1、A Reference number ISO 6270-1:1998(E) INTERNATIONAL STANDARD ISO 6270-1 First edition 1998-04-01 Paints and varnishes Determination of resistance to humidity Part 1: Continuous condensation Peintures et vernis Dtermination de la rsistance lhumidit Partie 1: Condensation continue ISO 6270-1:1998(E) I
2、SO 1998 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from the publisher. International Organization for Standardiza
3、tion Case postale 56 CH-1211 Genve 20 Switzerland Internetcentraliso.ch X.400c=ch; a=400net; p=iso; o=isocs; s=central Printed in Switzerland ii ContentsPage 1Scope.1 2Normative references.1 3Principle2 4Required supplementary information .2 5Apparatus.2 6Sampling 2 7Test panels.3 8Method of exposur
4、e of test panels.3 9Examination of test panels.3 10Precision 4 11Test report4 Annex A (normative) Required supplementary information5 ISOISO 6270-1:1998(E) iii Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies)
5、. The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non
6、- governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. Draft International Standards adopted by the technical committees are circulated to the member bodies
7、 for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. International Standard ISO 6270-1 was prepared by Technical Committee ISO/TC 35, Paints and varnishes, Subcommittee 9, General test methods for paints and varnishes. It cance
8、ls and replaces ISO 6270:1980, of which it constitutes a minor technical revision. It differs from ISO 6270:1980 in that the angle of the panels to the horizontal has been changed from (15 5) to (60 5) and the temperature of the air below the panels is maintained at (38 2) C rather than at that of t
9、he water itself. Work has shown that the results do not differ substantially between the two sets of conditions. At the date of publication, ISO 6270 consisted of only one part, under the general title Paints and varnishes Determination of resistance to humidity: Part 1: Continuous condensation Othe
10、r parts will be added at a later date. One of these parts will be ISO 11503:1995, Paints and varnishes Determination of resistance to humidity (intermittent condensation), which will be renumbered into this series. Annex A forms an integral part of this part of ISO 6270. -,-,- -,-,- INTERNATIONAL ST
11、ANDARD ISOISO 6270-1:1998(E) 1 Paints and varnishes Determination of resistance to humidity Part 1: Continuous condensation 1 Scope This part of ISO 6270 is one of a series of standards dealing with the sampling and testing of paints, varnishes and related products. It specifies a method for determi
12、ning the resistance of paint films, paints systems and related products to conditions of high humidity in accordance with the requirements of coating or product specifications. The method is applicable to coatings both on porous substrates such as wood, plaster and plasterboard and on non-porous sub
13、strates such as metal. It provides an indication of the performance likely to be obtained under severe conditions of exposure where continuous condensation occurs on the surface. The procedure may reveal failures of the coating (including blistering, staining, softening, wrinkling and embrittlement)
14、 and deterioration of the substrate. 2 Normative references The following standards contain provisions which, through reference in this text, constitute provisions of this part of ISO 6270. At the time of publication, the editions indicated were valid. All standards are subject to revision, and part
15、ies to agreements based on this part of ISO 6270 are encouraged to investigate the possibility of applying the most recent editions of the standards indicated below. Members of IEC and ISO maintain registers of currently valid International Standards. ISO 1512:1991, Paints and varnishes Sampling of
16、products in liquid or paste form. ISO 1513:1992, Paints and varnishes Examination and preparation of samples for testing. ISO 1514:1993, Paints and varnishes Standard panels for testing. ISO 2808:1997, Paints and varnishes Determination of film thickness. ISO 3270:1984, Paints and varnishes and thei
17、r raw materials Temperatures and humidities for conditioning and testing. ISO 3696:1987, Water for analytical laboratory use Specification and test methods. ISO 4628-1:1982, Paints and varnishes Evaluation of degradation of paint coatings Designation of intensity, quantity and size of common types o
18、f defect Part 1: General principles and rating schemes. ISO 4628-2:1982, Paints and varnishes Evaluation of degradation of paint coatings Designation of intensity, quantity and size of common types of defect Part 2: Designation of degree of blistering. ISO 4628-3:1982, Paints and varnishes Evaluatio
19、n of degradation of paint coatings Designation of intensity, quantity and size of common types of defect Part 3: Designation of degree of rusting. -,-,- ISO 6270-1:1998(E) ISO 2 ISO 4628-4:1982, Paints and varnishes - Evaluation of degradation of paint coatings Designation of intensity, quantity and
20、 size of common types of defect Part 4: Designation of degree of cracking. ISO 4628-5:1982, Paints and varnishes - Evaluation of degradation of paint coatings Designation of intensity, quantity and size of common types of defect Part 5: Designation of degree of flaking. 3 Principle A coated test pan
21、el is exposed to continuous condensation and the effects of the exposure are evaluated by criteria agreed in advance between the interested parties, these criteria usually being of a subjective nature. 4 Required supplementary information For any particular application, the test method specified in
22、this part of ISO 6270 needs to be completed by supplementary information. The items of supplementary information are given in annex A. 5 Apparatus 5.1 The apparatus shall be constructed of chemically resistant materials and consist essentially of an electrically heated water bath, designed so that t
23、he cover is formed by the blanking panels (see 5.5) or test panels, the upper faces of which are exposed to the environment (see 5.2). It is preferable for the apparatus to be designed so that it will accommodate test panels of size 150 mm x 100 mm. 5.2 The sides of the water bath shall be suitably
24、insulated to ensure that the temperature in the air space above the water when measured approximately 25 mm below the test panels is maintained at a uniform temperature of (38 2) C unless otherwise specified (see annex A, item e). NOTE Temperatures of 49 C and 60 C are recommended if 38 C is too low
25、. 5.3 The apparatus shall be operated in a draught-free environment maintained at (23 2) C. NOTE This test method will not work if the ambient temperature is higher than the test temperature, as no condensation will be formed on the test panels. 5.4 The top of the bath shall be designed so that the
26、test panels are held at the preferred angle of (60 5) to the horizontal to permit drainage of condensed water, and shall be such that water draining from one panel does not come into contact with another. An angle of (15 5) may be used on old equipment if specified (see the foreword). 5.5 Suitable i
27、nert blanking panels shall be provided for use in setting up the apparatus and if the number of test panels is insufficient to form a complete cover. 5.6 The water used should preferably be of at least grade 3 purity as defined in ISO 3696. Water of lower quality may be used, but problems may arise
28、with build-up of insoluble matter in the water bath, which will require regular cleaning. 5.7 The water shall be maintained at a constant level by means of an automatic control device. 6 Sampling Take a representative sample of the product to be tested (or of each product in the case of a multicoat
29、system), as specified in lSO 1512. Examine and prepare the sample for testing, as specified in ISO 1513. -,-,- ISO ISO 6270:1998(E) 3 7 Test panels 7.1 Material and dimensions Unless otherwise specified or agreed, the test panels shall be of burnished steel complying with ISO 1514, and of minimum di
30、mensions 70 mm x 100 mm x 0,3 mm. NOTE As the results can be significantly affected by the thickness of the substrate, it is important to ensure that the dimensions of the panels are appropriate to the end use for which the coating is being tested. 7.2 Preparation and coating Unless otherwise specif
31、ied, prepare each test panel in accordance with ISO 1514 and then coat it by the specified method with the product or system under test. For many purposes, it is sufficient to coat only one face of the test panel. However, it is necessary to specify whether the back and/or edges of the panel are to
32、be sealed and, if so, whether it should be with the product or system under test or with a suitable sealant (see annex A, item b). 7.3 Drying and conditioning Dry (or stove) and age (if applicable) each coated test panel for the specified time under the specified conditions, and, unless otherwise sp
33、ecified, condition them in a standard atmosphere in accordance with ISO 3270 for at least 16 h, with free circulation of air and without exposing them to direct sunlight. The test procedure shall then be carried out as soon as possible. 7.4 Thickness of coating Determine the thickness, in micrometre
34、s, of the dry coating using one of the non-destructive procedures described in ISO 2808. 8 Method of exposure of test panels Carry out the determination in duplicate, unless otherwise specified. 8.1 Set up the apparatus with blanking panels in position and allow the apparatus to come to equilibrium.
35、 When the conditions specified in 5.2 are attained, swiftly replace the blanking panels with the test panels so that the test surface faces the water. NOTE It is recommended that a control specimen of a paint with known durability be included with each series of test panels. In order to prevent a ga
36、lvanic couple, the test panels shall not be allowed to come into contact with each other or with other metallic material. If the panels have not been edged (see 7.2) then non-metallic filler strips shall be used between the panels. 8.2 Run the apparatus continuously throughout the prescribed test pe
37、riod, maintaining the conditions specified in clause 5.2 except for a short daily interruption (see annex A, item f) to inspect, re-arrange or remove test panels or to check and, if not performed automatically, adjust the level of the water. 9 Examination of test panels 9.1 Make a periodic examinati
38、on of the panels as quickly as possible, taking care not to damage the surfaces under test. Do not remove the panels for more than 30 min in any 24 h period. Immediately replace panels which have been removed by blanking panels. Panels may be blotted with absorbent paper to examine them more clearly
39、, but shall then be immediately returned to the apparatus. They shall not be allowed to dry fully. -,-,- ISO 6270-1:1998(E) ISO 4 9.2 At the end of the specified test period, immediately examine the test surface for signs of deterioration in accordance with the appropriate part of ISO 4628 (see anne
40、x A, item h). 9.3 If required, keep the panels in the standard atmosphere in accordance with ISO 3270 for the specified period and examine the test surfaces for deterioration. 9.4 If it is required to examine the substrate for signs of attack, remove the coating by means of a non-corrosive paint rem
41、over unless otherwise specified. 10 Precision The concept of precision is not applicable to this part of ISO 6270 due to the subjective nature of the assessment (see clause 3). Users of this part of ISO 6270 should be aware that, because of this subjective assessment of the deterioration of the coat
42、ing, the actual rating will depend upon a number of factors. These include the evaluation method (ISO 4628), the preparation of the test panels, the thickness of the coating, and the drying and conditioning of the test panels. 11 Test report The test report shall contain at least the following infor
43、mation: a) all details necessary to identify the product tested; b) a reference to this part of ISO 6270 (ISO 6270-1); c) the items of supplementary information referred to in annex A; d) a reference to the international or national standard, product specification or other document supplying the inf
44、ormation referred to in c) above; e) any deviation, by agreement or otherwise, from the test procedure described; f) the angle of the panels in the apparatus; g) the temperature of the test; h) the results of the test, in terms of the stated requirements; i) the dates and duration of the test. -,-,-
45、 ISO ISO 6270:1998(E) 5 Annex A (normative) Required supplementary information A.1 The items of supplementary information listed in this annex shall be supplied as appropriate to enable the method to be carried out. A.2 The information required should preferably be agreed between the interested part
46、ies and may be derived, in part or totally, from an international or national standard or other document related to the product under test. a) Material, dimensions and surface preparation of substrate (see 7.1). b) Method of application of test coating and details of sealing of edges and backs of th
47、e test panels (if required) (see 7.2). c) Thickness, in micrometres, of the dry coating, including the method of measurement and whether it is a single coating or a multicoat system (see 7.4). d) Duration and conditions of drying (or stoving) and ageing (if applicable) of the coated test panels befo
48、re testing (see 7.3). e) Test temperature (see 5.2). f) Duration of test period, including whether the test period is to be interrupted at intervals (for example during weekends) (see 8.2). g) When inspection of the test coating is to be carried out, including details of recovery period if applicable (see 9.3). h) How inspection of the test coating is to be carried out, and what characteristics are to be considered in evaluating its resistance properties (see clauses 9 and 10). i) Method of paint removal if the substrate is to be