1、INTERNATIONAL STANDARD IS0 9073-4 Second edition 1997-07- 15 Textiles - Test methods for nonwovens - Part 4: Determination of tear resistance Textiles - Mkthodes d essai pour nontissks - Parfie 4: Dgtermination de la ksistance 2 la dkhirure Reference number IS0 9073-4: 1997(E) Copyright Internationa
2、l Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 9073-4: 1997(E) Foreword IS0 (the international Organization for
3、Standardization) is a worldwide federation of national standards bodies (IS0 member bodies). The work of preparing International Standards is normally carried out through IS0 technical committees. Each member body interested in a subject for which a technical committee has been established has the r
4、ight to be represented on that committee. International organizations, governmental and non- governmental, in liaison with ISO, also take part in the work. IS0 collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. Draft Inte
5、rnational Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. International Standard IS0 9073-4 was prepared by Technical Committee ISOmC 38, Tex
6、tiles. This second edition replaces and cancels the first edition (IS0 9073-4:1989), clause 3, figure 1, subclause 6.2, subclause 7.2 and clause 8 of which have been technically revised. IS0 9073 consists of the following parts, under the general title Textiles - Test methods for nonwovens: Part 1:
7、Determination of mass per unit area - Part 2: Determination of thickness - Part 3: Determination of tensile strength and elongation - Part 4: Determination of tear resistance 0 IS0 1997 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any
8、form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from the publisher. International Organization for Standardization Case postale 56 l CH-1211 Geneve 20 l Switzerland Internet central iso.ch x.400 c=ch; a=400net; p=iso; o=isocs; s=cen
9、tral Printed in Switzerland ii Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 IS0 9073-4:
10、1997(E) Introduction Although nonwovens are classified within the textile industry, it should be recognized that nonwovens technologically share characteristics not only with textile products but also with paper and/or plastic products. There is no current International Standard for determination of
11、 tear strength of textiles, but work is proceeding on determination of tear resistance (falling pendulum method, IS0 92903990, TexMes - Woven fabrics - Deter- mination of tear resistance by falling pendulum method) and determination of tear resistance (tongue-tear method). This method, which uses a
12、trapezoidal tear, is a tension test in which the strength is determined primarily by the fibres of the composite structure and their bonding or interlocking. It is useful for estimating relative ease of tearing of nonwovens. In nonwovens, the mechanism of failure is affected by interfibre frictional
13、 forces and differs from that found for woven fabrics, where failure is essentially that of sequential rupture of yarns in tension. There is evidence that this test may not be applicable to nonwovens above a certain mass per unit area and stiffness. Additional work on this problem is in progress. Co
14、pyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,- This page intentionally left blank Copyright Inte
15、rnational Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,- INTERNATIONAL STANDARD IS0 IS0 9073-4: 1997(E) Textiles - Tes
16、t methods for nonwovens - Part 4: Determination of tear resistance 1 Scope This part of IS0 9073 specifies a method for the determination of tear resistance of nonwovens by the trapezoid method. 2 Normative references The following standards contain provisions which, through reference in this text,
17、constitute provisions of this part of IS0 9073. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this part of IS0 9073 are encouraged to investigate the possibility of applying the most recent editions of the sta
18、ndards indicated below. Members of IEC and IS0 maintain registers of currently valid International Standards. IS0 139: 1973, Texti/es - Standard atmospheres for conditioning and testing. IS0 186:1994, Paper and board - Sampling to determine average quality. 3 Principle Marking of a trapezoid on a te
19、st piece. Clamping of the non-parallel sides of the trapezoid in the jaws of a tensile testing machine. Application of a continuously increasing extension to the test piece in such a way that a tear propagates across its width. Determination of the average maximum tear resistance in newtons. 4 Appar
20、atus 4.1 Tensile testing machine, either constant rate of extension type or constant rate of traverse type, equipped with an autographic recorder to register applied force. 4.2 Clamps, of sufficient width to accommodate the full width of the test piece. 4.3 Template, with dimensions as shown in figu
21、re 1. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 9073-4: 1997(E) IS0 Dimensions in mil
22、iimetres / 1 1 1 / /I /I 1 1 / I Figure 1 - Template for trapezoid tearing test 5 Sampling Carry out sampling in accordance with IS0 186, ensuring that the areas from which the specimens are taken have no visible flaws and are not creased. NOTE 1 This method of sampling recognizes and makes provisio
23、ns for “anisotropy” (differences in properties along various directions, principally machine and cross direction) in the final specimens. However, these specimens are random representatives of the material and in some cases it may be desirable to investigate systematic variations of properties (incl
24、uding anisotropy), for example across the width, or in certain positions along the length of a given reel. In all such cases, special provisions should be agreed between purchaser and vendor and recorded in the test report. A procedure for more detailed examination of variability within a given batc
25、h of material is available in TAPPI T 11 n 5.74 and may be found helpful. This publication may be obtained from: The Technical Association of Pulp and Paper Industries, 1 Dunwoody Park, Atlanta, Georgia 30338, USA. 6 Preparation and conditioning of test pieces 6.1 Unless otherwise specified, cut fiv
26、e test pieces in the machine direction and five in the cross-machine direction. NOTE 2 The edge of the specimen should not normally form part of the test piece. 6.2 Cut test pieces (75 + 1) mm x (150 k 2) mm. Mark each test piece with an isosceles trapezoid using the template. Make a preliminary cut
27、 as shown in figure 1. NOTE 3 Other dimensions, respecting the general proportions of the original test piece, may be agreed between interested parties, especially in order to reproduce some in-use conditions of nonwovens, and should be noted in the test report. The values measured with different te
28、st piece dimensions cannot be compared. 6.3 Condition the test pieces as specified in IS0 139. 2 Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or ne
29、tworking permitted without license from IHS -,-,- IS0 IS0 9073-4: 1997(E) 7 Procedure 7.1 Carry out the testing in the standard atmosphere for testing (see IS0 139). 7.2 At the start of the test, set the clamps (25 + 1) mm apart and operate the machine at 100 mm/min. Select the force range of the te
30、sting machine so that the break occurs between 10 % and 90 % of full scale. 7.3 Secure the test piece in the machine, clamping along the non-parallel sides of the trapezoid with the cut half- way between the clamps. Hold the short edge taut and let the long edge lie in folds. 7.4 Start the machine w
31、ith pawls disengaged, if appropriate, and record the tearing autographic recorder. If the test piece does not tear at the cut, no resu It shall be registere force, in Id . newtons, on the NOTE 4 The tearing force will not usually be a single value but will generally appear as a series of maxima and
32、minima. 8 Expression of results Determine the average value of the series of significant load peaks (see note 5) represented on the autographic record for each individual test piece for both machine direction and cross direction. In the event that there is only one definite load peak on the autograp
33、hic record, this value shall be taken as the result for that specimen. Determine the mean and coefficient of variation of the results for the five test pieces in both the machine and cross directions. NOTES 5 The displacement of the clamps is measured with the starting distance between the clamps at
34、 25 mm. The tear propagation resistance is recorded until the test piece breaks completely, but the results are only valid up to the displacement of the clamps reaching 64 mm. Beyond this value, the measured tear force is reduced by the proximity of the border of the test piece. For this reason, the
35、 significant peak loads to be considered are those corresponding to the displacement of the clamps below the limit of 64 mm. 6 Where electronic recording machines are used, it is possible to obtain a mean force for each test piece, which is then averaged to give the final results. For the same reaso
36、n as expressed in note 5, the mean force should be calculated between the following two limits: - the displacement of the clamps corresponding to the first load peak; - the displacement of the clamps equal to 64 mm. 9 Test report The test report shall include the following information: a) a referenc
37、e to this par of IS0 9073; b) all details necessary for the identification of the material; c) the results of the tests in both the machine direction and cross direction (see clause 8); d) the conditioning atmosphere used; e) any unusual features noted during the testing, or deviations from the stan
38、dard procedure. Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,- IS0 9073-4: 1997(E) ICS 59.080.
39、30 Descriptors: textiles, fabrics, non-woven fabrics, tests, tear tests, determination, tear strength. Price based on 3 pages Copyright International Organization for Standardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/25/2007 23:55:29 MDTNo reproduction or networking permitted without license from IHS -,-,-