1、INTERNATIONAL STANDARD ISO 7617-2 Third edition 2003-08-01 Reference number ISO 7617-2:2003(E) ISO 2003 Plastics-coated fabrics for upholstery Part 2: Specification for PVC-coated woven fabrics Supports textiles revtus de plastique pour ameublement et garniture Partie 2: Spcifications pour les tissu
2、s revtus de PVC ISO 7617-2:2003(E) ii ISO 2003 All rights reserved PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed
3、 on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products
4、used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, pleas
5、e inform the Central Secretariat at the address given below. ISO 2003 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing
6、from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ISO 7617-2:2003(E) ISO 2003 All rights reserv
7、ed iii Contents Page 1Scope 1 2Normative references 1 3Technical requirements . 1 4Sampling . 2 5Testing and compliance 2 6Marking . 3 Annex A (normative) Method of selecting test specimens . 4 Annex B (normative) Determination of resistance to print wear . 6 Annex C (normative) Determination of col
8、our fastness to rubbing 8 -,-,- ISO 7617-2:2003(E) iv ISO 2003 All rights reserved Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out throu
9、gh ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collabora
10、tes closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standar
11、ds. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of th
12、is document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 7617-2 was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee SC 4, Products (other than hoses). This third edition cancels and repla
13、ces the second edition (ISO 7617-2:1994), which has been technically revised. ISO 7617 consists of the following parts, under the general title Plastics-coated fabrics for upholstery: Part 1: Specification for PVC-coated knitted fabrics Part 2: Specification for PVC-coated woven fabrics Part 3: Spec
14、ification for polyurethane-coated woven fabrics -,-,- INTERNATIONAL STANDARDISO 7617-2:2003(E) ISO 2003 All rights reserved 1 Plastics-coated fabrics for upholstery Part 2: Specification for PVC-coated woven fabrics 1Scope This part of ISO 7617 specifies requirements for coated fabrics for upholster
15、ed furniture, manufactured by applying to one side of a woven cloth a substantially continuous coating of a suitably plasticized polymer of vinyl chloride, or a copolymer the major constituent of which is vinyl chloride. Such coatings are known as poly(vinyl chloride) (PVC) coatings. The present spe
16、cification covers two grades (A and B) of PVC-coated woven fabric. 2Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced docum
17、ent (including any amendments) applies. ISO 105-A02:1993, Textiles Tests for colour fastness Part A02: Grey scale for assessing change in colour ISO 105-B01:1994, Textiles Tests for colour fastness Part B01: Colour fastness to light: Daylight ISO 105-B02:1994, Textiles Tests for colour fastness Part
18、 B02: Colour fastness to artificial light: Xenon arc fading lamp test ISO 105-X12:2001, Textiles Tests for colour fastness Part X12: Colour fastness to rubbing ISO 176:1976, Plastics Determination of loss of plasticizers Activated carbon method ISO 1421:1998, Rubber- or plastics-coated fabrics Deter
19、mination of tensile strength and elongation at break ISO 2231:1989, Rubber- or plastics-coated fabrics Standard atmospheres for conditioning and testing ISO 2286-1:1998, Rubber- or plastics-coated fabrics Determination of roll characteristics Part 1: Methods for determination of length, width and ne
20、t mass ISO 2411:2000, Rubber- or plastics-coated fabrics Determination of coating adhesion ISO 4674-1:2003, Rubber- or plastics-coated fabrics Determination of tear resistance Part 1: Constant rate of tear methods ISO 5978:1990, Rubber- or plastics-coated fabrics Determination of blocking resistance
21、 ISO 7854:1995, Rubber- or plastics-coated fabrics Determination of resistance to damage by flexing 3Technical requirements 3.1Physical requirements The material shall comply with the appropriate requirements of Table 1. -,-,- ISO 7617-2:2003(E) 2 ISO 2003 All rights reserved 3.2Colour fastness requ
22、irements The material shall comply with the requirements of Table 2. 3.3Visual examination The coating of the material shall be uniformly applied and shall be free from visible flaws and cracks and when viewed under a magnification of shall be substantially free from pinholes. The base fabric, unles
23、s coated with an unpigmented coating, shall not be visible when viewed from the coated side. 3.4Colour, grain and finish The colour, grain and finish of the material, whether in single-colour or multicolour effects, shall be agreed between the purchaser and the supplier. Colours shall be compared un
24、der the conditions stipulated in ISO 105-B01. 3.5Width of material The usable width of material when measured in accordance with ISO 2286-1 shall be as agreed between the purchaser and the supplier. For this purpose, the term “usable width” means the width of material that is coated in such a manner
25、 that it complies with the requirements of 3.3. 3.6Flammability A method of test for determination of the flammability characteristics of these materials shall be included as a mandatory requirement to be complied with in the absence of other, more stringent, requirements of national authorities. 4S
26、ampling If individual rolls can be identified with manufacturing batches, at least one sample shall be taken from each batch in the consignment. Each sample shall be regarded as being representative of its source, and suitable measures shall be taken to preserve identity between the samples and batc
27、h numbers. If individual rolls cannot be identified in this way, the number of samples to be regarded as being representative of the bulk shall be fixed by agreement between the purchaser and the supplier. Such samples shall be drawn at random. 5Testing and compliance Tests shall be conducted on a s
28、et of specimens selected from each sample. The method of selecting specimens from each sample shall be in accordance with the requirements of Annex A. If the specimens after testing comply with the appropriate requirements given in Tables 1 and 2, the bulk of the coated fabric which the sample repre
29、sents shall be deemed to comply with the requirements of this part of ISO 7617. If any of the specimens tested do not comply with any of the appropriate requirements given in Tables 1 and 2, the tests which the specimens have failed shall be repeated twice. For this purpose, two further samples shal
30、l be taken from the same source as the original sample, and test specimens shall be taken from each sample so that duplicate tests may be conducted. If all the re-test results comply with the appropriate requirements of Table 1 and/or Table 2, then the bulk represented by the samples from which the
31、specimens for re-testing were taken, together with the original samples, shall be deemed to comply with the requirements of this part of ISO 7617. If any of the results of the re-tests do not comply with the appropriate requirements of Table 1 or 2, 10 ISO 7617-2:2003(E) ISO 2003 All rights reserved
32、 3 the bulk represented by those samples shall be deemed not to comply with the requirements of this part of ISO 7617. 6Marking Each roll of fabric shall have a label attached bearing the following information: a)the name and/or distinctive mark of the manufacturer and an identification reference fo
33、r that material; b)the batch number; c)the colour; d)the length; e)the usable width; f)the reference number of this part of ISO 7617 (i.e. ISO 7617-2) and the appropriate grade reference. Table 1 Physical requirements PropertyLimit Requirements Method of test Grade AGrade B Total mass/unit area ()a.
34、550420ISO 2286-1 Coating mass/unit area ()a.300240ISO 2286-1 Tearing force (N) longitudinal.4431ISO 4674-1:2003, method A transverse.4431 Coating adhesion (N per width).2626ISO 2411 Breaking load ( ) longitudinal.580450ISO 1421:1998, method 2 transverse.580450 Flex cracking (cycles)b.400 000300 000I
35、SO 7854 Heat ageing ( coating mass loss).55ISO 176 Print wear (change in appearance) (grey scale rating) .33See Annex B Thickness () at , minimum individual reading .0,40,4ISO 2286-1 Blocking resistance Separation without damage to surface ISO 5978 a The inclusion of minimum values for total mass/un
36、it area and coating mass/unit area does not imply that a minimum value for base fabric mass/unit area may be calculated by subtraction. b In the event of dispute, Schildknecht apparatus shall be employed. Table 2 Colour fastness requirements PropertyLimit Requirements Method of test Grade AGrade B C
37、olour-fastness to artificial light (xenon arc).66ISO 105-B02 to rubbing (wet and dry).44See Annex C g/m2min g/m2min min min 50 mmmin N min min min %max min mm2 kPa min min min -,-,- ISO 7617-2:2003(E) 4 ISO 2003 All rights reserved Annex A (normative) Method of selecting test specimens The specimens
38、 for testing shall be selected from the sample in accordance with the scheme illustrated in Figure A.1, which shows the positions from which the specimens for each type of test shall be taken, except that the specimens required for testing colour fastness to light and those required for heat ageing
39、tests shall be selected from any suitable portion of the sample. In the case of multicolour samples, the specimen shall if possible include all colours. If it is not possible to include all colours, sufficient specimens shall be taken to enable all colours to be tested. -,-,- ISO 7617-2:2003(E) ISO
40、2003 All rights reserved 5 Key mass determinations tear strength (across longitudinal threads) tear strength (across transverse threads) breaking load (longitudinal) breaking load (transverse) coating adhesion resistance to flex cracking (longitudinal direction) resistance to flex cracking (transver
41、se direction) heat ageing (any convenient location) colour fastness to rubbing (wet) colour fastness to rubbing (dry) print wear (2 pieces, ) blocking resistance thickness determination Figure A.1 Scheme for selection of test specimens M Tr Tr Tn Tn Ad Fl Fl Rb(w) Rb(d) P230 mm50 mm B Th ISO 7617-2:
42、2003(E) 6 ISO 2003 All rights reserved Annex B (normative) Determination of resistance to print wear B.1Principle A specimen is subjected to 500 cycles of simple harmonic abrasion using a known abradant under a known pressure. It is then assessed for colour difference with an unabraded portion using
43、 the grey scale for assessing change in colour. B.2Apparatus The apparatus shall be as described in ISO 105-X12, but with the following modifications: a)The weightpiece applied to the rubbing finger, or peg, shall be such that a total mass of is brought to bear on the glass plate. b)The frequency of
44、 operation of the apparatus shall be (i.e. 0,5 strokes per second: each cycle comprises one outward stroke and one return stroke). c)Use as the abradant a cotton fabric, desized scoured and bleached, free from fluorescent brightening agents, and having a fluidity no greater than 8, a mass per unit a
45、rea of and a construction of , , 11,36 tex warp and 9,23 tex weft in plain weave. d)Use the grey scale for assessing change in colour (see ISO 105-A02). B.3Test specimens Cut out two specimens of coated fabric, each , one with its length parallel to the longitudinal direction of the sample and the o
46、ther with its length parallel to the transverse direction. Also cut out two circular pieces of the bleached cotton fabric, each in diameter, avoiding lumps and neps. NOTEInitially, four circular pieces of abradant cotton fabric can be cut out and a double thickness of cotton mounted on the peg, so t
47、hat only the outermost layer coming into contact with the coated-fabric specimen needs to be renewed at each test. B.4Procedure Condition the test specimens and bleached cotton fabric in accordance with ISO 2231. Using the clamps, mount the test specimen securely on the bed of the machine with the c
48、oated side uppermost and under sufficient tension to hold the specimen flat. Wipe the coated surface of the specimen with a clean, dry cloth to remove dust before testing. Secure the conditioned bleached cotton fabric to base of the brass peg, making sure that the face of the sateen is presented to the specimen under test, i.e. with the ribbed side of the bleached cotton fabric in contact with the brass peg. Lower the peg on to the specimen and run the machine for 500 cycles. Repeat the procedure using the second specimen and bleached cotton fabric. Assess the degree