1、BRITISH STANDARD AEROSPACE SERIES BS EN 2561:1995 Carbon fibre reinforced plastics Unidirectional laminates Tensile test parallel to the fibre direction The European Standard EN 2561:1995 has the status of a British Standard ICS 49.040.10 UDC 678.6.046:667.494-039.626:620.172.629.7 Licensed Copy: sh
2、effieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS EN 2561:1995 This British Standard, having been prepared under the direction of the Engineering Sector Board, was published under the authority of the Standards Board and comes into effect on 15 December 199
3、5 BSI 09-1999 The following BSI references relate to the work on this standard: Committee reference ACE/64 Draft for comment 88/72264 DC ISBN 0 580 23109 7 Committees responsible for this British Standard The preparation of this European Standard was entrusted to Technical Committee ACE/64, Aerospac
4、e structural reinforced plastics, upon which the following bodies were represented: British Plastics Federation Ministry of Defence Society of British Aerospace Companies Limited Amendments issued since publication Amd. No.DateComments Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14
5、GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS EN 2561:1995 BSI 09-1999i Contents Page Committees responsibleInside front cover National forewordii Foreword2 Text of EN 25613 List of referencesInside back cover Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontroll
6、ed Copy, (c) BSI BS EN 2561:1995 ii BSI 09-1999 National foreword This British Standard has been prepared under the direction of the Aerospace Standards Policy Committee and is the English language version of EN 2561:1995 Aerospace series Carbon fibre reinforced plastics Unidirectional laminates Ten
7、sile test parallel to the fibre direction, published by the European Committee for Standardization (CEN). EN 2561 was produced as a result of international discussions in which the United Kingdom took an active part. A British Standard does not purport to include all the necessary provisions of a co
8、ntract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Cross-references Publication referred toCorresponding British Standard EN 2744:1992BS EN 2744:1992 Non-metallic materials Pr
9、eferred test temperatures Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, the EN title page, pages 2 to 10, an inside back cover and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be
10、 indicated in the amendment table on the inside front cover. Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 2561 September 1995 ICS 49.040.10 Descriptors: Aircraft industry, laminates, re
11、inforced plastics, carbon fibres, thermosetting resins, tension tests English version Aerospace series Carbon fibre reinforced plastics Unidirectional laminates Tensile test parallel to the fibre direction Srie arospatiale Plastiques renforcs de fibres de carbone Stratifis unidirectionnels Essai de
12、traction paralllement la direction des fibres Luft und Raumfahrt Kohlenstoffaserverstrkte Kunststoffe Unidirektionale Laminate Zugprfung parallel zur Faserrichtung This European Standard was approved by CEN on 1995-09-19. CEN members are bound to comply with the CEN/CENELEC Internal Regulations whic
13、h stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or to any CEN member. This European Stan
14、dard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official versions. CEN members are the national stan
15、dards bodies of Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. CEN European Committee for Standardization Comit Europen de Normalisation Europisches Komitee fr Normung Cen
16、tral Secretariat: rue de Stassart 36, B-1050 Brussels 1995 Copyright reserved to CEN members Ref. No. EN 2561:1995 E Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 2561:1995 BSI 09-1999 2 Foreword This European Standard has been prepared
17、 by the European Association of Aerospace Manufacturers (AECMA). After inquiries and votes carried out in accordance with the rules of this Association, this Standard has successively received the approval of the National Associations and the Official Services of the member countries of AECMA, prior
18、 to its presentation to CEN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by March 1996, and conflicting national standards shall be withdrawn at the latest by March 1996. According to the CEN/CEN
19、ELEC Internal Regulations, the following countries are bound to implement this European Standard: Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. Contents Page Foreword2 1S
20、cope3 2Normative references3 3Definitions3 4Principle4 5Apparatus4 6Specimens4 7Procedure4 8Expression of results5 9Designation7 10Test report7 Annex A (normative) Form, dimensions of specimen, test fixture8 Figure 16 Figure A.1 Specimen and test fixture, types A and B8 Figure A.2 Specimen and test
21、fixture, type C8 Table A.19 Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 2561:1995 BSI 09-19993 1 Scope This standard specifies the method of determination of the ultimate tensile strength, tensile modulus and, if required, the Poisson
22、s ratio and strain at failure in tension of carbon fibre reinforced plastics in the form of unidirectional laminates. This method is only applicable to specimens where the axis is parallel to the direction of the fibres. 2 Normative references This European Standard incorporates by dated or undated
23、reference, provisions from other publications. These normative references are cited at the appropriate places in the text and the publications are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when inco
24、rporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies. EN 2489, Aerospace series Fibre reinforced plastics Determination of the action of test fluids. EN 2565, Aerospace series Preparation of carbon fibre reinforced resin panels for
25、 test purposes1). EN 2743, Aerospace series Reinforced plastics Standard procedures for conditioning prior to testing1). EN 2744, Aerospace series Non-metallic materials Preferred test temperatures. EN 2823, Aerospace series Fibre reinforced plastics Test method for the determination of the effect o
26、f exposure to humid atmosphere on physical and mechanical characteristics1). 3 Definitions For the purposes of this standard, the following definitions apply: 3.1 tensile stress tensile load experienced by the specimen at any moment during the test, per initial unit cross sectional area within the f
27、ree length 3.2 ultimate tensile strength (T11) tensile stress at the moment failure occurs 3.3 ultimate tensile strength related to the fibre (f) the ultimate tensile strength calculated as a function of the fibre cross sectional area and based on the hypothesis that all the tensile load is carried
28、by the fibres 3.4 strains (11 and 22) change in the distance between reference points in the specimen free length, produced by a tensile load and expressed with respect to the initial distance between these points 11 is the strain measured parallel to the fibre direction 22 is the strain measured pe
29、rpendicular to the fibre direction (in the plane of the laminate) 3.5 percentage strain to failure (A %) increase in the distance between reference points in the specimen free length, produced by a tensile load and expressed as a percentage of the initial distance between these points and measured a
30、t the moment of failure 1) Published as AECMA Prestandard at the date of publication of this standard Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 2561:1995 4 BSI 09-1999 3.6 secant modulus between PR/10 and PR/2 (ET11) slope of the st
31、raight line passing through: the point of the stress/strain diagram parallel to the load axis, corresponding to a stress calculated from PR/2; the point on the same diagram corresponding to a stress calculated from PR/10. PR is the load at failure of the specimen 3.7 secant modulus related to the fi
32、bre (Ef) the secant modulus calculated as a function of the fibre cross sectional area and based on the hypothesis that all the tensile load is carried by the fibres 3.8 poissons ratio (v12) absolute value of the ratio of the difference in strain 22 to the difference in strain 11, measured between P
33、R/10 and PR/2 (see Figure 1) 4 Principle The method consists of the measurement of the longitudinal and, if required, the lateral strains in the material, in relation to the load applied, during a tensile test carried out at a constant rate of displacement until failure occurs. 5 Apparatus 5.1 Micro
34、meter with 6 mm diameter flat faces and accurate to 0,01 mm 5.2 Testing machine, accurate to within 1 % in the load range used 5.3 A means of recording strains, in relation to the load (extensometer or strain gauges), accurate to within 1 % in the strain range used. The instrument shall not mark the
35、 specimen in a way which may cause premature failures. 5.4 If necessary, heated cabinet, regulated so as to conform to EN 2744 for tests at temperatures other than ambient 5.5 Thermocouple and recorder for tests at temperatures other than ambient 6 Specimens Take specimens from panels prepared accor
36、ding to EN 2565. 6.1 Form and dimensions See Annex A. 6.2 Number Minimum of five 7 Procedure 7.1 Conditioning EN 2743 for tests in the initial state; EN 2489 for tests after immersion; EN 2823 for tests after humidity exposure. 7.2 Tests 7.2.1 Measure the width to within 0,01 mm in the centre of the
37、 specimen and at two opposite points located 30 mm from the centre. b is the arithmetic mean of these three measurements. Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 2561:1995 BSI 09-19995 Measure the thickness to within 0,01 mm in th
38、e centre of the specimen and at two opposite points on the specimen axis and located 30 mm from the centre. h is the arithmetic mean of these three measurements. 7.2.2 For tests at temperatures other than ambient, the period separating the conditioning and start of the test shall conform to the foll
39、owing conditions: For specimens which have not been aged or subjected to immersion, the exposure time at the test temperature shall be established by preliminary tests. For specimens subjected to immersion, see EN 2489. For humidity aged specimens, see EN 2823. 7.2.3 The alignment of the specimen in
40、 the test machine jaws shall be sufficient to avoid the introduction of any bending loads. 7.2.4 The jaws shall entrap the tabs of the specimens of types A and B (see Figure A.1). 7.2.5 The load shall be applied at a constant rate of jaw separation of 2 mm/min. 7.2.6 Record the strain 11 and, if nec
41、essary, the strain 22 using the extensometer or strain gauges as a function of load. 7.2.7 Record the load at failure PR and, if necessary, the strain at failure (11)R. 8 Expression of results 8.1 Ultimate tensile strength T11 (MPa) where: 8.2 Ultimate tensile strength related to the fibre f(MPa) wh
42、ere: PRis the load at failure, in newtons; bis the width, in millimeters; his the thickness, in millimeters. nis the number of plies; Msfis the mass per unit area of fibre, in grams per square meter, per ply; fis the density of fibre, in kilograms per cubic meter; PRis the load at failure, in newton
43、s; bis the width, in millimeters. T11 PR b h - -= f PR f n b Msf - -= Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 2561:1995 6 BSI 09-1999 8.3 Secant modulus ET11 (MPa) between PR/10 and PR/2 Determine the strains from the recorded loa
44、d/strain diagram (Figure 1): where: 8.4 Secant modulus Ef (MPa) between PR/10 and PR/2 related to the fibre where: Figure 1 PRis the load at failure, in newtons; bis the width, in millimeters; his the thickness, in millimeters; (11)Ais the strain parallel to the fibre direction corresponding to PR/1
45、0; (11)Bis the strain parallel to the fibre direction corresponding to PR/2. PRis the load at failure, in newtons; nis the number of plies; fis the density of fibre, in kilograms per cubic meter; Msfis the mass per unit area of fibre, in grams per square meter; bis the width, in millimeters; License
46、d Copy: sheffieldun sheffieldun, na, Fri Nov 03 01:20:14 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 2561:1995 BSI 09-19997 8.5 Poissons ratio 12 where: 8.6 Percentage strain to failure A % A % = 100 (11)R (11)R = strain to failure parallel to the fibre direction 8.7 Validity The failure shall occ
47、ur within the free length of the specimen but may extend under the end tabs or within the test machine jaws. 9 Designation EXAMPLE: 10 Test report It shall include the following: designation (see 9); all data ensuring the traceability of the material (trade mark, identification, marking, date of rec
48、eipt etc.); all information regarding specimen preparation; specimen dimensions; test conditions, for example test temperature, relative humidity if these differ from this standard; exposure time at the test temperature; load/strain diagram; ultimate tensile strength T11 and mode of failure; method
49、of strain measurement (extensometer or strain gauges); secant modulus ET11 between PR/10 and PR/2; Poissons ratio 12 (if required); ultimate tensile strength related to the fibre f (if required); secant modulus Ef between PR/10 and PR/2 related to the fibre (if required); percentage strain to failure A (%); individual values, arithmetic mean and standard deviation; any incident which may have affected the resu