1、 Reference number ISO 124:2008(E) ISO 2008 INTERNATIONAL STANDARD ISO 124 Fifth edition 2008-09-15 Latex, rubber Determination of total solids content Latex de caoutchouc Dtermination des matires solides totales Copyright International Organization for Standardization Provided by IHS under license w
2、ith ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 124:2008(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or vie
3、wed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in
4、 this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable
5、for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. COPYRIGHT PROTECTED DOCUMENT ISO 2008 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utiliz
6、ed in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax +
7、41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2008 All rights reserved Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or net
8、working permitted without license from IHS -,-,- ISO 124:2008(E) ISO 2008 All rights reserved iii Contents Page Foreword iv Introduction v 1 Scope 1 2 Normative references1 3 Principle1 4 Apparatus .1 5 Sampling.2 6 Procedure .2 6.1 General2 6.2 Heating at atmospheric pressure (70 C) Natural and syn
9、thetic rubber latex2 6.3 Heating at atmospheric pressure (105 C) Synthetic rubber latex 2 6.4 Heating at atmospheric pressure (up to 160 C) Synthetic rubber latex.2 6.5 Heating at reduced pressure Synthetic rubber latex.2 7 Expression of results 3 8 Precision.3 9 Test report3 Annex A (informative) D
10、rying conditions for synthetic latices at atmospheric pressure .4 Annex B (informative) Precision5 Bibliography7 Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or net
11、working permitted without license from IHS -,-,- ISO 124:2008(E) iv ISO 2008 All rights reserved Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally car
12、ried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
13、 ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare Interna
14、tional Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the
15、elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 124 was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee SC 3, Raw materials (including latex) for use in the rubber
16、industry. This fifth edition cancels and replaces the fourth edition (ISO 124:1997), of which it constitutes a minor revision to incorporate the two amendments ISO 124:1997/Amd.1:2006 and ISO 124:1997/Amd.2:2008, providing precision data and permitting the use of higher drying temperatures, respecti
17、vely. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 124:2008(E) ISO 2008 All rights reserved v Introductio
18、n The need in commercial practice to determine solids content rapidly has led to the introduction of higher drying temperatures. This new edition recognizes this requirement while retaining the older conventional methods. Copyright International Organization for Standardization Provided by IHS under
19、 license with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Boeing Co/5910770001 Not for Resale,
20、10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- INTERNATIONAL STANDARD ISO 124:2008(E) ISO 2008 All rights reserved 1 Latex, rubber Determination of total solids content WARNING Persons using this International Standard should be familiar with normal lab
21、oratory practice. This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user to establish appropriate safety and health practices and to ensure compliance with any national regulatory conditions. 1 Scope This Internatio
22、nal Standard specifies methods for the determination of the total solids content of natural rubber latex concentrate and synthetic rubber latices. These methods are not necessarily suitable for latex from natural sources other than the Hevea Brasiliensis, for vulcanized latex, for compounded latex o
23、r for artificial dispersions of rubber. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendme
24、nts) applies. ISO 123, Rubber latex Sampling 3 Principle A test portion of the latex is dried to constant mass under specified conditions, either at atmospheric pressure or under vacuum. The total solids content is determined by weighing before and after drying to constant mass. NOTE The determinati
25、on of the residue after drying for a specific period of time is the subject of ISO 3251. 4 Apparatus Standard laboratory apparatus, plus the following: 4.1 Flat-bottomed dishes, lipless, of diameter approximately 60 mm. 4.2 Ovens, capable of being maintained at 70 C 2 C, or at a selected temperature
26、 between 100 C and 160 C accurate to 5 C. 4.3 Vacuum oven, capable of being maintained at 125 C 2 C and at a pressure below 20 kPa1). 4.4 Analytical balance, capable of being read to 0,1 mg. 1) 1 kPa = 1 kN/m2. Copyright International Organization for Standardization Provided by IHS under license wi
27、th ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 124:2008(E) 2 ISO 2008 All rights reserved 5 Sampling Carry out sampling in accordance with one of the methods specified in ISO 123. 6 Procedure 6.1
28、General For natural rubber latex concentrate, proceed in accordance with 6.2 and for synthetic rubber latex proceed in accordance with 6.2, 6.3, 6.4 or 6.5. Perform the determination in duplicate. 6.2 Heating at atmospheric pressure (70 C) Natural and synthetic rubber latex Weigh, to the nearest 0,1
29、 mg, a dish (4.1). Pour into the dish 2,0 g 0,5 g of latex and determine the exact mass (m0) by weighing to the nearest 0,1 mg. Gently swirl the contents of the dish to ensure that the latex covers the bottom. If desired, approximately 1 cm3 of distilled water or water of equivalent purity may be ad
30、ded and mixed with the latex by swirling. Place the dish in the oven (4.2) so that it is horizontal, and heat it at 70 C 2 C for 16 h or until the test portion has lost its whiteness. Remove the dish from the oven and allow it to cool to ambient temperature in a desiccator. Remove the dish and weigh
31、. Return the dish to the oven for 30 min at 70 C 2 C. Remove the dish and allow it to cool to ambient temperature in a desiccator as before and reweigh. Repeat the drying procedure for periods of 30 min until the loss in mass between two successive weighings is less than 0,5 mg. Record the mass of t
32、he dried latex (m1). 6.3 Heating at atmospheric pressure (105 C) Synthetic rubber latex Proceed in accordance with 6.2, but heat the dish containing the latex at 105 C 5 C for 2 h or until the test portion has lost its whiteness. After allowing to cool in a desiccator and weighing, return the dish t
33、o the oven at 105 C 5 C for 15 min. If the loss in mass is greater than 0,5 mg, repeat the drying process. If, after heating at 105 C 5 C, the dried deposit becomes excessively sticky, repeat the determination in accordance with 6.2. NOTE Stickiness is symptomatic of oxidation of some rubbers when e
34、xposed to air at too high a temperature. 6.4 Heating at atmospheric pressure (up to 160 C) Synthetic rubber latex By agreement between the interested parties, the drying process can be carried out at temperatures up to 160 C to shorten drying times. NOTE The maximum drying temperature for CR latex i
35、s 130 C, while any rubber latex except CR in Table A.1 may be dried at up to 160 C. Proceed in accordance with 6.2 and 6.3, but heat the dish containing the latex at for instance 130 C 5 C for 40 min or 160 C 5 C for 20 min (see Annex A). After allowing to cool in a desiccator and weighing, repeat t
36、he drying for periods of 10 min until the loss in mass between two successive weighings is less than 0,5 mg. In the event of a dispute over the results, drying shall be done in accordance with 6.2. 6.5 Heating at reduced pressure Synthetic rubber latex Weigh, to the nearest 0,1 mg, a dish (4.1). Pou
37、r into the dish 1,0 g 0,2 g of latex and weigh to the nearest 0,1 mg. Add approximately 1 cm3 of distilled water or water of equivalent purity and mix by swirling, ensuring that the latex covers the bottom of the dish. Copyright International Organization for Standardization Provided by IHS under li
38、cense with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 124:2008(E) ISO 2008 All rights reserved 3 Place the dish in the vacuum oven (4.3) so that it is horizontal. Reduce the pressure slowly to av
39、oid foaming and splattering, and heat at 125 C for 45 min to 60 min at a pressure below 20 kPa. Release the vacuum slowly, remove the dish from the oven and allow to cool in a desiccator. Remove the dish and weigh. Repeat the above drying procedure for periods of 15 min until the loss in mass betwee
40、n two successive weighings is less than 0,5 mg. 7 Expression of results Calculate the total solids content, TSC, expressed as a percentage by mass of the latex, using the equation 1 0 TSC100 m m = where m0 is the mass, in grams, of the test portion before drying; m1 is the mass, in grams, of the fin
41、al dried material. The results of the duplicate determinations shall not differ by more than 0,2 % (mass/mass). NOTE Over a large number of determinations, the vacuum method (6.5) tends to give marginally lower values, but does not differ by more than 0,1 %. 8 Precision See Annex B. 9 Test report Th
42、e test report shall include the following: a) a reference to this International Standard; b) details of the drying method and temperature used; c) all details necessary for identification of the test sample; d) the average value of the results and the units in which they have been expressed; e) deta
43、ils of any unusual features noted during the determination; f) details of any operation not included in this International Standard or in the International Standard to which reference is made, as well as any operation regarded as optional. Copyright International Organization for Standardization Pro
44、vided by IHS under license with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 03:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 124:2008(E) 4 ISO 2008 All rights reserved Annex A (informative) Drying conditions for synthetic latices at atmospheric
45、pressure A.1 Suitable drying conditions for various synthetic latices have been determined, i.e. conditions which give a constant mass. These are summarized in Table A.1. The conditions given for each latex are not to be considered as required conditions, but as recommended conditions for the measur
46、ement of total solids content. A.2 CR (chloroprene rubber) latex should not be heated at more than 130 C, because of possible decomposition. Table A.1 Drying conditions at 130 C and 160 C Drying time min Latex a 130 C 160 C X-SBR 40 20 CR 30 Not applicable b VP 40 20 SBR 40 20 X-SBR (with antidegrad
47、ant) 40 20 NBR (with antidegradant) 40 20 X-NBR 40 20 X-NBR (with antidegradant) 40 20 X-MBR 40 20 a “X-” means “carboxylated”. b See Clause A.2. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Boeing Co/5910770001 Not for Resale, 10/25/2008 0
48、3:59:25 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 124:2008(E) ISO 2008 All rights reserved 5 Annex B (informative) Precision B.1 The precision data presented in Tables B.1 and B.2 were obtained in separate inter-laboratory test programmes (ITPs) carried out at different times