 12/06/2009 03:03, Uncontrolled Copy, (c) BSI BS EN 10244-1:2009 BSI Group Headquarters 389 Chiswick High Road, London, W4 4AL, UK Tel +44 (0)20 8996 9001 Fax +44 (0)20 8996 7001 standards BSI - British Standards Institution BSI is the independent nati
49、onal body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We wo