《ISO-1163-1-1995.pdf》由会员分享,可在线阅读,更多相关《ISO-1163-1-1995.pdf(8页珍藏版)》请在三一文库上搜索。
1、INTERNATIONAL STANDARD IS0 1163-1 Third edition 1995-I 2-I 5 Plastics - Unplasticized poly(vinyl chloride) (PVC-U) moulding and extrusion materials - Part 1: Designation system and basis for specifications Plastiques - Poly(chlorure de viny/e) non plastifi6 (PVC-U) pour moulage et extrusion - Partie
2、 1: $&me de dksignation et base de spkcification Reference number IS0 1163-l 1995(E) . . Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking
3、 permitted without license from IHS -,-,- IS0 1163-1:1995(E) Foreword IS0 (the International Organization for Standardization) is a worldwide federation of national standards bodies (IS0 member bodies). The work of preparing International Standards is normally carried out through IS0 technical commi
4、ttees Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. IS0 collaborates closely with the In
5、ternational Electrotechnical Commission (IEC) on all matters of electrotechnical standardization Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member
6、 bodies casting a vote. lnternational Standard IS0 1163-l was prepared by Technical Committee lSO/rC 61, Plastics, Subcommittee SC 9, Thermoplastic materials. This third edition cancels and replaces the second edition (IS0 1163-1.1985), which has been technically revised The main changes concern the
7、 code-numbers and ranges for the impact strength and modulus of elasticity in table2. IS0 1163 consists of the following parts, under the general title Plastics - Unplasticized polyfvinyl chloride) (PVC-U) moulding and extrusion materials: - Part 1: Designation system and basis for specifications -
8、Part 2. Preparation of test specimens and determination of proper- ties 0 IS0 1995 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permissio
9、n in writing from the publisher International Organization for Standardization Case Postale 56 l CH-1211 Geneve 20 l Switzerland Printed in Switzerland ii Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 No
10、t for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking permitted without license from IHS -,-,- INTERNATIONAL STANDARD 0 ISO IS0 1163-1:1995(E) Plastics - Unplasticized poly(vinyl chloride) (PVC-U) moulding and extrusion materials - Part 1: Designation system and basis for specifications
11、 1 Scope 1.1 This part of IS0 1163 establishes a system of designation for unplasticized PVC thermoplastic material which may be used as the basis for specifications. 1.2 The types of PVC-U plastics are differentiated from each other by a classification system based on appro- priate levels of the de
12、signatory properties a) Vicat softening temperature b) impact strength (Charpy notched) c) modulus of elasticity and on information about basic polymer parameters, intended application and/or method of processing, important properties, additives, colorants, fillers and reinforcing materials. 1.3 Thi
13、s part of IS0 1163 is applicable to all unplasticized compositions of homopolymers and copolymers that contain at least 50 % (m/m) of vinyl chloride. It is also applicable to compositions containing chlorinated poly(vinyl chloride) and to compositions containing blends of one or more of the above-me
14、ntioned polymers, provided that the total amount of these polymers represents at least 50 % (m/m) of the polymer content of the composition It applies to materials ready for normal use in the form of powder, granules or pellets and to materials unmodified or modified by colorants, additives, fillers
15、, etc. This part of IS0 1163 does not apply to cellular plastics. 1.4 It is not intended to imply that materials having the same designation give necessarily the same perform- ance. This part of IS0 1163 does not provide engineering data, performance data or data on processing conditions which may b
16、e required to specify a material for a particular application and/or method or processing. If such additional properties are required, they may be determined in accordance with the test methods specified in part 2 of this International Standard, if suitable. 1.5 In order to specify a thermoplastic m
17、aterial for a particular application or to ensure reproducible processing, additional requirements may be given in data block 5 (see clause 3, introductory paragraph). Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/
18、9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 1163-1:1995(E) 0 is0 2 Normative references The following standards contain provisions which, through reference in this text, constitute provisions of this part of IS0 1163 At
19、 the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this part of IS0 1163 are encouraged to investigate the possibility of applying the most recent editions of the standards indicated below. Members of IEC and IS0 mai
20、ntain registers of currently valid International Standards. IS0 1043-I : 1987, Plastics - Symbols - Part 1. Basic polymers and their special characteristics. IS0 1163-2:1995, Plastics - Unplasticized polylvinyl chloride) (PVC-U) moulding and extrusion materials - Part 2: Preparation of test specimen
21、s and determination of properties. 3 Designation and specification system The designation and specification system for thermoplastics is based on the following standardized pattern Designation Identity block Individual-item block Description block (optional) International Standard Data Data Data Dat
22、a Data Number block block block block block block 1 2 3 4 5 The designation consists of an optional description block, reading “Thermoplastics”, and an identity block com- prising the International Standard number and an individual-item block. For unambiguous coding, the individual-item block is sub
23、divided into 5 data blocks comprising the following information: Data block 1: Data block 2: Identification of the plastic by its symbol PVC-U in accordance with IS0 1043-I (see 3.1) Position 1: Intended application or method of processing (see 3.2) Positions 2 to 8: Important properties, additives
24、and supplementary information (see 3 2) Data block 3: Designatory properties (see 3.3). Data block 4: Fillers or reinforcing materials and their nominal content (not included in this part of IS0 1163). Data block 5. For the purpose of specifications, a fifth data block may be added containing additi
25、onal information. The first character of the individual-item block shall be a hyphen. The data blocks shall be separated from each other by commas. If a data block is not used, this shall be indicated by doubling the separation sign, i.e. by two commas (,) 3.1 Data block 1 In this data block, after
26、the hyphen, PVC-U plastics are identified by the symbol “PVC-U”, in accordance with IS0 1043-I. 2 Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or n
27、etworking permitted without license from IHS -,-,- 0 IS0 IS0 1163-1:1995(E) 3.2 Data block 2 In this data block, information about intended application and/or method of processing is given in position 1 and information about important properties, additives and colour in positions 2 to 8. The code-le
28、tters used are specified in table 1. If information is presented in positions 2 to 8 and no specific information is given in position 1, the letter X shall be inserted in position 1 Table 1 - Code-letters used in data block 2 Code-letter Position 1 Code-letter Positions 2 to 8 B Blow moulding B Anti
29、blocking C Calendering C Coloured D Disc manufacture D Powder dry blend E Extrusion E Expandable F Extrusion of films F Special burning characteristics G General use G Granules H Coating H Heat ageing stabilized L Monofilament extrusion L Light or weather stabilized M Injection moulding N Natural (n
30、o colour added) P Impact modified 0 Compression moulding R Rotational moulding R Mould release agent s Sintering S Lubricated T Tape manufacture T Transparent v Thermoforming X No indication Y Increased electrical conductivity 2 Antistatic 3 Copyright International Organization for Standardization P
31、rovided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 1163-1:1995(E) Q IS0 Table 2 - Code-numbers used for designatory properties in data block 3 Vicat sof
32、tening temperature Impact strength Modulus of elasticity Code-number Range Code-number Range Code-number Range “C kJ/m* MPa 058 60 butlObut 2000 but 64but 40 28 2500 but 68 but 3000 074 72 but, 76 but 80 but 84 but 88but 92butG96 098 96but 100 but 104 but 108 but 112 but, 116 but 120 3.3 Data block
33、3 In this data block, the range of the Vicat softening temperature is represented by a 3-figure code-number (see 3.3.1), the range of the impact strength by a 2-figure code-number (see 3.3.2) and the range of the modulus of elasticity by a letter and a 2-figure code-number (see 3.3.3). The code-numb
34、ers are separated from each other by hyphens. If a property value falls on or near a range limit, the manufacturer shall state which range will designate the ma- terial If subsequent individual test values lie on, or on either side of, the cell limit because of manufacturing tol- erances, the design
35、ation is not affected. NOTE? Not all combinations of the values of designatory properties are provided in currently available polymers 3.3.1 Vicat softening temperature The Vicat softening temperature shall be determined in accordance with IS0 1163-2. The possible values of Vicat softening temperatu
36、re are represented by a 3-figure code-number as specified in table 2. 3.3.2 Impact strength The impact strength (Charpy notched) shall be determined in accordance with IS0 1163-2. The possible values of impact strength are divided into 3 ranges, each represented by a 2-figure code-number as specifie
37、d in table 2. 4 Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking permitted without license from IHS -,-,- 0 IS0 IS0 1163-1:1995(E) 3.3.3
38、Modulus of elasticity The modulus of elasticity shall be determined in accordance with IS0 1163-2. The possible values of modulus of elasticity are divided into 4 ranges, each represented by a 2-figure code-number as specified in table2 The fact that it is a tensile modulus shall be indicated by the
39、 code-letter T (tension) im- mediately preceding the code-number indicating the range. 3.4 Data block 4 Not included in this part of IS0 1163. 3.5 Data block 5 Indication of additional requirements in this optional data block is a way of transforming the designation of a ma- terial into a specificat
40、ion for a particular application. This may be done for example by reference to a suitable national standard or to a standard-like, generally established specification. 4 Examples of designations An unplasticized-PVC thermoplastic material (PVC-U), intended for the extrusion of pipes (E), in the form
41、 of a granular material (G), light stabilized (L), natural (N), with a Vicat softening temperature of 82 “C (082), an impact strength of 8 kJ/m2 (05) and a tensile modulus of elasticity of 3700 MPa (T33) would be designated. Description block International Standard Individual-item block (optional) N
42、umber block 1 2 3 I I I I I Thermoplastics Data block 1: symbol Data block 3: Position 1: Vicat softening temperature Position 2: impact strength Position 3: tensile modulus of elasticity Designation: IS0 1163-PVC-U,EGLN.082-OS-T33 5 An unplasticized-PVC thermoplastic material (PVC-U), intended for
43、blow moulding (B), in the form of a dry blend (D) with improved transparency (T), a Vicat softening temperature of 74 “C (074), an impact strength of 25 kJ/m2 (25) and a tensile modulus of elasticity of 2670 MPa (T28) would be designated: Description block International Standard Individual-item bloc
44、k (optional) Number block 1 2 3 Data block 1: symbol Data block 2: Position 1: BLow moulding Position 2: dry blend Position 3: improved transparency Data block 3: Position 1: Vicat softening temperature Position 2: impact strength Position 3: tensile modulus of elasticity Oeslgnation: IS0 1163-PVC-U
45、.BOT.074-25-TZB Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 1163-1:1995(E) KS 83.080.20
46、 Descriptors: plastics, thermoplastic resins, moulding materials, extrusion materials, vinyl chloride, unplasticized polyvinyl chloride, specifications, data blocks, designation Price based on 5 pages Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/26/2007 00:43:44 MDTNo reproduction or networking permitted without license from IHS -,-,-