《ISO-17087-2006.pdf》由会员分享，可在线阅读，更多相关《ISO-17087-2006.pdf（28页珍藏版）》请在三一文库上搜索。
1、 Reference number ISO 17087:2006(E) ISO 2006 INTERNATIONAL STANDARD ISO 17087 First edition 2006-11-15 Specifications for adhesives used for finger joints in non-structural lumber products Spcifications pour des adhsifs utiliss pour des aboutages dans des produits en bois non structuraux Copyright I
2、nternational Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polytechnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 17087:2006(E) PDF disclaimer This PDF file may contain
3、 embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibilit
4、y of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parame
5、ters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. ISO 2006 All rights reserved. Unless otherwise
6、 specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright off
7、ice Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2006 All rights reserved Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polyt
8、echnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 17087:2006(E) ISO 2006 All rights reserved iii Contents Page Foreword iv 1 Scope . 1 2 Normative references. 1 3 Terms and definitions. 1 4 General principles. 2 5
9、 Apparatus and materials 3 6 Requirements 4 7 Test specimens. 4 8 Moisture content and conditioning. 7 9 Test procedures Flexure and tension 7 10 Exposure conditions 10 11 Expression of results . 12 12 Precision 12 Annex A (informative) Report forms. 13 Annex B (informative) Reading wood failure in
10、finger joints. 20 Bibliography. 22 Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polytechnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 17087:20
11、06(E) iv ISO 2006 All rights reserved Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body
12、 interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotec
13、hnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by
14、the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent righ
15、ts. ISO shall not be held responsible for identifying any or all such patent rights. ISO 17087 was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 11, Products. Based with permission of ASTM, on ASTM D 5572, Standard Specification for Adhesives Used for Finger Joints in Nonstruc
16、tural Lumber Products. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polytechnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo reproduction or networking permitted without license from IHS -,-,- INTERNATIONAL STANDARD I
17、SO 17087:2006(E) ISO 2006 All rights reserved 1 Specifications for adhesives used for finger joints in non-structural lumber products 1 Scope This International Standard specifies performance levels for adhesives to be used in finger joints in nonstructural bonded lumber products. Such products incl
18、ude, but are not limited to, interior and exterior mouldings, window and door components or parts, and bonded lumber panels. Adhesives that meet the requirements of the various performance classes are considered capable of providing an adequate bond for use under the conditions described for the cla
19、ss. This specification is intended to be used to evaluate adhesives as well as the adhesive bonds in the finger joints. 2 Normative references The following referenced documents are indispensable for the application of this International Standard. For dated references, only the edition cited applies
20、. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 7500-1, Metallic materials Verification of static uniaxial testing machines Part 1: Tension/compression testing machines Verification and calibration of the force-measuring system 3 Terms
21、and definitions For the purposes of this document, the following terms and definitions apply. 3.1 bond union between materials produced using adhesives 3.2 finger joint joint formed by bonding two precut members shaped like fingers (see Figure 1) a) Horizontal joint b) Vertical joint Key 1 face 2 ed
22、ge Figure 1 Finger joint Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polytechnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo reproduction or networking permitted without license from IHS -,-,- ISO 17087:2006(E) 2 IS
23、O 2006 All rights reserved 3.3 dry-use nonstructural adhesive adhesive capable of producing sufficient strength and durability to make the bonded lumber product serviceable in nonstructural use, under conditions in which the equilibrium moisture content (EMC) of the wood does not exceed 16 % 3.4 wet
24、-use nonstructural adhesive adhesive capable of producing sufficient strength and durability to make the bonded lumber product serviceable in nonstructural use, under conditions in which the EMC of the wood may be 16 % or greater 3.5 equilibrium moisture content EMC moisture content at which wood ne
25、ither gains nor loses moisture to the surrounding air NOTE Adapted from ASTM D 9. 3.6 moisture content MC amount of water contained in the wood, usually expressed as a percentage of the mass of the oven-dry wood NOTE Adapted from ASTM D 9. 4 General principles 4.1 Adhesives are classified as dry-use
26、 or wet-use. Each classification includes consideration of short-term in-transit exposure conditions at elevated temperatures up to 104 C. NOTE This specification reflects results obtained with laboratory-made specimens compared to those obtained with industrially manufactured specimens. These finge
27、r joints were prepared using previously certified adhesives in cooperation with a manufacturer or equipment supplier who had the necessary finger joint cutter and assembly equipment. Such finger joints may vary in geometry and length from manufacturer to manufacturer, and this variation could affect
28、 the performance of the bonded finger joint assembly. Figure 2 depicts a typical finger joint configuration. 4.2 When changes are made in the design of industrially manufactured finger joints, the new design should preferably be compared to a control design that has been used successfully. 4.3 An in
29、dustrially made finger joint assembly should preferably be evaluated using the requirements for compliance with this specification. When this specification is used to evaluate specimens made from laboratory-made assemblies, the results may not compare favourably with those obtained with specimens ma
30、de from industrially made assemblies. 4.4 Test requirements are provided to determine if the adhesive is suitable for dry use or wet use. 4.5 The dry test and exposure conditions and treatments are to evaluate adhesives used in nonstructural finger joints for typical service conditions. 4.6 The 104
31、C test is a more severe test designed to evaluate the product after exposure to short-term elevated-temperature conditions. This test is intended to simulate conditions that might be experienced in transit, during further processing or in service conditions. NOTE Service conditions could typically i
32、nclude stress and time under stress, as well as elevated temperature. 4.7 Procedures are described in sufficient detail to permit duplication in different test laboratories. To avoid potential problems that would be caused by interrupting the bonding process, the adhesive performance level should pr
33、eferably be determined by the finger joint manufacturer prior to handling and early shipment. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polytechnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo reproduction or netwo
34、rking permitted without license from IHS -,-,- ISO 17087:2006(E) ISO 2006 All rights reserved 3 Before beginning the full testing process, the test laboratory should preferably take a representative sample and check the dry strength first, in order to ensure that the product basically conforms to th
35、e dry-strength performance level certified by the adhesive manufacturer. Key a height of joint 33 mm f length of finger 6 mm wt width of finger tip 1 mm wb width of finger base 2 mm s slope of finger 5 NOTE The dimensions given are examples for a typical horizontal finger joint. Figure 2 Example of
36、cross-section of finger joint test specimen 5 Apparatus and materials 5.1 Tensile-testing machine, capable of maintaining a pre-determined constant crosshead rate. The machine shall be capable of determining a maximum load. The measured strength shall be between 15 % and 85 % of the capacity of the
37、machine. The machine shall permit the measurement and recording of the applied force with an uncertainty of 1 % or better. The machine shall have a capacity of not less than 9 800 N in compression, shall be equipped for one-third- span, two-point loading for the flexure test as described in 9.1 and
38、shown in Figure 3, shall be equipped with grips of sufficient length to hold the specimen firmly, preferably with a minimum length of 63 mm and minimum width of 19 mm, and shall be located in an atmosphere such that the moisture content of the specimen is not noticeably altered during testing. The e
39、quipment shall be calibrated regularly in accordance with ISO 7500-1. It is recommended that the machine be autographic, giving a chart that can be read in terms of millimetres of crosshead movement as one coordinate and applied force as the other coordinate. It is also recommended that inertialess
40、equipment be used. The finger joint specimens to be broken in tension are shorter than those to be broken in flexure. Accommodation shall be made in the equipment for handling the larger flexure specimen. 5.2 Environmental chamber, capable of conditioning specimens at (23 2) C and (65 5) % relative
41、humidity, having a capacity for at least 20 specimens well spaced and supported on racks to allow free air flow. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=Hong Kong Polytechnic Univ/9976803100 Not for Resale, 04/17/2007 09:49:59 MDTNo re
42、production or networking permitted without license from IHS -,-,- ISO 17087:2006(E) 4 ISO 2006 All rights reserved 5.3 Oven(s), with sufficient air circulation to remove moisture from the oven chamber, capable of meeting all the following temperature requirements: (41 2) C (see 10.2.3), (65 2) C (se
43、e 10.2.6 and 10.3.3), (104 2) C (see 10.2.4, 10.2.5 and 10.3.4) and (110 2) C (see 10.2.4). 5.4 Specimen-soaking tank, having a capacity meeting the requirements of 10.2.3, so that all of the specimens are at least 50 mm below the water level for the duration of the soak cycles. 5.5 Specimen-boiling
44、 tank, having a capacity meeting the requirements of 10.3.3, so that all of the specimens are at least 50 mm below the water level for the duration of the boil cycles. 5.6 Vacuum/pressure vessel, having a capacity meeting the requirements of 10.3.5, so that all of the specimens are at least 50 mm be
45、low the water level for the duration of the vacuum/pressure cycles. 5.7 PVDC wrap: poly(vinylidene chloride) film for wrapping test specimens. 6 Requirements 6.1 To demonstrate compliance with this specification, the test adhesive shall be tested for performance in accordance with Clauses 9 and 10,
46、and it shall meet the requirements in Table 1 for the selected test mode and performance classification. 6.2 Compliance with this specification shall warrant certification of the adhesive for use on the species of wood that is used for the tests, or for use on a designated group of species when test
47、ed and found to be in compliance for any one member of said group of species. The designated species groupings for commonly used woods, as accepted in this specification, are given in Table 2. In the event that the user or supplier of the adhesive, or both, cannot accept the designated groupings in
48、Table 2, either party shall have the option of requesting a test on an individual species. Furthermore, the user and supplier may agree to change any of the wood-failure requirements of Table 1 when applied to tests on group 3 and 4 hardwoods in Table 2. 6.3 The wood-failure requirements listed in Table 1 are given for softwoods and hardwoods. 6.4 An industrially manufactured finger joint may be used to evaluate the adhesive, provided its construction meets the requirements set forth in Clauses 7 to 10, and t