1、 Reference number ISO 15106-3:2003(E) ISO 2003 INTERNATIONAL STANDARD ISO 15106-3 First edition 2003-01-15 Plastics Film and sheeting Determination of water vapour transmission rate Part 3: Electrolytic detection sensor method Plastiques Film et feuille Dtermination du coefficient de transmission de
2、 vapeur deau Partie 3: Mthode utilisant un dtecteur lectrolytique Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,
3、- ISO 15106-3:2003(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In d
4、ownloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in
5、the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the addre
6、ss given below. ISO 2003 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs
7、member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2003 All rights reserved Copyright International Organization for Standardization P
8、rovided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 15106-3:2003(E) ISO 2003 All rights reserved iii Contents Page Forewordiv 1 Scope 1 2 Normative references . 1 3 Term
9、and definition. 1 4 Principle. 1 5 Test specimens . 2 6 Conditioning 2 7 Apparatus 2 8 Test conditions 3 9 Procedure 4 10 Calculation. 4 11 Test result 4 12 Precision 5 13 Test report . 5 Annex A (informative) Relationship between relative humidity and concentration of sulfuric acid solution 6 Copyr
10、ight International Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 15106-3:2003(E) iv ISO 2003 All rights reserved Foreword ISO (the
11、 International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committe
12、e has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechni
13、cal standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member b
14、odies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying a
15、ny or all such patent rights. ISO 15106-3 was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 11, Products. ISO 15106 consists of the following parts, under the general title Plastics Film and sheeting Determination of water vapour transmission rate: Part 1: Humidity detection s
16、ensor method Part 2: Infrared detection sensor method Part 3: Electrolytic detection sensor method Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permit
17、ted without license from IHS -,-,- INTERNATIONAL STANDARD ISO 15106-3:2003(E) ISO 2003 All rights reserved 1 Plastics Film and sheeting Determination of water vapour transmission rate Part 3: Electrolytic detection sensor method 1 Scope This part of ISO 15106 specifies an instrumental method for det
18、ermining the water vapour transmission rate of plastic film, plastic sheeting and multi-layer structures including plastics, using an electrolytic detection sensor. NOTE The method provides rapid measurement over a wide range of water vapour transmission rates. 2 Normative references The following r
19、eferenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 2528:1995, Sheet materials Determination of water vapour tra
20、nsmission rate Gravimetric (dish) method ISO 4593:1993, Plastics Film and sheeting Determination of thickness by mechanical scanning 3 Term and definition For the purposes of this document, the following term and definition apply. 3.1 water vapour transmission rate the amount of water vapour transmi
21、tted through unit area of test specimen per unit time under specified conditions NOTE Water vapour transmission rate is expressed in grams per square metre 24 hours g/(m224 h). 4 Principle The gas transmission cell is designed in such a way that, with the test specimen inserted, it is divided into a
22、 dry chamber and a controlled-humidity chamber. The dry side of the specimen is swept by a flow of dry carrier gas, and water vapour permeating through the specimen from the controlled-humidity chamber is carried by the carrier gas into an electrolytic cell. This cell contains two spiral wire electr
23、odes, coated with a thin layer of phosphorous pentoxide, mounted on the inside wall of a glass capillary. The carrier gas is passed through the capillary where the moisture it holds is quantitatively absorbed by the phosphorous pentoxide and decomposed electrolytically into hydrogen and oxygen by th
24、e application of a D.C. voltage of about 70 V to the electrodes. The mass of the moisture which permeates through the specimen and is decomposed per unit time is calculated from the electrolytic current required. Copyright International Organization for Standardization Provided by IHS under license
25、with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 15106-3:2003(E) 2 ISO 2003 All rights reserved 5 Test specimens 5.1 The specimens shall be representative of the material, be free from wrinkles, c
26、reases and pinholes, and have uniform thickness. Each specimen shall have a larger area than the transmission area of the cell used for the test, and shall be hermetically mounted. 5.2 Three specimens shall be used unless otherwise specified or agreed between the interested parties. NOTE For some pr
27、oducts, testing more than three specimens gives a more representative result. 5.3 Unless otherwise specified, determine the thickness of each specimen in accordance with ISO 4593 at three points that are equally spaced. 6 Conditioning Condition the specimens at 23 C 2 C and a relative humidity of (5
28、0 10) %. The period of conditioning shall be as stated in the relevant specification for the material. 7 Apparatus 7.1 An example of a suitable apparatus is shown in Figure 1. The apparatus includes a transmission cell with two chambers, a lower (dry) chamber and an upper (controlled-humidity) chamb
29、er between which a specimen is mounted, an electrolytic cell to determine the amount of water vapour transmitted, a flow meter, two drying tubes (containing e.g. molecular-sieve material) and a switch valve. 7.2 The transmission area shall be between 5 cm2 and 100 cm2. The temperature of the transmi
30、ssion cell shall be kept within 0,5 C of the test temperature by means of a temperature controller. 7.3 The flow meter shall be capable of measuring flow rates from 5 ml to 100 ml per minute. 7.4 The drying tubes shall be capable of drying the carrier gas down to the detection limit of the electroly
31、tic cell or lower. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 15106-3:2003(E) ISO 2003 All rights reser
32、ved 3 Key 1 Drying tubes (containing e.g. a molecular sieve) 2 Two-chamber transmission cell (with thermostatted liquid flowing through both halves) 3 Specimen 4 Glass-fibre plate impregnated with sulfuric acid solution 5 Electrolytic cell 6 Switch valve 7 Copper tubing for carrier-gas supply (in th
33、ermostatted liquid to bring gas to test temperature) Figure 1 Example of water vapour transmission rate measuring apparatus with electrolytic sensor 8 Test conditions The test conditions should preferably be chosen from those given in Table 1. Table 1 Choice of test conditions Set of test conditions
34、 Temperature C RH % 1 2 3 4 5 25 0,5 38 0,5 40 0,5 23 0,5 25 0,5 90 2 90 2 90 2 85 2 75 2 Test conditions other than these shall be agreed upon by the interested parties. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not
35、 for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 15106-3:2003(E) 4 ISO 2003 All rights reserved 9 Procedure 9.1 Measure the water vapour transmission rate of each specimen as described in 9.2 to 9.7. 9.2 Place a glass-fibre plate impregna
36、ted with a suitable sulfuric acid solution in the upper chamber to produce a constant humidity level. NOTE The relationship between relative humidity and the concentration of the sulfuric acid solution is shown in Annex A. 9.3 Place the specimen between the upper and lower chambers (see Figure 1), a
37、nd close the transmission cell to give a gastight assembly. 9.4 With the switch valve positioned so that the carrier gas follows the path A-B, feed carrier gas through the drying tubes into the lower chamber. NOTE The gas now bypasses the electrolytic cell and passes directly into the atmosphere. Th
38、is prevents the humid air which enters the lower chamber when a specimen is put in place from being carried into the electrolytic cell and moistening it, invalidating the test results. 9.5 Apply a constant D.C. voltage of about 70 V to the electrolytic cell. NOTE It is recommended that the electroly
39、tic cell be kept permanently switched on, unless it is not going to be used for a long period. 9.6 After about 30 min, position the switch valve so that the carrier gas follows the path C-B and passes through the electrolytic cell. Monitor the current. 9.7 When the current remains constant, indicati
40、ng that permeation has reached a steady state, record this value. 10 Calculation Calculate the water vapour transmission rate of each test specimen using the following equation: WVTR8,067 I A = where WVTR is the water vapour transmission rate of the specimen, expressed in grams per square metre 24 h
41、ours g/(m224 h; A is the transmission area, in square metres, of the test specimen; I is the electrolytic current, in amperes; 8,076 is the instrument constant. 11 Test result Calculate the test result as the arithmetic mean of the results obtained for each test specimen, rounding to the second plac
42、e of decimals if the value is less than one, and to two significant figures if the value is greater than one. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networ
43、king permitted without license from IHS -,-,- ISO 15106-3:2003(E) ISO 2003 All rights reserved 5 12 Precision The precision of this test method is not known because inter-laboratory data are not available. When inter-laboratory data are obtained, a precision statement will be added at the following
44、revision. 13 Test report The test report shall include the following information: a) a reference to this part of ISO 15106; b) the name of the apparatus used; c) the test conditions; d) all details necessary for identification of the sample tested; e) the method of preparation of the test specimens;
45、 f) the side of the test specimen which faced the supply of water vapour; g) the transmission area of the test specimen; h) the mean thickness of the specimen; i) the number of specimens tested; j) details of specimen conditioning; k) the test result; l) the date of the test. Copyright International
46、 Organization for Standardization Provided by IHS under license with ISO Licensee=Aramco HQ/9980755100 Not for Resale, 04/23/2007 03:34:43 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 15106-3:2003(E) 6 ISO 2003 All rights reserved Annex A (informative) Relationship b
47、etween relative humidity and concentration of sulfuric acid solution Relative humidity (%) 80 75 70 65 60 55 50 45 40 35 30 25 20 10 0 Temp. C Concentration of H2SO4 solution (% by mass) 0 0,31 1,20 3,36 8,23 15,0 23,6 33,9 45,2 55,7 66,8 74,9 81,2 87,8 95,7 100,0 5 0,35 1,33 3,59 8,53 15,7 24,5 34,
48、5 45,7 56,4 67,2 75,5 81,5 89,7 96,3 100,0 10 0,39 1,39 3,71 8,69 15,9 22,3 34,6 45,5 56,7 67,7 75,0 81,0 87,4 95,6 100,0 15 0,43 1,52 3,96 8,99 16,0 24,9 35,2 45,7 56,8 67,6 75,5 82,1 88,4 96,2 100,0 20 0,48 1,62 4,12 9,18 16,4 25,3 35,4 46,2 56,7 67,3 75,3 81,6 87,8 94,7 100,0 25 0,52 1,72 4,34 9,43 16,7 25,9 35,6 45,9 56,8 66,5 74,9 81,7 87,6 94,3 100,0 30 0,58 1,82 4