1、BRITISH STANDARD BS 5212-1: 1990 Cold applied joint sealant systems for concrete pavements Part 1: Specification for joint sealants UDC 625.848.083 Licensed Copy: sheffieldun sheffieldun, na, Mon Dec 04 16:18:26 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 5212-1:1990 This British Standard, having
2、been prepared under the direction of the Road Engineering Standards Policy Committee, was published under the authority of the Board of BSI and comes into effect on 31 July 1990 BSI 03-1999 First published, as BS 5212, April 1975 Second edition, as BS 5212-1 July 1990 The following BSI references re
3、late to the work on this standard: Committee reference RDB/10 Draft for comment 89/11487/DC ISBN 0 580 18353 X Committees responsible for this British Standard The preparation of this British Standard was entrusted by the Road Engineering Standards Policy Committee (RDB/-) to Technical Committee RDB
4、/10, upon which the following bodies were represented: Association of Consulting Scientists British Adhesives and Sealants Association British Airports Authority British Tar Industry Association County Surveyors Society Department of the Environment (Property Services Agency) Department of Transport
5、 Department of Transport (Transport and Road Research Laboratory) Institution of Civil Engineers Institution of Highways and Transportation Coopted members Amendments issued since publication Amd. No.DateComments Licensed Copy: sheffieldun sheffieldun, na, Mon Dec 04 16:18:26 GMT+00:00 2006, Uncontr
6、olled Copy, (c) BSI BS 5212-1:1990 BSI 03-1999i Contents Page Committees responsibleInside front cover Forewordii 1Scope1 2Definitions1 3Sampling1 4Types of sealant1 5Performance1 6Containers3 7Marking3 Appendix A Information to be given with enquiry or order5 Appendix B Typical manufacturers certif
7、icate5 Table 1 Types of cold applied joint sealants1 Publications referred toInside back cover Licensed Copy: sheffieldun sheffieldun, na, Mon Dec 04 16:18:26 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 5212-1:1990 ii BSI 03-1999 Foreword This Part of BS 5212 has been prepared under the direction
8、of the Road Engineering Standards Policy Committee. BS 5212:1975 has been revised in three Parts, namely: Part 1: Specification for joint sealants; Part 2: Code of practice for the application and use of joint sealants; Part 3: Methods of test. BS 5212-1, BS 5212-2 and BS 5212-3 supersede BS 5212:19
9、75 which is withdrawn. Exposure to excessive heat (e.g. jet blast) can have deleterious effects on all sealants but knowledge of this effect is limited. A test method has been included to assess flame resistance qualitatively. Information which should be given with an enquiry or order is shown in Ap
10、pendix A, and a typical form of manufacturers certificate is shown in Appendix B. Hot applied joint sealants are specified in BS 2499. It has been assumed in the drafting of this standard that the execution of its provisions is entrusted to appropriately experienced people. Product certification. Us
11、ers of this British Standard are advised to consider the desirability of third party certification of product conformity with this British Standard based on testing and continuing surveillance, which may be coupled with assessment of a suppliers quality systems against the appropriate Part of BS 575
12、0. Enquiries as to the availability of third party certification schemes will be forwarded by BSI to the Association of Certification Bodies. If a third party certification scheme does not already exist, users should consider approaching an appropriate body from the list of Association members. A Br
13、itish Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a fr
14、ont cover, an inside front cover, pages i and ii, pages 1 to 6, an inside back cover and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover. Licensed Copy: sheffieldun she
15、ffieldun, na, Mon Dec 04 16:18:26 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 5212-1:1990 BSI 03-19991 1 Scope This Part of BS 5212 specifies requirements for hand applied and machine applied, ordinary, fuel and flame resistant cold applied sealants for use in joints in roads, airfields and other
16、exposed concrete pavements. NOTEThe titles of the publications referred to in this standard are listed on the inside back cover. 2 Definitions For the purposes of this Part of BS 5212 the following definitions apply. 2.1 joint a vertical discontinuity between adjacent faces of slabs in the concrete
17、layer of a pavement 2.2 joint filler a strip of compressible material used to fill a joint space 2.3 joint sealant a material that, when applied in a uniform state to a joint, seals it by adhering to appropriate surfaces within the joint 2.4 primer a surface coating applied to the faces of the joint
18、 before placing the sealant in order to secure its adhesion 2.5 cold applied sealant a base component and a curing component that, when mixed at ambient temperature in the correct proportions and applied to a joint, will chemically cure to form a joint sealant 3 Sampling 3.1 Sealant The sample shall
19、 comprise components sufficient for at least 2.5 kg of mixed sealant material and be in unopened containers (see clause 6). When a 2.5 kg sample constitutes more than one packaging unit, the units shall be from the same batch. 3.2 Primer A sample shall consist of a minimum of 0.5 L taken at random f
20、rom the stock supplied with the sealant. 3.3 Stages of sampling Provision shall be made for sampling at the following stages. a) At the factory or source of distribution to determine the quality of the material as manufactured; NOTE 1Representative samples may be tested by the manufacturer to enable
21、 him to provide a certificate of quality for a particular production batch. b) From the packages or containers to determine the quality of the material as delivered. NOTE 2The purchaser may take samples on site to determine the quality of the material applied to a joint in accordance with BS 5212-2.
22、 4 Types of sealant 4.1 Cold applied joint sealants The sealant shall be one of the types specified in Table 1. 4.2 Primers The primer shall be identified as part of the sealant system and there shall be a visual indication of its presence. NOTEA suitable primer should always be specified by the man
23、ufacturer. Table 1 Types of cold applied joint sealants 5 Performance 5.1 Shelf life When stored in the original unopened containers and within the temperature range recommended by the manufacturer, the base component, the curing component and the primer shall be capable of being readily mixed to fo
24、rm a compound which complies with this standard, at any time up to the manufacturers stated expiry date. MaterialTypeCompliance criteria Hand or machine applied NormalNClause 5 except 5.9 and 5.10 Either or both Fuel resistantFClause 5 except 5.10 Either or both Flame and fuel resistant FBClause 5Ei
25、ther or both NOTE 1See BS 5212-2 for guidance on selection of type of sealant. NOTE 2Where the purchaser requires resistance to specific fuels, to hydraulic fluids or to de-icing fluids then the tests and limits for those specific fuels or fluids should be in accordance with the tests for resistance
26、 to immersion in fuel (see 5.9). Licensed Copy: sheffieldun sheffieldun, na, Mon Dec 04 16:18:26 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 5212-1:1990 2 BSI 03-1999 5.2 Application life NOTE 1The application life of hand applied sealants is that time after mixing during which the sealant exhibit
27、s sufficient flow to comply with clause 3 of BS 5212-3:1990. When tested in accordance with clause 3 of BS 5212-3:1990, hand applied sealants shall have an application life of at least 0.5 h. NOTE 2For machine applied sealants the application life and its method of determination should be agreed bet
28、ween the supplier and the purchaser. 5.3 Resistance to flow 5.3.1 General The sealant shall comply with both 5.3.2 and 5.3.3. 5.3.2 Using a horizontal mould at 5 C When tested in accordance with 5.3 of BS 5212-3:1990, the flow of a properly mixed sealant shall not exhibit a difference in depth betwe
29、en highest and lowest readings of more than 3 mm. 5.3.3 Using a mould inclined at 2.5 % at 23 2 C When tested in accordance with clause 5.4 of BS 5212-3:1990, the flow of a properly mixed sealant shall not exhibit a difference in depth at either end of the channel greater than 4 mm. NOTEWhere a cros
30、sfall is steeper than 2.5 % or where a joint width is greater than 20 mm the resistance to flow should be agreed between the supplier and the purchaser. 5.4 Tack-free time When tested in accordance with clause 4 of BS 5212-3:1990 the sealant shall not adhere to the polyethylene film after a period o
31、f 3 0.1 h for machine applied sealants or after 16 0.1 h for hand applied sealants. 5.5 Plastic flow When tested in accordance with clause 6 of BS 5212-3:1990, the flow of a properly mixed sealant down an aluminium plate inclined at 75 at 60 C shall not exceed 2 mm. 5.6 Penetration and recovery When
32、 tested in accordance with clause 7 of BS 5212-3:1990, the initial ball penetration shall not exceed 2.0 mm and the recovery shall be not less than 75 %. 5.7 Forces and adhesion and cohesion in tension and compression 5.7.1 General When subjected to three cycles of compression at 15 1 C and extensio
33、n at 20 1 C the sealant shall exhibit forces within the range specified in 5.7.2 and adhesion and cohesion properties within the range specified in 5.7.3. Three specimens shall be subjected to three cycles each in accordance with the requirements of 8.5 of BS 5212-3:1990. If the sealant fails to com
34、ply with 5.7.2.1, a fresh set of samples shall be tested. If only one specimen fails to comply with 5.7.2.2 or 5.7.2.3 or 5.7.3, then a retest of three specimens shall be permitted, all of which shall pass the requirements of 5.7.2.2 and 5.7.2.3 and 5.7.3. In all other cases of failure to comply wit
35、h the above requirements, the material shall be deemed to have failed the test. 5.7.2 Force on specimen 5.7.2.1 Difference between specimens The highest and lowest of the three maximum tensile forces recorded for the three samples on the first cycle of extension shall not differ from the average of
36、the three maximum tensile forces by more than 20 N or 20 % whichever is the lower. 5.7.2.2 Maximum force The highest maximum tensile force on any sample on any of the three cycles shall not exceed 300 N. 5.7.2.3 Lowest maximum force The lowest maximum tensile force in extension on any sample on any
37、of three cycles shall be 40 N. 5.7.3 Adhesion and cohesion The total area of the face of any specimen in which the sealant becomes completely separated from the primer during test plus the total superficial area of any ruptures on the face of the sealant shall together not exceed an area of 100 mm2.
38、 5.8 Resistance to heat ageing 5.8.1 General After heat ageing at 70 C for 14 days, in accordance with clause 9 of BS 5212-3:1990, the sealant shall comply with 5.7 and 5.8.2 to 5.8.4 inclusive. 5.8.2 Mass loss When tested in accordance with 9.3 of BS 5212-3:1990, the sealant shall not lose more tha
39、n 6 % of its original mass. Licensed Copy: sheffieldun sheffieldun, na, Mon Dec 04 16:18:26 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS 5212-1:1990 BSI 03-19993 5.8.3 Penetration and recovery When tested in accordance with 9.4 of BS 5212-3:1990, the initial ball penetration shall be not more than
40、2.0 mm and the recovery shall be not less than 75 %. 5.8.4 Forces and adhesion and cohesion in tension and compression 5.8.4.1 The sealant shall be tested in accordance with 9.5 of BS 5212-3:1990 except that the sealant shall be subjected to only one cycle of compression at 15 1 C and extension at 2
41、0 1 C. Forces shall be within the range specified in 5.7.2 and adhesion and cohesion properties shall be as specified in 5.7.3. Additionally, the mean force in extension shall not differ by more than 100 N from that measured in 5.7.2. 5.8.4.2 The procedures of 5.8.4.1 shall be repeated but with the
42、period of ageing, in accordance with 5.8.1, extended to 28 days. Sealants shall comply with 5.8.4.1, except that the mean force in extension shall not differ from that reported from 5.8.4.1 by more than 25 %. 5.9 Resistance to fuel immersion of sealant types F and FB 5.9.1 Change in mass When tested
43、 in accordance with 10.5 of BS 5212-3:1990, the mass of the sealant shall not increase by more than 5 % nor decrease by more than 10 %. 5.9.2 Penetration and recovery When tested in accordance with 10.6 of BS 5212-3:1990, the initial ball penetration shall be not more than 2.0 mm and the recovery sh
44、all be not less than 75 %. 5.9.3 Forces and adhesion and cohesion in tension and compression When tested in accordance with 10.7 of BS 5212-3:1990 and subjected to three cycles of compression at 15 1 C and extension at 20 1 C, the sealant shall exhibit forces within the range specified in 5.7.2 and
45、adhesion and cohesion properties as specified in 5.7.3. 5.10 Resistance to flame During heating in accordance with clause 11 of BS 5212-3:1990, the sealant shall not show any visual evidence of ignition, support of combustion or flow and separation. On subsequent examination when cool the sealant sh
46、all not show any visual evidence of hardening or loss of flexibility. 6 Containers 6.1 Delivery Joint sealants and primers shall be supplied in containers which are sealed and which allow the sealant to be stored without detriment for the full shelf life under the manufacturers recommended condition
47、s. 6.2 Disposal The manufacturer shall supply relevant advice regarding the disposal of empty containers on the container label. NOTEAttention is drawn to the provisions of the Health and Safety at Work Act 1974 and related legislation. 7 Marking 7.1 Certificate A certificate containing at least the
48、 information shown in Appendix B shall be supplied if requested by the purchaser. 7.2 Joint sealant components Each container of sealant component shall be clearly and indelibly marked with the following: a) the manufacturers name; b) the type, grade and batch number of the compound; c) the expiry d
49、ate or the date of manufacture together with the storage life under the conditions specified by the manufacturer; d) whether the sealant is for hand or machine application; e) the type of primer to be used; f) the number and date of this British Standard, i.e. BS 5212-1:19901). Each container shall be clearly and indelibly marked to differentiate between the components of the sealant and, where required, with the batch numbers of components that are to be used together. 1) Marking BS 5212-1:1990 on or in relation to a product re