1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS ISO 5832-2:1999 ICS 11
2、.040.40; 77.120.50 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Implants for surgery Metallic materials Part 2: Unalloyed titanium Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI This British Standard, having been p
3、repared under the direction of the Health and Environment Sector Committee, was published under the authority of the Standards Committee and comes into effect on 15 December 1999 BSI 12-1999 ISBN 0 580 35725 2 BS ISO 5832-2:1999 Amendments issued since publication Amd. No.DateComments National forew
4、ord This British Standard reproduces verbatim ISO 5832-2:1999 and implements it as the UK national standard. It supersedes BS 7252-2:1994 which is withdrawn. The UK participation in its preparation was entrusted by Technical Committee CH/18, Surgical implant materials, to Subcommittee CH/18/2, Metal
5、lic materials, which has the responsibility to: aid enquirers to understand the text; present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments
6、and promulgate them in the UK. A list of organizations represented on this subcommittee can be obtained on request to its secretary. Cross-references The British Standards which implement international publications referred to in this document may be found in the BSI Standards Catalogue under the se
7、ction entitled International Standards Correspondence Index, or by using the Find facility of the BSI Standards Electronic Catalogue. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. C
8、ompliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, the ISO title page, pages ii and iii, a blank page, pages 1 to 3 and a back cover. The BSI copyright notice displayed in this do
9、cument indicates when the document was last issued. Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI A Reference number ISO 5832-2:1999(E) INTERNATIONAL STANDARD ISO 5832-2 First edition 1999-07-15 Implants for surgery Metallic materials Part
10、 2: Unalloyed titanium Implants chirurgicaux Produits base de mtaux Partie 2: Titane non alli Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ISO 5832-2:1999(E) ii Foreword ISO (the International Organization for Standardization) is a worldw
11、ide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on th
12、at committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in
13、accordance with the rules given in the ISO/IEC Directives, Part 3. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Intern
14、ational Standard ISO 5832-2 was prepared by Technical Committee ISO/TC 150, Implants for surgery, Subcommittee SC 1, Materials. This third edition cancels and replaces the second edition (ISO 5832-2:1993), which has been technically revised. ISO 5832 consists of the following parts, under the genera
15、l title Implants for surgery Metallic materials: Part 1: Wrought stainless steel Part 2: Unalloyed titanium Part 3: Wrought titanium 6-aluminium 4-vanadium alloy Part 4: Cobalt-chromium-molybdenum casting alloy Part 5: Wrought cobalt-chromium-tungsten-nickel alloy Part 6: Wrought cobalt-nickel-chrom
16、ium-molybdenum alloy Part 7: Forgeable and cold-formed cobalt-chromium-nickel-molybdenum-iron alloy Part 8: Wrought cobalt-nickel-chromium-molybdenum-tungsten-iron alloy Part 9: Wrought high nitrogen stainless steel Part 10: Wrought titanium 5-aluminium 2,5-iron alloy Part 11: Wrought titanium 6-alu
17、minium 7-niobium alloy Part 12: Wrought cobalt-chromium-molybdenum alloy Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ISO 5832-2:1999(E) iii Introduction No known surgical implant material has ever been shown to cause absolutely no advers
18、e reaction in the human body. However, long-term clinical experience of the use of the material referred to in this part of ISO 5832 has shown that an acceptable level of biological response can be expected when the material is used in appropriate applications. Licensed Copy: sheffieldun sheffieldun
19、, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI INTERNATIONAL STANDARD ISO 5832-2:1999(E) 1 Implants for surgery Metalic materials Part 2: Unalloyed titanium 1 Scope This p
20、art of ISO 5832 specifies the characteristics of, and corresponding test methods for, unalloyed titanium for use in the manufacture of surgical implants. Provision is made for six grades of titanium based on tensile strength (see Table 2). NOTE The mechanical properties of a sample obtained from a f
21、inished product made of this metal may not necessarily comply with those specified in this part of ISO 5832. 2 Normative references The following normative documents contain provisions which, through reference in this text, constitute provisions of this International Standard. For dated references,
22、subsequent amendments to, or revisions of, any of these publications do not apply. However, parties to agreements based on this International Standard are encouraged to investigate the possibility of applying the most recent editions of the normative documents indicated below. For undated references
23、, the latest edition of the normative document referred to applies. Members of ISO and IEC maintain registers of currently valid International Standards. ISO 6892:1998, Metallic materials Tensile testing at ambient temperature. ISO 7438:1995, Metallic materials Bend test. ASTM E 112:1988, Standard T
24、est Methods for Determining Average Grain Size. 3 Chemical composition The heat analysis when determined as specified in clause 6 shall conform to the requirements as to chemical composition specified in Table 1. Ingot analysis may be used for reporting all chemical requirements except hydrogen, whi
25、ch shall be determined after the last heat treatment and pickling procedure. 4 Microstructure The microscopic structure of the titanium in the annealed condition shall be uniform. The grain size, determined as specified in clause 6, shall be no coarser than grain size No. 5. At a magnification of 10
26、03, no inclusions or foreign phases shall be visible. Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ISO 5832-2:1999(E) 2 5 Mechanical properties 5.1 Tensile properties The tensile properties of the titanium, determined as specified in clau
27、se 6, shall be in accordance with the requirements of Table 2. Should any of the test pieces not meet the specified requirements, two further test pieces representative of the same batch shall be tested in the same manner. The titanium shall be deemed to comply only if both additional test pieces me
28、et the specified requirements. If a test piece fails outside the gauge limits, the test is invalid and a retest shall be performed. If any of the retests fails to meet the appropriate requirements, the product represented shall be deemed not to comply with this part of ISO 5832. However, the manufac
29、turer may, if desired, re-heat-treat the material and resubmit it for testing in accordance with the requirements of this part of ISO 5832. 5.2 Bending properties Titanium sheet and strip, when tested as specified in clause 6, shall not show any cracking on the outside surface of the test piece. Tab
30、le 1 Chemical composition Element Maximum compositional limits percent mass fraction Grade 1 ELI Grade 1 Grade 2 Grade 3 Grades 4A and 4B Nitrogen 0,012 0,03 0,03 0,05 0,05 Carbon 0,03 0,10 0,10 0,10 0,10 Hydrogen 0,012 5 a0,012 5 a0,012 5 a0,012 5 a0,012 5 a Iron 0,10 0,20 0,30 0,30 0,50 Oxygen 0,1
31、0 0,18 0,25 0,35 0,40 Titanium Balance Balance Balance Balance Balance a Except for billets, for which the maximum hydrogen content shall be 0,010 0 % (mass fraction) and for flat products for which the maximum hydrogen content shall be 0,015 % (mass fraction). Licensed Copy: sheffieldun sheffieldun
32、, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI ISO 5832-2:1999(E) 3 Table 2 Mechanical properties Grade Condition Tensile stength a Proof stress of non-proportional elongation Percentage elongation b Mandrel diameter for bend test for sheet and strip c min. min. min. mm MPa MPa
33、 % where t 2 mm where 2 mm t 5 mm 1 ELI Annealed 200 140 30 3 t 4 t 1 Annealed 240 170 24 3 t 4 t 2 Annealed 345 275 20 4 t 5 t 3 Annealed 450 380 18 4 t 5 t 4A Annealed 550 483 15 5 t 6 t 4B Cold-worked 680 520 10 6 t 6 t a Tensile, yield and bending requirements of sheet shall apply to material ta
34、ken both parallel and perpendicular to the direction of rolling. b Gauge length = 5,65 S0or 50 mm, where S0 is the original cross-sectional area, in square millimetres. c t = thickness of the sheet or strip. 6 Test methods The test methods to be used in determining compliance with the requirements o
35、f this part of ISO 5832 shall be those given in Table 3. Representative test pieces for the determination of mechanical properties shall be prepared in accordance with the provisions of ISO 6892. Table 3 Methods of test Requirement Relevant clause Method of test Chemical composition 3 Recognized ana
36、lytical procedures Grain size 4 ASTM E 112 Mechanical properties Ultimate tensile strength Yield strength Elongation Reduction of area Bend test 5 ISO 6892 ISO 6892 ISO 6892 ISO 6892 ISO 7438 Bend the sheet or strip through an angle of at least 105 around a mandrel of the diameter specified in Table
37、 2 Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS ISO 5832-2:1999 BSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |
38、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the in
39、ternational level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services
40、. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individ
41、ual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response
42、to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its
43、 Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: 020 8996 7111. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standa
44、rds developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 7001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of
45、the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior wri
46、tten permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel: 020 8996 7070. Licensed Copy: sheffieldun sheffieldun, na, Sun Nov 26 02:14:34 GMT+00:00 2006, Uncontrolled Copy, (c) BSI