《BS-EN-ISO-6506-4-2005.pdf》由会员分享，可在线阅读，更多相关《BS-EN-ISO-6506-4-2005.pdf（22页珍藏版）》请在三一文库上搜索。
1、BRITISH STANDARD BS EN ISO 6506-4:2005 Metallic materials Brinell hardness test Part 4: Table of hardness values The European Standard EN ISO 6506-4:2005 has the status of a British Standard ICS 77.040.10 ? Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled
2、Copy, (c) BSI BS EN ISO 6506-4:2005 This British Standard was published under the authority of the Standards Policy and Strategy Committee on 13 January 2006 BSI 13 January 2006 ISBN 0 580 47565 4 National foreword This British Standard is the official English language version of EN ISO 6506-4:2005.
3、 It is identical with ISO 6506-4:2005. The UK participation in its preparation was entrusted by Technical Committee ISE/NFE/4, Mechanical testing of metals, to Subcommittee ISE/NFE/4/5, Indentation hardness testing, which has the responsibility to: A list of organizations represented on this subcomm
4、ittee can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “
5、Search” facility of the BSI Electronic Catalogue or of British Standards Online. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself confer immunity from lega
6、l obligations. aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep UK interests informed; monitor related international and European developments and promulgate them in the UK. Summar
7、y of pages This document comprises a front cover, an inside front cover, the EN ISO title page, the EN ISO foreword page, the ISO title page, pages ii to iv, pages 1 to 12, an inside back cover and a back cover. The BSI copyright notice displayed in this document indicates when the document was last
8、 issued. Amendments issued since publication Amd. No. DateComments Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 6506-4 December 2005 ICS 77.040.10 English Version Metallic materials
9、 - Brinell hardness test - Part 4: Table of hardness values (ISO 6506-4:2005) Matriaux mtalliques - Essai de duret Brinell - Partie 4: Tableaux des valeurs de duret (ISO 6506-4:2005) Metallische Werkstoffe - Hrteprfung nach Brinell - Teil 4: Tabelle zur Bestimmung der Hrte (ISO 6506-4:2005) This Eur
10、opean Standard was approved by CEN on 14 December 2005. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references
11、 concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into it
12、s own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Lux
13、embourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: rue de Stassart, 36 B-1050 Brussels 2005 CENAll rights of
14、exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 6506-4:2005: E Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI Foreword This document (EN ISO 6506-4:2005) has been prepared by Technical
15、Committee ISO/TC 164 “Mechanical testing of metals“ in collaboration with Technical Committee ECISS/TC 1 “Steel - Mechanical testing“, the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by
16、endorsement, at the latest by June 2006, and conflicting national standards shall be withdrawn at the latest by June 2006. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgiu
17、m, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. Endorsement notice The text of ISO 6506-4:2
18、005 has been approved by CEN as EN ISO 6506-4:2005 without any modifications. EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI Reference number ISO 6506-4:2005(E) INTERNATIONAL STANDARD ISO 6506-4 First edition 2005-12-15 M
19、etallic materials Brinell hardness test Part 4: Table of hardness values Matriaux mtalliques Essai de duret Brinell Partie 4: Tableaux pour les essais de duret EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ii Licensed Co
20、py: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI iii Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally
21、carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the wo
22、rk. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. Draft International Standards adopted by the technical c
23、ommittees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall n
24、ot be held responsible for identifying any or all such patent rights. ISO 6506-4 was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals, Subcommittee SC 3, Hardness testing. This first edition of ISO 6506-4 cancels and replaces Annex C of ISO 6506-1:1999. ISO 6506 consists of t
25、he following parts, under the general title Metallic materials Brinell hardness test: Part 1: Test method Part 2: Verification and calibration of testing machines Part 3: Calibration of reference blocks Part 4: Table of hardness values EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, S
26、un Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI iv Introduction Attention is drawn to the fact that in this part of ISO 6506, only the use of the hardmetal ball indenter is specified. The designation of the Brinell hardness is HBW and should not be confused with the former designation
27、HB, or HBS when a steel ball indenter was used. EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI 1 Metallic materials Brinell hardness test Part 4: Table of hardness values 1 Scope This part of ISO 6506 gives a table of the
28、 Brinell hardness values for use in tests on flat surfaces. 2 Determination of the Brinell hardness for testing on flat surfaces See Table 1. Table 1 Ball indenter, D mm Force-diameter ratio, 0,102 F/D2 30 15 10 5 2,5 1 Test force, F 10 29,42 kN14,71 kN 9,807 kN 4,903 kN 2,452 kN 980,7 N 5 7,355 kN
29、2,452 kN 1,226 kN 612,9 N 245,2 N 2,5 1,839 kN 612,9 N 306,5 N 153,2 N 61,29 N 1 294,2 N 98,07 N 49,03 N 24,52 N 9,807 N Mean diameter of the indentation, d mm Brinell hardness, HBW 2,40 1,200 0,600 0 0,240 653 327 218 109 54,5 21,8 2,41 1,205 0,602 4 0,241 648 324 216 108 54,0 21,6 2,42 1,210 0,605
30、 0 0,242 643 321 214 107 53,5 21,4 2,43 1,215 0,607 5 0,243 637 319 212 106 53,1 21,2 2,44 1,220 0,610 0 0,244 632 316 211 105 52,7 21,1 2,45 1,225 0,612 5 0,245 627 313 209 104 52,2 20,9 2,46 1,230 0,615 0 0,246 621 311 207 104 51,8 20,7 2,47 1,235 0,617 5 0,247 616 308 205 103 51,4 20,5 2,48 1,240
31、 0,620 0 0,248 611 306 204 102 50,9 20,4 2,49 1,245 0,622 5 0,249 606 303 202 101 50,5 20,2 2,50 1,250 0,625 0 0,250 601 301 200 100 50,1 20,0 2,51 1,255 0,627 5 0,251 597 298 199 99,4 49,7 19,9 EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncont
32、rolled Copy, (c) BSI 2 Table 1 (continued) Ball indenter, D mm Force-diameter ratio, 0,102 F/D2 10 5 2,5 1 30 15 10 5 2,5 1 Mean diameter of the indentation, d mm Brinell hardness, HBW 2,52 1,260 0,630 0 0,252 592 296 197 98,6 49,3 19,7 2,53 1,265 0,632 5 0,253 587 294 196 97,8 48,9 19,6 2,54 1,270
33、0,635 0 0,254 582 291 194 97,1 48,5 19,4 2,55 1,275 0,637 5 0,255 578 289 193 96,3 48,1 19,3 2,56 1,280 0,640 0 0,256 573 287 191 95,5 47,8 19,1 2,57 1,285 0,642 5 0,257 569 284 190 94,8 47,4 19,0 2,58 1,290 0,645 0 0,258 564 282 188 94,0 47,0 18,8 2,59 1,295 0,647 5 0,259 560 280 187 93,3 46,6 18,7
34、 2,60 1,300 0,650 0 0,260 555 278 185 92,6 46,3 18,5 2,61 1,305 0,652 5 0,261 551 276 184 91,8 45,9 18,4 2,62 1,310 0,655 0 0,262 547 273 182 91,1 45,6 18,2 2,63 1,315 0,657 5 0,263 543 271 181 90,4 45,2 18,1 2,64 1,320 0,660 0 0,264 538 269 179 89,7 44,9 17,9 2,65 1,325 0,662 5 0,265 534 267 178 89
35、,0 44,5 17,8 2,66 1,330 0,665 0 0,266 530 265 177 88,4 44,2 17,7 2,67 1,335 0,667 5 0,267 526 263 175 87,7 43,8 17,5 2,68 1,340 0,670 0 0,268 522 261 174 87,0 43,5 17,4 2,69 1,345 0,672 5 0,269 518 259 173 86,4 43,2 17,3 2,70 1,350 0,675 0 0,270 514 257 171 85,7 42,9 17,1 2,71 1,355 0,677 5 0,271 51
36、0 255 170 85,1 42,5 17,0 2,72 1,360 0,680 0 0,272 507 253 169 84,4 42,2 16,9 2,73 1,365 0,682 5 0,273 503 251 168 83,8 41,9 16,8 2,74 1,370 0,685 0 0,274 499 250 166 83,2 41,6 16,6 2,75 1,375 0,687 5 0,275 495 248 165 82,6 41,3 16,5 2,76 1,380 0,690 0 0,276 492 246 164 81,9 41,0 16,4 2,77 1,385 0,69
37、2 5 0,277 488 244 163 81,3 40,7 16,3 2,78 1,390 0,695 0 0,278 485 242 162 80,8 40,4 16,2 2,79 1,395 0,697 5 0,279 481 240 160 80,2 40,1 16,0 2,80 1,400 0,700 0 0,280 477 239 159 79,6 39,8 15,9 2,81 1,405 0,702 5 0,281 474 237 158 79,0 39,5 15,8 2,82 1,410 0,705 0 0,282 471 235 157 78,4 39,2 15,7 2,8
38、3 1,415 0,707 5 0,283 467 234 156 77,9 38,9 15,6 2,84 1,420 0,710 0 0,284 464 232 155 77,3 38,7 15,5 2,85 1,425 0,712 5 0,285 461 230 154 76,8 38,4 15,4 EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI 3 Table 1 (continued)
39、 Ball indenter, D mm Force-diameter ratio, 0,102 F/D2 10 5 2,5 1 30 15 10 5 2,5 1 Mean diameter of the indentation, d mm Brinell hardness, HBW 2,86 1,430 0,715 0 0,286 457 229 152 76,2 38,1 15,2 2,87 1,435 0,717 5 0,287 454 227 151 75,7 37,8 15,1 2,88 1,440 0,720 0 0,288 451 225 150 75,1 37,6 15,0 2
40、,89 1,445 0,722 5 0,289 448 224 149 74,6 37,3 14,9 2,90 1,450 0,725 0 0,290 444 222 148 74,1 37,0 14,8 2,91 1,455 0,727 5 0,291 441 221 147 73,6 36,8 14,7 2,92 1,460 0,730 0 0,292 438 219 146 73,0 36,5 14,6 2,93 1,465 0,732 5 0,293 435 218 145 72,5 36,3 14,5 2,94 1,470 0,735 0 0,294 432 216 144 72,0
41、 36,0 14,4 2,95 1,475 0,737 5 0,295 429 215 143 71,5 35,8 14,3 2,96 1,480 0,740 0 0,296 426 213 142 71,0 35,5 14,2 2,97 1,485 0,742 5 0,297 423 212 141 70,5 35,3 14,1 2,98 1,490 0,745 0 0,298 420 210 140 70,1 35,0 14,0 2,99 1,495 0,747 5 0,299 417 209 139 69,6 34,8 13,9 3,00 1,500 0,750 0 0,300 415
42、207 138 69,1 34,6 13,8 3,01 1,505 0,752 5 0,301 412 206 137 68,6 34,3 13,7 3,02 1,510 0,755 0 0,302 409 205 136 68,2 34,1 13,6 3,03 1,515 0,757 5 0,303 406 203 135 67,7 33,9 13,5 3,04 1,520 0,760 0 0,304 404 202 135 67,3 33,6 13,5 3,05 1,525 0,762 5 0,305 401 200 134 66,8 33,4 13,4 3,06 1,530 0,765
43、0 0,306 398 199 133 66,4 33,2 13,3 3,07 1,535 0,767 5 0,307 395 198 132 65,9 33,0 13,2 3,08 1,540 0,770 0 0,308 393 196 131 65,5 32,7 13,1 3,09 1,545 0,772 5 0,309 390 195 130 65,0 32,5 13,0 3,10 1,550 0,775 0 0,310 388 194 129 64,6 32,3 12,9 3,11 1,555 0,777 5 0,311 385 193 128 64,2 32,1 12,8 3,12
44、1,560 0,780 0 0,312 383 191 128 63,8 31,9 12,8 3,13 1,565 0,782 5 0,313 380 190 127 63,3 31,7 12,7 3,14 1,570 0,787 0 0,314 378 189 126 62,9 31,5 12,6 3,15 1,575 0,787 5 0,315 375 188 125 62,5 31,3 12,5 3,16 1,580 0,790 0 0,316 373 186 124 62,1 31,1 12,4 3,17 1,585 0,792 5 0,317 370 185 123 61,7 30,
45、9 12,3 3,18 1,590 0,795 0 0,318 368 184 123 61,3 30,7 12,3 3,19 1,595 0,797 5 0,319 366 183 122 60,9 30,5 12,2 EN ISO 6506-4:2005 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 19 12:42:04 GMT+00:00 2006, Uncontrolled Copy, (c) BSI 4 Table 1 (continued) Ball indenter, D mm Force-diameter ratio,
46、 0,102 F/D2 10 5 2,5 1 30 15 10 5 2,5 1 Mean diameter of the indentation, d mm Brinell hardness, HBW 3,20 1,600 0,800 0 0,320 363 182 121 60,5 30,3 12,1 3,21 1,605 0,802 5 0,321 361 180 120 60,1 30,1 12,0 3,22 1,610 0,805 0 0,322 359 179 120 59,8 29,9 12,0 3,23 1,615 0,807 5 0,323 356 178 119 59,4 2
47、9,7 11,9 3,24 1,620 0,810 0 0,324 354 177 118 59,0 29,5 11,8 3,25 1,625 0,812 5 0,325 352 176 117 58,6 29,3 11,7 3,26 1,630 0,815 0 0,326 350 175 117 58,3 29,1 11,7 3,27 1,635 0,817 5 0,327 347 174 116 57,9 29,0 11,6 3,28 1,640 0,820 0 0,328 345 173 115 57,5 28,8 11,5 3,29 1,645 0,822 5 0,329 343 17
48、2 114 57,2 28,6 11,4 3,30 1,650 0,825 0 0,330 341 170 114 56,8 28,4 11,4 3,31 1,655 0,827 5 0,331 339 169 113 56,5 28,2 11,3 3,32 1,660 0,830 0 0,332 337 168 112 56,1 28,1 11,2 3,33 1,665 0,832 5 0,333 335 167 112 55,8 27,9 11,2 3,34 1,670 0,835 0 0,334 333 166 111 55,4 27,7 11,1 3,35 1,675 0,837 5
49、0,335 331 165 110 55,1 27,5 11,0 3,36 1,680 0,840 0 0,336 329 164 110 54,8 27,4 11,0 3,37 1,685 0,842 5 0,337 326 163 109 54,4 27,2 10,9 3,38 1,690 0,845 0 0,338 325 162 108 54,1 27,0 10,8 3,39 1,695 0,847 5 0,339 323 161 108 53,8 26,9 10,8 3,40 1,700 0,850 0 0,340 321 160 107 53,4 26,7 10,7 3,41 1,705 0,852 5 0,341 319 159 106 53,1 26,6 10,6 3,42 1,710 0,855 0 0,342 317 158 106 52,8 26,4 10,6 3,43 1,715 0,857 5 0,343 315 157 105 52,5 26,2 10,5 3,44 1,720 0,8