1、 Reference number ISO 1522:2006(E) ISO 2006 INTERNATIONAL STANDARD ISO 1522 Third edition 2006-12-01 Paints and varnishes Pendulum damping test Peintures et vernis Essai damortissement du pendule ISO 1522:2006(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes
2、licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. Th
3、e ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care ha
4、s been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. ISO 2006 All rights reserved. Unless otherwise specified, no part of this publication may be
5、reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41
6、 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2006 All rights reserved ISO 1522:2006(E) ISO 2006 All rights reserved iii Contents Page Foreword iv Introduction v 1 Scope . 1 2 Normative references. 1 3 Principle. 1 4 Apparatus 1 5 Samplin
7、g 4 6 Test panels 4 7 Procedure 5 8 Expression of results . 5 9 Precision 5 10 Supplementary test conditions. 6 11 Test report . 6 Annex A (normative) Calibration of the Knig pendulum 7 Annex B (normative) Calibration of the Persoz pendulum 8 Bibliography. 9 ISO 1522:2006(E) iv ISO 2006 All rights r
8、eserved Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for w
9、hich a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all
10、 matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are c
11、irculated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held resp
12、onsible for identifying any or all such patent rights. ISO 1522 was prepared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee SC 9, General test methods for paints and varnishes. This third edition cancels and replaces the second edition (ISO 1522:1998), which has been technicall
13、y revised. The main changes are the following. The references to the original national standards, DIN 53157 (Knig pendulum) and NF T 30-016 (Persoz Pendulum), and to the ASTM standard ASTM D 4366 have been deleted since Germany, France and ASTM have adopted ISO 1512. The hardness of the ball bearing
14、s for the Persoz pendulum has been corrected. For the Persoz pendulum, the tolerance on the time for damping from a 12 displacement to a 4 displacement on a polished plate-glass panel has been changed from 10 s to 15 s. A preferred minimum dry-film thickness of the coating under test of 30 m has bee
15、n added. For the Knig pendulum, it is common practice to measure the number of swings. A note has been added explaining how the number of swings can be converted into the time for the amplitude of swing to decrease. ISO 1522:2006(E) ISO 2006 All rights reserved v Introduction Two test procedures are
16、 considered in some detail, namely those of Knig and Persoz. The instruments embody the same principle that the amplitude of oscillation of a pendulum touching a surface decreases more rapidly the softer the surface but differ in respect of dimensions, period and amplitude of oscillation. The intera
17、ction between the pendulum and the paint film is complex, depending as it does on both elastic and viscoelastic properties, and it is not possible to establish a general relationship between results obtained by the two tests. Therefore, only one type of pendulum should be used in a given series of m
18、easurements of damping time. The following considerations may serve as a guide when considering which pendulum may offer an advantage for a particular purpose. a) On surfaces with a low coefficient of friction, the Persoz pendulum may skid, which would invalidate results; however, this occurs only r
19、arely with paints and varnishes. b) It should be noted that both instruments reflect the sensitivity of the physical properties of a paint to its environment, and the test therefore should be under controlled conditions of temperature and humidity and in the absence of draughts. The thickness of the
20、 paint film and the nature of the substrate may also affect the damping times. -,-,- INTERNATIONAL STANDARD ISO 1522:2006(E) ISO 2006 All rights reserved 1 Paints and varnishes Pendulum damping test 1 Scope This International Standard specifies two methods of carrying out a pendulum damping test on
21、a coating of paint, varnish or other, related, product. It is applicable to single coatings and to multicoat systems. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated re
22、ferences, the latest edition of the referenced document (including any amendments) applies. ISO 1513, Paints and varnishes Examination and preparation of samples for testing ISO 1514, Paints and varnishes Standard panels for testing ISO 2808, Paints and varnishes Determination of film thickness ISO
23、15528, Paints, varnishes and raw materials for paints and varnishes Sampling 3 Principle A pendulum resting on a coating surface is set into oscillation and the time for the oscillation amplitude to decrease by an amount specified in this International Standard is measured. The shorter the damping t
24、ime, the lower the hardness. 4 Apparatus 4.1 Pendulum. 4.1.1 Both the pendulums, as described in 4.1.2 and 4.1.3, comprise an open framework connected by a cross-bar on the under face of which two balls are inset to serve as the fulcrum, the lower end of the framework being formed into a pointer. Th
25、e two pendulums differ in shape, mass, swinging time and other details, as described in 4.1.2 and 4.1.3. The pendulum shall be used away from draughts and vibrations. The use of a protective enclosure is recommended. ISO 1522:2006(E) 2 ISO 2006 All rights reserved 4.1.2 The Knig pendulum (see Figure
26、 1) rests on two tungsten-carbide balls of (5 0,005) mm diameter, of hardness (1 600 32) HV 30 1), and (30 0,2) mm apart and is counterpoised (to adjust the natural frequency of oscillation) by means of a weight sliding on a vertical rod attached to the cross-bar. On a polished plate-glass panel, th
27、e period of oscillation shall be (1,40 0,02) s and the time for damping from a 6 displacement to a 3 displacement shall be (250 10) s. The total mass of the pendulum shall be (200 0,2) g. Dimensions in millimetres Key 1 counterpoise (adjustable) 2 cross-bar, width 12 0,1 3 ball, 5 0,005 4 frame 5 ti
28、p Figure 1 Knig pendulum 1) HV = Vickers hardness determined in accordance with ISO 6507-1 2. ISO 1522:2006(E) ISO 2006 All rights reserved 3 4.1.3 The Persoz pendulum (see Figure 2) rests on two tungsten-carbide balls of (8 0,005) mm diameter, of hardness (1 600 32) HV 30 1) and (50 1) mm apart. A
29、counterpoise is not provided. On a polished plate- glass panel, the period of oscillation shall be (1 0,01) s and the time for damping from a 12 displacement to a 4 displacement on the same substrate shall be (430 15) s. The total mass of the pendulum shall be (500 0,1) g and its centre of gravity a
30、t rest shall be (60 0,1) mm below the plane of the fulcrum, the pointer tip being (400 0,2) mm below the plane of the fulcrum. Dimensions in millimetres Key 1 ball, 8 0,005 2 centre of gravity Figure 2 Persoz pendulum ISO 1522:2006(E) 4 ISO 2006 All rights reserved 4.2 Instrument stand. The stand fo
31、r supporting test panel and pendulum is common to both pendulums and comprises a heavy supported vertical rod to which is attached a horizontal table with a flat working surface, the dimensions of which may conveniently be 95 mm 110 mm and not less than 10 mm thick. The stand also has a stirrup to s
32、upport the pendulum away from the table and a mechanism for shock-free lowering of the pendulum on to the test panel. 4.3 Scale. The front of the stand shall be marked to show angular displacement of the pendulum from a centre point, indicating the rest position of the pendulum, through 6 and 3 for
33、a Knig pendulum and through 12 and 4 for a Persoz pendulum. The scale may be moved horizontally, and locked in position so that the zero marking and the test position of the pendulum tip coincide. This scale may be marked on a mirror, or a mirror may be placed behind the scale, to assist in eliminat
34、ing parallax errors during observation. 4.4 Stopwatch, or other timing device, for timing the oscillation damping of the pendulum. 4.5 Polished plate (float) glass panel, for calibrating the pendulum. 5 Sampling Take a representative sample of the product to be tested (or of each product in the case
35、 of a multicoat system), as specified in ISO 15528. Examine and prepare each sample for testing, as specified in ISO 1513. 6 Test panels 6.1 Substrate Select the substrate from one of those specified in ISO 1514, ensuring that the panels are plane, rigid and free from distortion. Metal or glass pane
36、ls are recommended, with dimensions of approximately 100 mm 100 mm 5 mm. 6.2 Preparation and coating Unless otherwise specified, prepare each test panel in accordance with ISO 1514 and then coat it by the specified method with the product or system under test. The test coating shall then be smooth a
37、nd free from surface irregularities. 6.3 Drying and conditioning Dry (or stove) and age (if applicable) each coated test panel for the specified time and under the conditions specified by contract between the interested parties. Before testing, condition the test panels at a temperature of (23 2) C
38、and relative humidity of (50 5) %, unless otherwise specified, for a minimum of 16 h. Fingerprints, dust or other contamination on the surface will result in lower accuracy. The coated panels should therefore be stored and handled in an appropriate way. 6.4 Thickness of coating Determine the thickne
39、ss, in micrometres, of the dried coating by one of the procedures specified in ISO 2808. The minimum dry-film thickness of the coating should preferably be 30 m. ISO 1522:2006(E) ISO 2006 All rights reserved 5 7 Procedure 7.1 Calibration of the instruments Calibrate the instrument using the procedur
40、es specified in Annexes A and B. 7.2 Ambient conditions Unless otherwise specified, test panels shall be tested at (23 2) C and a relative humidity of (50 5) % (see also ISO 3270). 7.3 Determination of pendulum damping time Determine pendulum damping time on three different parts of the same test pa
41、nel. Place the panel on the table with the paint film uppermost. Gently bring the pendulum onto the panel surface. Deflect the pendulum, without lateral displacement of the fulcrum, through the appropriate angle (6 for the Knig pendulum, 12 for the Persoz pendulum) and allow it to rest against the s
42、top provided. Release the pendulum and simultaneously start the stopwatch or other timing device. NOTE 1 In the case of automatic versions, the damping time will be measured automatically. Record the time, in seconds, for the amplitude of swing to decrease from either 6 to 3 (Knig pendulum) or from
43、12 to 4 (Persoz pendulum). NOTE 2 For the pendulum damping test using the Knig pendulum, it is common practice to measure the number of swings. The time for the amplitude of swing to decrease can be calculated by multiplying the number of swings by 1,4 s. 8 Expression of results Record each result a
44、nd the mean of the three determinations to the nearest second. 9 Precision 9.1 Knig pendulum 9.1.1 Repeatability limit (r) The repeatability limit r is the value below which the absolute difference between three single test results, each mean of duplicates, can be expected to lie when this method is
45、 used under repeatability conditions. In this case, the test results are obtained on identical material by one operator in one laboratory within a short interval of time using the standardized test method. In this International Standard, r is 5 swings, with a 95 % probability. 9.1.2 Reproducibility
46、limit (R) The reproducibility limit R is the value below which the absolute difference between three single test results, each the mean of duplicates, can be expected to lie when this method is used under reproducibility conditions. In this case, the test results are obtained on identical material b
47、y operators in different laboratories using the standardized test method. In this International Standard, R is 10 swings, with a 95 % probability. -,-,- ISO 1522:2006(E) 6 ISO 2006 All rights reserved 9.2 Persoz pendulum 9.2.1 Repeatability limit (r) The repeatability limit r is the value below whic
48、h the absolute difference between three single test results, each mean of duplicates, can be expected to lie when this method is used under repeatability conditions. In this case, the test results are obtained on identical material by one operator in one laboratory within a short interval of time us
49、ing the standardized test method. In this International Standard, r is 3 % of their mean value, with a 95 % probability. 9.2.2 Reproducibility limit (R) The reproducibility limit R is the value below which the absolute difference between three single test results, each the mean of duplicates, can be expected to lie when this method is us