1、INTERNATIONAL STANDARD IS0 1890 Third edition 1997-05- 15 Reinforcement yarns - Determination of twist Fils de renfort 1 Dktermination de la torsion Reference number IS0 1890: 1997(E) Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Techni
2、cal Standards 1/9972545001 Not for Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 1890: 1997(E) Foreword IS0 (the International Organization for Standardization) is a worldwide federation of national standards bodies (IS0 member bodies). The
3、 work of preparing International Standards is normally carried out through IS0 technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non- gov
4、ernmental, in liaison with ISO, also take part in the work. IS0 collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. Draft International Standards adopted by the technical committees are circulated to the member bodies for
5、voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. International Standard IS0 1890 was prepared by Technical Committee ISORC 61, Plastics, Subcommittee SC 13, Composites and reinforcement fibres. This third edition cancels and rep
6、laces the second edition (IS0 1890:1986), which has been technically revised. 0 IS0 1997 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without per
7、mission in writing from the publisher. International Organization for Standardization Case postale 56 l CH-1211 Geneve 20 l Switzerland Internet central iso.ch x.400 c=ch; a=400net; p=iso; o=isocs; s=central Printed in Switzerland ii Copyright International Organization for Standardization Provided
8、by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,- INTERNATIONAL STANDARD IS0 IS0 1890: 1997(E) Reinforcement yarns - Determination of twist 1 Scope This Internatio
9、nal Standard specifies a method for the determination of twist in yarns made from textile glass, carbon or aramid filaments. The method applies to single yarns (one twist) and to folded or cabled yarns (two or more twists). For folded and cabled yarns, the method is generally applied only to the fin
10、al twist step. This International Standard is applicable to package-wound yarns. If the measurement is carried out on yarns taken from a beam (or warp) or from a fabric, the result is of an indicative nature only. The method is not applicable to products made from staple fibres. 2 Normative referenc
11、es The following standards contain provisions which, through reference in this text, constitute provisions of this International Standard. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this International Stand
12、ard are encouraged to investigate the possibility of applying the most recent editions of the standards indicated below. Members of IEC and IS0 maintain registers of currently valid International Standards. IS0 2:1973, Textiles - Designation of the direction of twist in yarns and related products. I
13、S0 291: -A Plastics - Standard atmospheres for conditioning and testing. , IS0 1889: 1997, Reinforcement yarns - Determination of linear density. 3 Definition For the purposes of this International Standard, the following definition applies. 3.1 Z twist or S twist: The twist in a product if, when it
14、 is held in a vertical position, the spirals or helices formed by the fibres or filaments around its axis incline in the same direction as the central portion of the letter Z or S, respectively. (See IS0 2:1973, clause 2). 1) To be published. (Revision of IS0 291:1977) 1 Copyright International Orga
15、nization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 1890:1997(E) IS0 4 Principle The twist in a specimen of known length is
16、 removed by untwisting, i.e. by turning one of the ends of with regard to the other, until all the elements (yarns, filaments) constituting the specimen are parallel. the specimen The direction of twist in the yarn is noted and the value of the twist is expressed eliminate the twist in 1 m of yarn.
17、as the number of turns needed to The determination of the twist must allow for the fact that the take-off system may have an influence on the result. Thus when the yarn is taken off tangentially, the degree of twist inserted by the twist frame is not changed. On the other hand, if the yarn is taken
18、off over-end, the measured twist is modified depending on the circumference of the bobbin. It will increase or decrease depending whether the yarn is taken off from alternate sides of the package. The method specified in this International Standard is based on the tangential take-off system. If requ
19、ired, the over-end twist can be either measured or an approximate value calculated using the following equation: T over-end = Ttangential k -IL 7cD where 1 - 7cD corresponds to the twist induced by over-end take-off; D is the diameter, in metres at the place on the bobbin where the specimen is taken
20、. 5 Apparatus 5.1 Twist tester, i.e. an apparatus which has two clamps, one moving horizontally, the other rotating, mounted on a bar. The twist tester shall satisfy the following conditions: It shall be capable of measuring the number of turns to the nearest turn. - The clamps shall grip the yarn w
21、ithout slipping and shall not damage the yarn. - The tester shall include a device capable accuracy of +I mm. of measuring the length of the yarn between the clamps to an - It shall be possible to adjust the tension in the yarn between the clamps to a given value calculated as a function of the nomi
22、nal linear density of the yarn. In practice however, this tension, particularly for single yarns (and the final twist step in folded or cabled yarns) does not affect the result. For routine checks and also when the measurement of the elongation of the yarn resulting from untwisting is not required,
23、this adjustment tension can be omitted, making sure however that the specimen is clamped so that it is just taut. The initial distance between the clamps shall be of 500 mm k 1 mm. - For carbon-fibre yarn with no twist or with a twist of less than 20 turns per metre, the yarn specification or the pe
24、rson ordering the determination may stipulate that a stand with a fixed clamp be incorporated to make it possible to test a specimen of length L given by 4 m G L G 5 m. For the calculation of the twist, the actuat length shall be measured to an accuracy of 0,05 m. 2 Copyright International Organizat
25、ion for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 IS0 1890:1997(E) 5.2 Dissection needle or thin blade. 5.3 Magnifying glass,
26、for examination of specimen, used to facilitate the separation of the yarn. 6 Test specimens The determination elementary unit*) or is based laboratory on measurements carried out on three specimens taken consecutively from an sample3). The yarn specification or the person requesting the determinati
27、on may stipulate that the determination be performed on a (specified) higher number of specimens which are generally taken from adjacent positions in the elementary unit or laboratory sample. Moreover, it may be stipulated th at the dete rmi nation be repeated at diffe rent places wit hin the eleme
28、ntary u laboratory sample 1 either at given m eterages or in the cyli ndrical pa .rt of the package if it is not all of this shape. nit or 7 Conditioning and text atmosphere No conditioning is required. However, in cases of dispute, the dertermination shall be carried out in a standard atmosphere as
29、 defined in IS0 291. 8 Procedure 81 . Single yarns 8.1.1 If required, adjust the tension in the yarn to 0,25 cN/tex + 0,l cN/tex. 8.1.2 If the linear density of the yarn is not known, determine it by the method specified in IS0 1889. 8.1.3 Ensure that the elementary unit or laboratory sample to be e
30、xamined is free of external damage. If necessary, remove yarn from the elementary unit or laboratory sample to obtain undamaged yarn. 8.1.4 Take off yarn tangentially (perpendicularly to the bobbin axis) and bring it directly, without cutting it, to the twist tester, fixing it first to the rotating
31、clamp, then to the sliding clamp. Make sure that, during these clamping operations, the yarn is just taut, first between the elementary unit or laboratory sample and rotating clamp, then between the two clamps. 8.15 Set the twist tester counter to zero. 8.1.6 Turn the rotating clamp in the direction
32、 which eliminates the twist until it becomes possible to insert a dissection needle or thin blade between the filaments from the sliding clamp up to the rotating clamp. If necessary, use a magnifying glass to assist in inserting the needle and also to verify that all twist has been removed. 8.1.7 Re
33、cord the number of turns on the counter and also the twist direction (Z or S, as per IS0 2). 8.1.8 Repeat the measurement on the two other specimens. 2) The elementary unit (as defined in IS0 1886:1990, Reinforcement f - reset the counter to zero and make sure that the specimen is under slight tensi
34、on so as to keep it straight; - determine the degree of twist, taking into account the actual length of the specimen; - if necessary (for cabled yarns), repeat the operation on the previous twist step. 9 Expression of results Calculate, for each specimen, the twist T, in turns per metre, using the e
35、quation T A/ =- L where r metre. A/ is the number of turns necessary to untwist the specimen; L is the length, in metres, under standard tension prior to untwisting. Calculate, from the measurements made on the three specimens, the average of the twist, 7, in turns pe Report this value as the result
36、 of the determination. If more than three specimens were taken for the determination (see clause 6), the results obtained for the specimens in each determination shall be dealt with in accordance with the referring yarn specificatio specified by the person ordering the determination. various n or as
37、 10 Precision The precision of this test method is not known because interlaboratory data are not available. Interlaboratory data are being obtained and a precision statement will be added at the next revision. 11 Test report The test report shall include the following information: a a reference to
38、this International Standard; b) all details necessary for identification of the yarn examined; c) the sampling procedure used and the length of the specimens if not 0,5 m; Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standard
39、s 1/9972545001 Not for Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,- 0 IS0 IS0 1890:1997(E) d) the individual result of each determination (direction of twist and value of twist) and, if required, the results for each specimen; e) details of an
40、y operation not specified in this International Standard, as well as any incident liable to have had an affect on the results; f) the date of the test. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not f
41、or Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 1890: 1997(E) ICS 59.100.01 Descriptors: plastics, reinforced plastics , rei aramid fibres, tests, determination, twisti w nforcin g materials, textile glass yarns, mineral fibres, textile gl
42、ass fibres, carbon fibres, Price based on 5 pages Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:32:13 MDTNo reproduction or networking permitted without license from IHS -,-,-