1、JIS GX0563 93 m Y933608 0532933 37T m JIS UDC 669.14-1 55.331620.1 78.1 JAPANESE INDUSTRIAL STANDARD Method of measuring surface hardness for nitrided iron and steel JIS G 0 5 6 3 - 1 9 9 3 Translated and Published bY Japanese Standards. Association Printed i n Japan 4 s Copyright Japanese Standards
2、 Association Provided by IHS under license with JSALicensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 03/10/2007 07:28:57 MSTNo reproduction or networking permitted without license from IHS -,-,- In the event of any doubt arising, the original Standard in Japanese is to be final au
3、thority. i * o . o Copyright Japanese Standards Association Provided by IHS under license with JSALicensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 03/10/2007 07:28:57 MSTNo reproduction or networking permitted without license from IHS -,-,- JIS Gu05b3 JAPANE 93 = 4933608 E INDUST
4、RIAL 0512913 142 UDC 669.14 - 155.33: 620. 178. 1 TANDARD J I S Method of measuring surface hardness G 0563-1993 for nitrided iron and steel 1. Scope This Japanese Industrial Standard specifies measuring methods for the surface hardness of nitrided layer (hereafter referred to as the “surface hardne
5、ss“) of iron and steel by means of nitriding, nitrocarburizing, etc. (hereaf- ter referred to as the “processing“). Remarks 1. The specification on processing, etc. shall be as given in JIS B 6915. 2. The standards cited in this Standard shall be the following: JIS B 6915 JIS G 0201 Nitriding of ste
6、el Glossary of terms used in iron and steel (Heat treatment) Method of Vickers hardness test Method of Rockwell and Rockwell superficial hardness test Method of Shore hardness test Method of Knoop hardness test JIS Z 2244 JIS Z 2245 JIS 2 2246 JIS Z 2251 2. Definitions the following, and for the res
7、t of the terms, definitions given in JIS G 0201 shall be applied. The principal terms used in this Standard are as defined in (4) (5) Vickers surface hardness iron and steel which is determined by Vickers hardness test. The hardness of surface of nitrided layer for Knoop surface hardness and steel w
8、hich is determined by Knoop hardness test. The hardness of surface of nitrided layer for iron Rockwell superficial surface hardness, scale 15 N The hardness of surface of nitrided layer for iron and steel which is determined by Rockwell superfi- cial hardness test of scale 15 N. Shore surface hardne
9、ss and steel which is determined by Shore hardness test. compound layer depth nitride, carbide, carbo-nitride, etc. from the surface. diffusion layer depth diffusion of nitrogen, carbon, or the like, but excluding the compound layer. nitrided case depth The distance from the surface of nitrided laye
10、r to the point where the difference between the physical or chemical behavior of the nitrided layer and that of matrix is infeasible to identify. The nitrided case depth is the summation of the depths of compound layer and diffusion layer. The hardness of surface of nitrided layer for iron The depth
11、 of the layer which includes mainly The depth of the layer which is appreciated Copyright Japanese Standards Association Provided by IHS under license with JSALicensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 03/10/2007 07:28:57 MSTNo reproduction or networking permitted without l
12、icense from IHS -,-,- i J I S 6x0563 93 a 4933608 0532934 089 2 G 0563-1993 3. Test specimen For the test specimen, the product itself shall be used. If this is infeasible, iron and steel of the same quality of the said product which is treated under the same conditions thereof may be used. 4. Measu
13、ring method of surface hardness 4.1 for the test specimen approximately 0.01 mm or more in nitrided case depth. Measuring method of Vickers surface hardness This method is applicable Vickers hardness test specified in JIS 2 2244 shall be applied to the test surface, whereby the hardness shall be det
14、ermined, In this case, the test load shall be 0.9807 N or less. 4.2 This method is applicable for the test specimen approximately 0.01 mm or more in nitrided case depth. Knoop hardness test specified in JIS Z 2251 shall be applied to the test surface, whereby the hardness shall be determined. In thi
15、s case, the test load shall be 0.9807 N or less. Measuring method of Knoop surface hardness 4.3 Measuring method of Rockwell superficial surface hardness, scale 15 N This method is applicable for the test specimen approximately 0.2 mm or more in nitrided case depth. Rockwell superficial surface-hard
16、ness test of scale 15 N specified in JIS 2 2245 shall be applied to the test surface, whereby the hardness shall be determined. 4.4 This method is applicable for the test specimen approximately 0.3 mm or more in nitrided case depth. Shore hardness test specified in JIS 2 2246 shall be applied to the
17、 test surface, whereby the hardness shall be determined. Measuring method of Shore surface hardness Remarks: Measurement on surface hardness shall be made on the as-processed surface of test specimen. According to the purpose of processing, however, hardness test is applied to a test speci- men bein
18、g removed to its compound layer. In this case, the hardness test is conducted after removing the equivalent layer depth to the compound layer by polishing. With this respect, sufficient care shall be taken during polishing so that this does not affect the surface hardness of the test sur- face. Desc
19、ription The description shall be as given in the following: The numerical value of surface hardness should, as a rule, be down to the first integer place. However, those for Rockwell superficial hardness of scale 15 N and for Shore hardness may be described down to the first decimal place. The symbo
20、l for description of surface hardness shall be as given in Table 1. t I Copyright Japanese Standards Association Provided by IHS under license with JSALicensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 03/10/2007 07:28:57 MSTNo reproduction or networking permitted without license f
21、rom IHS -,-,- JIS G+0563 93 = 4933608 0532935 T15 Surface hardness Vickers surface hardness 3. G 0563-1993 Table 1. Symbol for description of surface hardness Symbol NS - OOHV A Knoop surface hardness I NS-00HKA Rockwell superficial surface hardness, scale 15 N I NS - 0 0 H R 1 5 N Shore surface har
22、dness I NS-00HS Remarks 1. “NS“ stands for the surface of nitrided layer (Informative reference: nitrided surface). 2. “NSD“ stands for the diffusion layer being removed to the compound layer (Informative reference: diffusion zone). 3. As to “ OO“, the numerical value of hardness shall be entered, a
23、nd as to “ A I the numerical value of symbol of hardness which corre- sponds to the test load shall be entered. Example 1. Example 2. Example 3. Example 4. Example 5. Description for Vickers surface hardness of 988 (test load: 0.9807 N) NS - 988 HV 0.1 Description for Knoop surface hardness of 846 (
24、test load: 0.4903 N) NS - 846 HK 0.05 Description for Rockwell superficial surface hardness (scale 15 N) of 91 NS - 91 HR 15 N Description for Shore surface hardness of 86 NS - 86 HS Description for Vickers surface hardness of 680 (test load: 0.9807 N) concerning the test specimen being removed to t
25、he compound layer NSD - 680 HV 0.1 Related standard: JIS G 0562 Method of measuring nitrided case depth for iron and steel Copyright Japanese Standards Association Provided by IHS under license with JSALicensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 03/10/2007 07:28:57 MSTNo rep
26、roduction or networking permitted without license from IHS -,-,- Y G 0563-1993 Edition 1 Japanese Text Established by Minister of International Trade and Industry Date of Establishment: 1993-03-01 Date of Public Notice in Official Gazette: Investigated by: 1993-03-23 Japanese Industrial Standards Co
27、mmittee Divisional Council on Iron and Steel This English translation is published by: Japanese Standards Association 1-24, Akasaka 4, Minato-ku, Tokyo 107 Japan O JSA, 1993 Printed in Tokyo by Hohbunsha Co., Ltd. Copyright Japanese Standards Association Provided by IHS under license with JSALicensee=IHS Employees/1111111001, User=Wing, Bernie Not for Resale, 03/10/2007 07:28:57 MSTNo reproduction or networking permitted without license from IHS -,-,-