《【BS英国标准】BS EN 820-2-2003 Advanced technical ceramics — Methods of testing monolithic ceramics — Thermo-mechanical properties.doc》由会员分享，可在线阅读，更多相关《【BS英国标准】BS EN 820-2-2003 Advanced technical ceramics — Methods of testing monolithic ceramics — Thermo-mechanical properties.doc（16页珍藏版）》请在三一文库上搜索。
1、BRITISH STANDARDBS EN820-2:2003Advanced technical ceramics Methods of testing monolithic ceramics Thermo-mechanical properties Part 2: Determination of self-loaded deformation-,-,-The European Standard EN 820-2:2003 has the status of aBritish StandardICS 81.060.30 Copyright British Standards Institu
2、tionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/5959906001, 11/08/200406:05:45 MST Questions or comments about this message: please call the DocumentPolicy Group at 303-397-2295.BS EN 820-2:2003National forewordThis British Standard is
3、 the official English language version ofEN 820-2:2003. It supersedes DD ENV 820-2:1992 which is withdrawn.The UK participation in its preparation was entrusted to Technical CommitteeRPI/13, Advanced technical ceramics, which has the responsibility to:aid enquirers to understand the text;present to
4、the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed;monitor related international and European developments and promulgate them in the UK.A list of organizations represented on this committee can be obtaine
5、d on request to its secretary.Cross-referencesThe British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of th
6、e BSI Electronic Catalogue or of British Standards Online.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard does not of itself confer immunity from legal obligations.This Briti
7、sh Standard was published under the authority of the Standards Policy and Strategy Committee on22 April 2003 BSI 22 April 2003ISBN 0 580 41604 6Summary of pagesThis document comprises a front cover, an inside front cover, the EN title page,pages 2 to 11 and a back cover.The BSI copyright date displa
8、yed in this document indicates when the document was last issued.Amd. No.DateCommentsAmendments issued since publication-,-,-EUROPEAN STANDARD NORME EUROPENNEEUROPISCHE NORMEN 820-2April 2003ICS 81.060.30Supersedes ENV 820-2:1992English versionAdvanced technical ceramics - Methods of testing monolit
9、hic ceramics - Thermo-mechanical properties - Part 2: Determination of self-loaded deformationCramiques techniques avances - Mthodes dessai pour cramiques monolithiques - Proprits thermo-mcaniques- Partie 2: Dtermination de la dformation sous son propre poidsHochleistungskeramik - Prfverfahren fr mo
10、nolithische Keramik - Thermomechanische Eigenschaften - Teil 2: Bestimmung der Verformung unter EigengewichtThis European Standard was approved by CEN on 2 January 2003.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European S
11、tandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Management Centre or to any CEN member.This European Standard exists in three official versions (English, French,
12、 German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Management Centre has the same status as the official versions.CEN members are the national standards bodies of Austria, Belgium, Czech Republic, Denmark,
13、Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, Norway, Portugal, Slovakia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATION C O M I T EUR O P EN DE NOR M A L I S A TI ON EUR O P I S C H ES KOM I TEE F R NOR M U
14、NG Management Centre: rue de Stassart, 36 B-1050 Brussels 2003 CENAll rights of exploitation in any form and by any means reserved worldwide for CEN national Members.Ref. No. EN 820-2:2003 E-,-,-EN 820-2:2003 (E)ContentspageForeword .31Scope .42Normative references .43Term and definition.44Principle
15、 .45Apparatus .46Test pieces.57Procedure .57.1Setting up of measurement gauge .57.2Marking of the test pieces .57.3Measurement of test pieces before heat treatment.57.4Heat treatment of test pieces .57.5Measurement of the test pieces after heat treatment .67.6Calculation of deformation .68Determinat
16、ion of the temperature of commencement of self-loaded deformation.68.1Determination .68.2Limits.69Interferences.72-,-,-10Test report .7Copyright British Standards InstitutionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/5959906001, 11/08
17、/200406:05:45 MST Questions or comments about this message: please call the DocumentPolicy Group at 303-397-2295.EN 820-2:2003 (E)ForewordThis document (EN 820-2:2003) has been prepared by Technical Committee CEN/TC 184 Advanced technical ceramics, the secretariat of which is held by BSI.This docume
18、nt shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by October 2003, and conflicting national standards shall be withdrawn at the latest by October 2003.This document supersedes ENV 820-2:1992.EN 820 Advanced technical cera
19、mics Methods of testing monolithic ceramics Thermo-mechanical propertiesconsists of four parts: Part 1: Determination of flexural strength at elevated temperatures Part 2: Determination of self-loaded deformation Part 3: Determination resistance to thermal shock by water quenching Part 4: Determinat
20、ion of flexural creep deformation at elevated temperaturesAccording to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Hun
21、gary, Iceland, Ireland, Italy, Luxembourg, Malta, Netherlands, Norway, Portugal, Slovakia, Spain, Sweden, Switzerland and the United Kingdom.-,-,-Copyright British Standards InstitutionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/595990
22、6001, 11/08/200406:05:45 MST Questions or comments about this message: please call the DocumentPolicy Group at 303-397-2295.3EN 820-2:2003 (E)1ScopeThis European Standard specifies a method for the determination of the temperature at which the self-loaded deformation of a ceramic test piece commence
23、s and the extent of this deformation.2Normative referencesThis European Standard incorporates by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the text, and the publications are listed hereafter. For dated references
24、, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies (including amendments).EN 60584-1, Thermocouples - Part 1: Refe
25、rence tables (IEC 60584-1:1995).EN ISO/IEC 17025, General requirements for the competence of testing and calibration laboratories (ISO/IEC17025:1999).ENV 1006, Advanced technical ceramics - Methods of testing monolithic ceramics - Guidance on the sampling and selection of test pieces.3Term and defin
26、itionFor the purposes of this European Standard the following term and definition applies.3.1self-loaded deformationthe property induced by heat, which results in a ceramic body being readily deformed under its own weight4PrincipleThe method involves determining whether or not test bars supported on
27、ly at their ends deform at a series of temperatures, recording any self-loaded deformation observed, and recording the results graphically. The temperature of commencement of self-loaded deformation, taken from the graph, is reported.This test is intended as a simple method of determining the upper
28、use temperature of ceramic components in a self-loaded condition. The criterion is an upper limit of flexural distortion. The test is suitable for use on furnace construction materials and on any ceramic materials, from which components are subjected to further processing at high temperatures.5Appar
29、atus5.1Measurement apparatus, of the type shown in Figure 1. The distance between the knife edge supports shall be 160 mm 0,5 mm. The gauge for measuring deformation (sag or bow) shall be accurate to 0,01 mm.NOTEThe dial gauge shown in Figure 1 is an example only.5.2Steel bar, of dimensions as shown
30、 in Figure 2, with the top surface flat to 0,01 mm and parallel, to 0,01 mm, to the under surfaces in the regions of reduced thicknesses.45.3Laboratory furnace, capable of achieving 1600 C, and of holding the temperature uniformly over the area occupied by the test pieces (see Figure 3) to within 5
31、C. A controlled atmosphere, other than air, may be used if required. This shall be reported (see clause 10).-,-,-Copyright British Standards InstitutionReproduced by IHS under license with BSI - Uncontrolled CopyDocument provided by IHS Licensee=Bureau Veritas/5959906001, 11/08/200406:05:45 MST Ques
32、tions or comments about this message: please call the DocumentPolicy Group at 303-397-2295.EN 820-2:2003 (E)5.4Two refractory supports, with square cross-section of approximately 12 mm (see Figure 3), made of material which is compatible with the test material at the test temperature. The supports s
33、hall be inspected after each firing and where there is evidence of reaction with the test pieces, the supports shall be replaced.5.5Thermocouples (two), one to control the furnace and one to measure the temperature of the test pieces. The thermocouples shall be either type R, type S or type B in acc
34、ordance with EN 60584-1.-,-,-6Test piecesMaterials for testing shall be selected in accordance with the guidance given in ENV 1006. Test pieces shall be rectangular bars, within the following range of dimensions:a) length: 173 mm to 177 mm;b) width: 11,5 mm to 12,5 mm;c) thickness: 3,9 mm to 4,1 mm.
35、The test pieces shall be ground flat and parallel so that the thickness tolerance of a set of test pieces shall be 0,02 mm.NOTE 1A set is the number of test pieces which are required for the determination of the temperature of commencement of self-loaded deformation.Two pieces are required for each
36、determination at a single temperature. Test pieces may be either cut from fired ceramic products or may be prepared especially for this method of test.NOTE 2In the latter case they should be fired before testing in a manner comparable to production firing.7Procedure1.1 Setting up of measurement gaug
37、eCheck that the measurement gauge (see 5.1) probe is positioned at the mid-point between the two knife edges, as shown in Figure 1. Place the steel bar (see 5.2) on the knife edges and adjust the gauge to read zero.7.2 Marking of the test piecesMark the upper face of one end of the test piece with refractory paint, as the referenc