《ISO-6791-1981.pdf》由会员分享，可在线阅读，更多相关《ISO-6791-1981.pdf（5页珍藏版）》请在三一文库上搜索。
1、International Standard INTERNATIONAL ORGANIZATION FOR STANDARDIZATIONWdEYHAPOHAR OPl-AHM3Al:.;i;. “gsil p.j*i.:d j ?., . ;i Carbonaceous materials for the production of aluminium - Pitch for electrodes - Determination of content of quinoline-insoluble material Prod$ (,?, ! i ,Z j ;) j .,a,+u is I UD
2、C 665.777.43 : 669.713.7 : 543.21 Ref. No. IS0 6791-1981 (E) Descriptors : extraction metallurgy, electrodes, aluminium, pitch (materials), chemical analysis, determination of content, gravimetric analysis, insoluble matter. Price based on 3 pages Foreword IS0 (the international Organization for Sta
3、ndardization) is a worldwide federation of national standards institutes (IS0 member bodies). The work of developing Inter- national Standards is carried out through IS0 technical committees. Every member body interested in a subject for which a technical committee has been set up has the right to b
4、e represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. Draft International Standards adopted by the technical committees are circulated to the member bodies for approval before their acceptance as Internationa
5、l Standards by the IS0 Council. International Standard IS0 6791 was developed by Technical Committee ISO/TC 47, Chemistry, and was circulated to the member bodies in December 1979. It has been approved by the member bodies of the following countries : Australia Egypt, Arab Rep. of Austria France Bel
6、gium Germany, F. R. Brazil Hungary Bulgaria Italy Canada Korea, Rep. of China Poland Czechoslovakia Portugal Romania South Africa, Rep. of Sweden Switzerland Thailand United Kingdom USSR The member body of the following country expressed disapproval of the document on technical grounds : Netherlands
7、 This International Standard has also been approved by the International Union of Pure and Applied Chemistry (IUPAC). 0 International Organization for Standardization, 1981 0 Printed in Switzerland INTERNATIONAL STANDARD IS0 6791-1961 (E) Carbonaceous materials for the production of aluminium - Pitc
8、h for electrodes - Determination of content of quinoline-insoluble material 1 Scope and field of application This international Standard specifies a conventional gravimetric method for the determination of the content of quinoline- insoluble material in pitch used in the production of aluminium. 2 R
9、eference IS0 6257, Carbonaceous materials used in the production of aluminium - Pitch for electrodes - Sampling. Dry the material in the oven (5.4), controlled at 105 to 110 Y, for 1 h. Allow to cool in a desiccator and weigh. Repeat the process of heating, cooling and weighing until the difference
10、between two consecutive weighings does not exceed 0,005 g. Store the dried material in a desiccator. 5 Apparatus Ordinary laboratory apparatus and 5.1 Water bath, capable of being controlled at 70 to 80 OC. 3 Principle Extraction of a test portion with quinoline, at a specified temperature and for a
11、 specified period. Filtration and weighing of the residue. 4 Reagents and materials During the analysis, use only reagents of recognized analytical grade. 4.1 Quinoline, freshly distilled, boiling between 235 and 237 OC at 1 013 mbart). WARNING - Risk of poisoning by inhalation or swallow- ing. Irri
12、tating to skin and eyes. Prevent inhalation of vapour and contact with skin, eyes and clothing. 4.2 Toluene. WARNING - Highly flammable. Harmful by inhalation. Keep away from sources of ignition. No smoking. Do not empty into drains. Take precautionary measures against static discharges. 4.3 Filter
13、aid, diatomaceous silica type, free from organic compounds, and chemically neutral. The particle sizes shall be within the range 1 to 40 pm and the average particle size shall be within the range 6 to 10 pm. 5.2 Hartley funnel, or equivalent, having a disc diameter of 70 mm (a suitable type is shown
14、 in the figure). 5.3 Glass fibre filter pads, of diameter 70 mm, with reten- tion equal to 98 % for particles of size I,2 pm. NOTE - A larger funnel (5.2) and pad (5.31, for example of diameter 120 mm, may be used, if available, as this largely obviates the need to transfer any residue from the wall
15、s of the funnel to the pad during the determination (7.3). 5.4 Electric oven, capable of being controlled at 105 to 110 “C. 6 Sample preparation Sample in accordance with IS0 6257. Prepare the test sample immediately before the determination. If it is sufficiently hard, grind the whole of the test s
16、ample, using a mortar and pestle, to a particle size not exceeding 200 pm. If the pitch is too soft for grinding, melt and mix the sample, en- suring that its temperature does not exceed 150 OC and that the melting period does not exceed 10 min. NOTE - For soft pitches, the material for the test por
17、tion may be taken from the molten sample. 1) 1 mbar = 100 Pa 1 -,-,- IS0 6791-1981 (E) 7 Procedure WARNING - Attention is drawn to the dangers involved in the use of quinoline and toluene (see WARNINGS to clauses 4.1 and 4.2). Carry out all operations involving the use of these products in an effici
18、ently ventilated fume cupboard. 7.1 Test portion Weigh, to the nearest 0,005 g, approximately 1 g of the test sample. 7.2 Filter preparation Heat one of the filter pads (5.3) in the oven (5.41, controlled at 105 to 110 OC, for 1 h. Transfer the pad to a desiccator, allow to cool to ambient temperatu
19、re and weigh to the nearest 0,005 g. Repeat the process of heating, cooling and weighing until the difference between two consecutive weighings does not exceed 0,005 g. Fit the pad into the clean and dry Hartley funnel (5.2). 7.3 Determination Transfer the test portion 17.1) quantitatively to a 100
20、ml beaker. Add approximately 1 g of the dried filter aid (4.31, weighed to the nearest 0,005 g, and 25 ml of the quinoline (4.1). Stir the contents of the beaker to break up any lumps and cover the beaker with a watch glass. Partially immerse the beaker in the water bath (5.11, controlled at 70 to 8
21、0 “C, together with another suitable beaker contain- ing about 100 ml of the quinoline. Bring the temperature of the contents of each beaker to 70 to 80 OC and continue heating for I5 to 20 min, occasionally stirring the contents of the beaker containing the test portion. Fit the assembled Hartley f
22、unnel and filter pad (see 7.2) into the neck of a filter flask. Moisten the pad with a little of the hot quinoline and apply suction. As soon as filtration is complete, start filtering the dissolved test portion and any residue without unduly disturbing the solution, transferring about 2 ml of this
23、suspension at a time to the filter pad and allowing each portion to filter completely before making the next addition. Between each addition, maintain the temperature of the solution remain- ing in the beaker at 70 to 80 C by means of the heated water bath. When filtration is complete, rinse the bea
24、ker five times with approximately 5 ml portions of the hot quinoline from the other beaker, so as to transfer all remaining insoluble matter to the pad. Wash the residue on the filter pad with further 5 ml portions of the hot quinoline until the washings are clear. About ten washings are usually nec
25、essary. Wash the beaker which had contained the test portion with ten approximately 5 ml portions of the toluene (4.21, allowing each washing to pass completely through the filter pad before making the next addition. During the entire filtering operation, ensure that as little as possible of the sol
26、ution and residue is allowed to come into contact with the walls of the funnel. Release the suction, remove the filter pad with the residue and, after transferring to it any solid remaining on the walls of the funnel, place in the oven (5.4), controlled at 105 to 110 OC, for about 1 h. Transfer from
27、 the oven to the desiccator and allow to cool to ambient temperature. Weigh to the nearest 0,005 g. Repeat the operations of heating, cooling and weighing until the difference between two consecutive weighings does not exceed 0,005 g. A drying time of 2 to 3 h is usually sufficient. 8 Expression of
28、results 8.1 Method of calculation The content of quinoline-insoluble material, expressed as a percentage by mass, is given by the formula m3 - m2 - ml x 100 mo where m. is the mass, in grams, of the test portion (7.1); ml is the mass, in grams, of the dried filter pad (5.3); m2 is the mass, in grams
29、, of the filter aid (4.3) added; m3 is the mass, in grams, of the dried filter pad, the filter aid and the residue. 8.2 Precision Repeatability : 1 % Reproducibility : I,50 % 9 Test report The test report shall include the following particulars : a) an identification of the sample; b) the reference
30、of the method used; c) the results and the method of expression used; d) any unusual features noted during the determination; e) any operation not included in this International Stan- dard or in the International Standard to which reference is made, or regarded as optional. 2 IS0 6791-1981 (El Dimensions in millimetres 4 Terry spring clips or similar fastenings 68 holes, each 1 mm diameter PLAN Material : Aluminium or other suitable metal Finish : Fine machine all over polished bores and mating surfaces, i.e. flanges Figure - Details of Hartley funnel -,-,-