《BS-6057-3.7-1995 ISO-705-1994.pdf》由会员分享，可在线阅读，更多相关《BS-6057-3.7-1995 ISO-705-1994.pdf（10页珍藏版）》请在三一文库上搜索。
1、BRITISH STANDARD BS 6057-3.7: 1995 ISO 705:1994 Rubber latices Part 3: Methods of test Section 3.7 Determination of density of natural rubber latices Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 6057-3.7:1995 This British Standard, hav
2、ing been prepared under the direction of the Materials and Chemicals Sector Board (I/-), was published under the authority of the Standards Board and comes into effect on 15 February 1995 BSI 11-1999 First published May 1982 Second edition February 1995 The following BSI references relate to the wor
3、k on this standard: Committee reference PRI/51 Draft for comment 92/40282 DC ISBN 0 580 23669 2 Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Committee PRI/51, Rubber latices, upon which the following bodies were represented: Bri
4、tish Rubber Manufacturers Association Malaysian Rubber Producers Research Association Medical Sterile Products Association Tropical Growers Association Amendments issued since publication Amd. No.DateComments Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolle
5、d Copy, (c) BSI BS 6057-3.7:1995 BSI 11-1999i Contents Page Committees responsibleInside front cover National forewordii 1Scope1 2Normative reference1 3Definitions1 4Apparatus1 5Sampling1 6Procedure1 7Expression of results2 8Test report3 Figure 1 Density bottles (pyknometers)3 Table 1 Density of wat
6、er at various temperatures2 List of referencesInside back cover Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 6057-3.7:1995 ii BSI 11-1999 National foreword This Section of BS 6057 has been prepared by Technical Committee PRI/51, and is
7、 identical with ISO 705:1994 Rubber latex Determination of density between 5 C and 40 C, published by the International Organization for Standardization (ISO). It supersedes BS 6057-3.7:1982, which is withdrawn. In the current edition of this standard the scope has been broadened to include syntheti
8、c and prevulcanized natural rubber latices. Also the temperature correction calculation has been specified in accordance with current practice. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct appl
9、ication. Compliance with a British Standard does not of itself confer immunity from legal obligations. Cross-reference International StandardCorresponding British Standard ISO 123:1985BS 6057 Rubber latices Part 2:1987 Sampling (Identical) Summary of pages This document comprises a front cover, an i
10、nside front cover, pages i and ii, pages 1 to 4, an inside back cover and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Licensed Copy: sheffieldun sheffieldun, na, W
11、ed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 6057-3.7:1995 BSI 11-19991 1 Scope This International Standard specifies a method for the determination of the density of natural rubber latex concentrate between the temperatures of 5 C and 40 C. The standard is intended for use when
12、density determinations are used to calculate the mass of a measured volume of latex in locations where it is not practical to weigh directly or to control the temperature of the laboratory. For such purposes, it is essential that the density be determined on a latex sample containing the same amount
13、 of air as it contained when the volume was measured. Therefore, the latex bulk is allowed to stand for a minimum period of 24 h before sampling to ensure the removal of air bubbles. The density determination is preferably made at the same temperature as the volume measurement, otherwise a correctio
14、n must be applied. This method is suitable for all latices from natural sources, for synthetic latex and for compounded or prevulcanized latex, as well as for artificial dispersions of rubber; however, the temperature correction given in 7.2 is not necessarily valid for all these. For measurements m
15、ade at standard temperatures, ISO 8962:1987, Plastics Polymer dispersions Determination of density should be used. NOTE 1It is intended that future editions of ISO 8962 will be modified to include latex in the scope. 2 Normative reference The following standard contains provisions which, through ref
16、erence in this text, constitute provisions of this International Standard. At the time of publication, the edition indicated was valid. All standards are subject to revision, and parties to agreements based on this International Standard are encouraged to investigate the possibility of applying the
17、most recent edition of the standard indicated below. Members of IEC and ISO maintain registers of currently valid International Standards. ISO 123:1985, Rubber latex Sampling. 3 Definitions For the purposes of this International Standard, the following definitions apply. 3.1 density mass divided by
18、volume at a stated temperature density is expressed in megagrams per cubic metre (Mg/m3) 3.2 natural rubber latex concentrate natural rubber latex containing ammonia and/or other preservatives and which has been subjected to some form of concentration 4 Apparatus 4.1 Density bottle (pyknometer), cap
19、acity 50 cm3, having a ground-glass stopper through which a capillary tube passes, and fitted with a ground-glass cap (see Figure 1). 4.2 Constant-temperature bath, accurate to within 0,2 C and adjustable to a temperature above or below ambient temperature. If a constant-temperature bath is not avai
20、lable, a water bath shall be used to ensure that the latex is at a known temperature. 4.3 Balance, accurate to 1 mg. 4.4 Two conical flasks, of at least 200 cm3 capacity, each fitted with a rubber stopper holding a short glass inlet tube with a blowing ball at the external end and a glass tube at th
21、e inside end reaching nearly to the bottom of the flask. 5 Sampling The latex to be sampled shall have stood for at least 24 h to ensure the removal of air bubbles. Record the temperature of the bulk of the latex at the time of sampling. Carry out the sampling in accordance with one of the methods s
22、pecified in ISO 123, taking care to avoid entrapment of air and ensuring that the bottle in which the sample is placed is completely filled. 6 Procedure Carry out the determination as soon as possible after sampling. If an adjustable constant-temperature bath (4.2) is not available, proceed in accor
23、dance with 6.2. The procedure takes account of the difficulties of controlling the temperature at the point of sampling natural rubber latex concentrate and the consequent need for a temperature correction. 6.1 Adjust the temperature of the constant-temperature bath to (see clause 5). Stir the sampl
24、e of the latex gently without introducing any air bubbles. Partly fill one of the conical flasks (4.4) with a suitable volume of latex and place in the bath. Likewise, partly fill the second conical flask with cool, freshly boiled, distilled water and place in the bath. Licensed Copy: sheffieldun sh
25、effieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 6057-3.7:1995 2 BSI 11-1999 Weigh the clean and dry density bottle (4.1) with its stopper and cap to the nearest 1 mg. Immerse the density bottle up to its neck in the bath, with the ground-glass stopper in place but no
26、t the cap. Allow the density bottle and the two conical flasks containing the latex and the water to come to the temperature of the bath this will require a minimum of 20 min. Using the blowing ball, such a few cubic centimetres of latex from the conical flask containing the latex and discard, then
27、transfer sufficient into the density bottle to fill it completely. Put the stopper in place and immediately wipe clean the top surface (tissue paper is recommended for this purpose), taking care not to remove any latex from the capillary tube. Remove the bottle from the bath and immediately put in p
28、lace the ground-glass cap. Dry the outside of the density bottle with the minimum of handling and then weigh the bottle to the nearest 1 mg. Empty the bottle and wash free from latex with distilled water. Immerse the bottle up to its neck in the constant-temperature bath as before. Fill the density
29、bottle with distilled water, transferring it by blowing from the second conical flask. Allow it to stand for 5 min in the bath. Empty the bottle, put it back in the bath and refill by the same procedure. Immediately insert the stopper and wipe dry the top surface (tissue paper is recommended for thi
30、s purpose), taking care not to remove any water from the capillary tube. Remove the density bottle from the bath and immediately put in place the ground-glass cap. Dry the outside of the bottle with the minimum of handling and then weigh the bottle to the nearest 1 mg. 6.2 If a non-adjustable water
31、bath is used, the temperature of the bath shall be such that it is not likely to fluctuate during the course of the determination and it shall be as close as is practical to the temperature of the bulk latex (see clause 5). Record the temperature 1 of the bath. Proceed as described in 6.1. Recheck t
32、he temperature of the bath before filling the density bottle with latex and after filling it with water. If the temperature of the bath has altered by 1 C, repeat the procedure. 7 Expression of results 7.1 Calculate the density of the latex at the temperature of the bath, in megagrams per cubic metr
33、e, using the equation The results of duplicate determinations shall agree to within 0,001 Mg/m3. Table 1 Density of water at various temperatures where mLis the mass, in grams, of the latex in the density bottle; mLW mW - -= mWis the mass, in grams, of the water in the density bottle; Wis the densit
34、y, in megagrams per cubic metre, of water at the bath temperature as given in Table 1. Temperature C Density Mg/m3 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 1,000 0 0,999 9 0,999 9 0,999 8 0,999 8 0,999 7 0,999 6 0,999 5 0,999 4 0,999 2 0,
35、999 1 0,998 9 0,998 8 0,998 6 0,998 4 0,998 2 0,998 0 0,997 8 0,997 5 0,997 3 0,997 0 0,996 8 0,996 5 0,996 2 0,995 9 0,995 6 0,995 3 0,995 0 0,994 7 0,994 4 0,994 0 0,993 7 0,993 3 0,993 0 0,992 6 0,992 2 Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled C
36、opy, (c) BSI BS 6057-3.7:1995 BSI 11-19993 7.2 In the case of natural rubber latex concentrate of 55 % to 75 % total solids content, when the temperature of the density determination 1 (see 6.2) differs from that of the bulk latex, the corrected density shall be calculated using the following equati
37、on (correct over the range 5 C to 40 C): c= 11 0,0005 ( 1) 8 Test report The test report shall include the following information: a) a reference to this International Standard; b) all details necessary for the identification of the sample; c) the results and the units in which they have been express
38、ed; d) the temperatures of the bulk latex and the bath; e) any unusual features noted during the determination; f) the date of the test; g) any operation not included in the International Standard or regarded as optional. where cis the corrected density at temperature ; 1is the density determined at
39、 temperature 1. Figure 1 Density bottles (pyknometers) Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI 4 blank Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 6057-3.7:1995 BSI 11
40、-1999 List of references See national foreword. Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 6057-3.7: 1995 ISO 705:1994 BSI 389 Chiswick High Road London W4 4AL BSI British Standards Institution BSI is the independent national body re
41、sponsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest am
42、endments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be
43、 found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publ
44、ications should be addressed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards
45、 BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Cen
46、tre. Tel: 020 8996 7111. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 7
47、001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or tra
48、nsmitted in any form or by any means electronic, photocopying, recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these detai
49、ls are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel: 020 8996 7070. Licensed Copy: sheffieldun sheffieldun, na, Wed Dec 06 15:23:50 GMT+00:00 2006, Uncontrolled Copy, (c) BSI